采用连续相场模型对晶粒形核过程进行模拟,从动力学角度考虑,引入类似于纳米颗粒的界面效应,分析它对形核过程的影响:同时研究形核过程中晶核的析出、形核数目变化、晶界厚度变化以及晶核生长的特点.结果表明,界面效应为形核过程提供驱动力,促使晶核的快速长大；形核过程中晶核数目随时间逐渐增多,晶核尺寸逐渐增大,晶核生长速度较快,同时晶粒位向取向参数的变化反映了晶粒尺寸和晶界厚度的变化.
参考文献
| [1] | Xiaoyan S.;Guoquan L. .RE-ANALYSIS ON GRAIN SIZE DISTRIBUTION DURING NORMAL GRAIN GROWTH BASED ON MONTE CARLO SIMULATION[J].Scripta materialia,2000(4):355-359. |
| [2] | Nordbakke M W;Ryum N .[J].Acta Materialia,2002,50:3661. |
| [3] | Wang C;Liu G .[J].Materials Letters,2003,57:4424. |
| [4] | Geiger J;Roosz A;Barkoczy P .[J].Acta Materialia,2001,49:623. |
| [5] | Ivasishin O M;Shevchenko S V;Vasiliev N L et al.[J].Acta Materialia,2003,51:1019. |
| [6] | Moldovan D;Wolf D;Phillpot S R et al.[J].Philosophical Magazine,2002,82(A):1271. |
| [7] | Fan D;Chen L Q .[J].Acta Materialia,1997,45:611. |
| [8] | Chen L Q;Yang W .[J].Physical Review,1994,50(B):15752. |
| [9] | Cahn J W;Hilliard T E .[J].Journal of Chemical Physics,1958,28:258. |
| [10] | Zhang Yutuo;Wang Chengzhi .[J].Acta Metallurgica,2009,22:197. |
| [11] | 赵彦,陈铮,王永欣,张明义,张静.弹性应变能对Ni75Al17Zn8合金过渡有序行为影响的微观相场研究[J].科学通报,2010(02):182-187. |
| [12] | 李俊杰,王锦程,杨根仓.含第二相颗粒的晶粒长大过程相场法[J].稀有金属材料与工程,2008(10):1746-1750. |
| [13] | Kazaryan A;Wang Y;Dregia S A et al.[J].Acta Materialia,2002,50:2491. |
| [14] | Moelans N;Blanpain B;Wollants P .[J].Acta Materialia,2005,53:1771. |
| [15] | 高英俊,张海林,金星,黄创高,罗志荣.相场方法研究硬质颗粒钉扎的两相晶粒长大过程[J].金属学报,2009(10):1190-1198. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%