采用动态高温粉晶X射线衍射技术,对燃烧法合成的纳米α-Al2O3从室温到1100℃之间的晶格热膨胀系数进行了测定.实验结果表明:在测试温度范围内,纳米α-Al2O3的晶胞参数与温度呈线性关系.燃烧法合成的纳米α-Al2O3的晶胞参数随温度的变化符合关系式: △α/(α0△T)=7.27×10-6/℃、△c/(c0△T)=7.50×10-6/℃和△V/(V0△T)=21.92×10-6/℃.
The α-Al2O3 nanoparticles were prepared by the combustion synthesis method, The lattice parameters of α-Al2O3 were determined by XRD at temperatures ranging from roomtemperature to 1100℃, the thermal expansion coefficients of △α/α0; △c/c0 and △V/V0 per℃ of α-Al2O3 lattice were 7.27×10-6/℃, 7.50×10-6/℃ and 21.92×10-6/℃ respectively.
参考文献
| [1] | 张立德. 材料导报, 2001, 15 (7): 2--5. [2] 钟盛文, 焦永斌, 叶雪均, 等(ZHONG Sheng-Wen, et al). 无机材料学报(Journal of Inorganic Materials), 2001, 16 (3): 572--576. [3] 李继先, 孙旭东等. 材料研究学报, 1998, 12 (1): 105--107. [4] 王志强, 马铁成. 硅酸盐通报, 2000, 19 (5): 28--31. [5] 张剑光, 张明福, 韩杰才. 材料工程, 2001, (7): 40--42. [6] Lyon K G, Salinger G L, Swenson C A, et al. J. Appl. Phys., 1977, 48 (3): 865--868. [7] Lager G A, Jorgensen J D, Rotella F J. J. Appi. Phtys., 1982, 53 (10): 6751--6756. [8] 储刚, 翟秀静, 毕诗文, 等. 《化学通报》网络版(Chemistry Online), 2004, 67 (3): w22. [9] 南京大学地质学系矿物岩石教研室. 粉晶X射线物相分析. 北京: 地质出版, 1980. 103--110. [10] 储刚, 黄继亮. 计算机与应用化学, 1995, 12 (1): 72--76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%