介绍了聚合物改性砂浆在国内外的使用现状和应用前景、分类和性质、国内外研究现状以及研究趋势等,同时也探讨了聚合物改性砂浆的作用机理,并详细介绍了目前本领域所存在的几个问题,展望了聚合物改性砂浆未来的应用.
参考文献
| [1] | 曹双寅;邱洪兴;王恒华.结构可靠性鉴定与加固技术[M].北京:中国水利水电出版社,2002 |
| [2] | 王燕谋;苏慕珍.硫铝酸盐水泥[M].北京:北京工业大学出版社,1999:205. |
| [3] | 黄从运,陈超,付冰.聚合物改性修补水泥混凝土的研究进展[J].建材技术与应用,2008(03):1-4. |
| [4] | 钟世云,王培铭.聚合物改性砂浆和混凝土的微观形貌[J].建筑材料学报,2004(02):168-173. |
| [5] | XIAO Liguang,JIN Yujie,GU Lixia.Preparation and Properties of a New Composite of Epoxy Emulsion(EEM)Modified Cement[J].武汉理工大学学报(材料科学版)(英文版),2009(05):843-845. |
| [6] | 颜廷志,李长杰,张来红.BXS聚合物砂浆在音河水库混凝土建筑物维修工程中的应用[J].黑龙江水利科技,2008(04):136. |
| [7] | Ribeiro, MCS;Ferreira, AJM;Marques, AT .Effect of natural and artificial weathering on the long-term flexural performance of polymer mortars[J].Mechanics of composite materials,2009(5):515-526. |
| [8] | Hyug-Moon Kwon;Thuy Ninh Nguyen;Tuan Anh Le .Improvement of the strength of acrylic emulsion polymer-modified mortar in high temperature and high humidity by blast furnace slag[J].KSCE Journal of Civil Engineering,2009,13(01):23. |
| [9] | Barluenga G et al.SBR latex modified mortar theology and mechanical behaviors[J].Cement and Concrete Research,2004,34(03):527. |
| [10] | 陈华光,熊剑平.三种乳液改性路用水泥修补砂浆力学性能研究[J].公路与汽运,2005(02):75-77. |
| [11] | 黄从运,张明飞,曾俊杰,蔡肖,张美香.聚合物乳液改性硫铝酸盐水泥修补砂浆的试验研究[J].化学建材,2006(05):34-36. |
| [12] | 郑志伟,龚爱民,彭玉林.丙烯酸酯共聚乳液改性水泥砂浆性能的试验研究[J].云南农业大学学报（自然科学版）,2007(03):427-430. |
| [13] | 傅淑娟,李敬业,赵崇恒,刘涛.用"PC材料置换法"加固钢筋混凝土梁[J].建筑科学,2005(02):44-48. |
| [14] | 黄华,刘伯权,刘卫铎.高强钢绞线网-聚合物砂浆加固层与RC结构黏结面性能试验[J].中国公路学报,2009(03):70-75. |
| [15] | 葛序尧,武志刚,彭勃.聚合物与粉煤灰改性砂浆性能的研究[J].混凝土,2009(06):110-111,119. |
| [16] | 谢业明,葛序尧,单远铭.聚合物改性高强修补水泥砂浆的研究[J].工程与建设,2009(02):222-224,227. |
| [17] | Arnaud Perrot;Christophe Lanos;Yannick Melinge et al.Mortar physical properties evolution in extrusion flow[J].Rheologica Acta,2007,46(08):1065. |
| [18] | Vinckea E;Wanseele E V;Monteny J et al.Influence of polymer addition on biogenic sulfuric acid attack of concrete[J].International Biodeterioration and Biodegradation,2002,49:283. |
| [19] | J. Monteny;N. De Belie;E. Vincke .Chemical and microbiological tests to simulate sulfuric acid corrosion of polymer-modified concrete[J].Cement and Concrete Research,2001(9):1359-1365. |
| [20] | 郑宝红,王志新.EE聚合物修补砂浆的耐腐蚀性能的研究[J].中国建材科技,2005(04):13-16. |
| [21] | 宋俊美,谈慕华,吴科如.聚合物裹砂改性水泥砂浆的性能研究[J].建筑材料学报,1999(04):308. |
| [22] | Guangjing Xiong;Xiaohu Chen;Gengying Li .Sulphuric acid resistance of soluble soda glass-polyvinyl acetate latex-modified cement mortar[J].Cement and Concrete Research,2001(1):83-86. |
| [23] | 钟世云,谈慕华,迟克剑,许实.氯偏共聚物在水泥浆中的降解与稳定[J].建筑材料学报,2001(04):322-326. |
| [24] | Hansen W C.Actions of calcium sulphate and admixtures in Portland cement pastes[A].San Francisco.ASTM Spec Tech Publ,1960:266. |
| [25] | Su Hua Ding;Da Zuang Liu;Lin Li Duan .Accelerated aging and aging mechanism of acrylic sealant[J].Polymer Degradation and Stability,2006(5):1010-1016. |
| [26] | WANG Yuli,ZHOU Mingkai,SHAN Junhong,XU Fang,YANG Yuhui.Influences of Carboxyl Methyl Cellulose on Performances of Mortar[J].武汉理工大学学报（材料科学版）（英文版）,2007(01):108-111. |
| [27] | C. P. Ostertag;CK. Yi .Crack/fiber interaction and crack growth resistance behavior in microfiber reinforced mortar specimens[J].Materials and structures,2007(7):679-691. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%