借助高能球磨Al及5%CuO合成了纳米复合粉末,进而在退火后,通过热压和热挤制备出了组织均匀、致密、晶粒尺寸约为120 nm～150 nm的亚微米块体Al基复合材料.XRD和显微组织分析表明:粉体球磨时,Al与CuO之间发生了还原反应,但生成物的热稳定性较差,在400℃退火过程中发生了与球磨时相逆的固态反应;复合粉末显微组织上的冷焊条纹其实质是球磨产生的高畸变区,退火使之逐渐消失;制备的亚微米块体复合材料主要以Al2Cu和Al2O3颗粒为增强相,室温下具有良好的压缩性能,但拉伸时表现出极大的脆性.
参考文献
| [1] | Lo J et al.[J].Scripta Metallurgica et Materialia,1995,33:1423. |
| [2] | Tjong SC.;Ma ZY. .Microstructural and mechanical characteristics of in situ metal matrix composites [Review][J].Materials Science & Engineering, R. Reports: A Review Journal,2000(3/4):49-113. |
| [3] | Matin M A et al.[J].Scripta Materialia,2001,45:479. |
| [4] | 席生岐,屈晓燕,郑修麟.Al/CuO的高能球磨固态反应[J].中国有色金属学报,1998(01):43-46. |
| [5] | Ma Mingliang;Liu Xinkuan;Xi Shengqi;Chai Donglang;Zhou Jing'en .Effect of material characteristics on the ignition of the combustion reactions induced by ball milling[J].Journal of Materials Processing Technology,2001(2/3):124-127. |
| [6] | Wu J M et al.[J].Journal of Alloys and Compounds,2000,299:9. |
| [7] | 樊建中 et al.[J].金属学报,1998,34(11):1199. |
| [8] | 丛洪涛,杨志卿,贺连龙,卢柯.Al2O3/Al纳米复合材料的强化机制[J].金属学报,2003(03):320-324. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%