在扫描电子显微镜下观察分析了B级船板钢试样在原位拉伸过程中的断裂行为以及低温脆性断口中二次裂纹的扩展.结果表明:在拉伸变形过程中,微裂纹首先在试样缺口处形成,然后沿铁素体+珠光体界面扩展.加载过程中,多边形铁素体发生塑性变形,裂纹在基体内以"Z"字型扩展.在低温脆性断裂区,二次裂纹以穿晶方式通过铁素体基体,在扩展到珠光体区域时有时沿铁素体和珠光体的界面扩展,有时穿过珠光体区域扩展.
参考文献
| [1] | Mishnaevsky L L;Lippmann Jr N;Chmauder S S et al.InSitu Observation of Damage Evolution and Fracture in AlSi7Mg0.3 Cast Alloys[J].Engineering Fracture Mechanics,1999,63:395. |
| [2] | Zhang J Z .A Shear Band Decohesion Model for Small Fatigue Crack Growth in an Ultra-Fine Grain Aluminium Alloy[J].Engineering Fracture Mechanics,2000,65:665. |
| [3] | Sohn K S;Lee Y J;Kim N J .Deformation and Fracture Behavior of an 8090 Al-Li Alloy at Cryogenic Temperature[J].Scripta Metallugical et Materiallia,1995,32(08):1255. |
| [4] | 朱维斗;顾海澄;郭延东 .Ti-1023合金拉伸试验的电镜原位观察[J].金属学报,1994,30(10):462. |
| [5] | 钟群鹏;赵子华.断口学[M].北京:高等教育出版社,2005 |
| [6] | Akhmad A;Korda Y;Mutoh et al.Effects of Pearlite Morphology and Specimen Thickness on Fatigue Crack Growth Resistance in Ferrite-Pearlite Steels[J].Materials Science and Engineering,2006,428A:262. |
| [7] | 徐平光,方鸿生,白秉哲,杨志刚.仿晶界型铁素体/粒状贝氏体复相组织的韧性[J].金属学报,2002(03):255-260. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%