以Fe-1.8Ni-0.5Mo-1.2Cu-0.2C预合金粉为原料,采用温压、烧结、渗碳、淬火与低温回火的工艺制备了粉末冶金齿轮,利用光学显微镜、扫描电子显微镜和硬度仪等研究了齿轮的组织与性能。结果表明:温压压坯的密度为7.35g.cm-3,相对密度为94.2%;烧结态齿轮的显微组织主要是珠光体和铁素体,硬度达到46~54HRA,密度为7.37g.cm-3,相对密度为94.5%,烧结态齿轮有轻微收缩现象,但其仍表现出良好的尺寸稳定性;热处理后齿轮渗碳层的组织主要由回火马氏体和少量残余奥氏体组成,齿轮断齿扳力为9.6kN,硬度提高至66~75HRA。

Taking Fe-1.8Ni-0.5Mo-1.2Cu-0.2C pre-alloy powder as raw material,a powder metallurgy gear was prepared by warm compaction,sintering,carburizing,quenching and low temperature tempering technologies.The microstructure and properties of the gear were studied by optical microscopy,scanning electron microscopy and hardness testing,etc.The results show that the warm compaction green density was 7.35 g·cm-3 and relative density was 94.2%.The microstructure of sintered gear mainly was pearlite and ferrite,the hardness,density,relative density of the sintered gear was 46-54 HRA,7.37 g·cm-3 and 94.5%,respectively.The slight shrinkage of sintered gear was found,but it still kept good dimensional stability.The microstructure of carburized layer after heat treatment mainly was tempered martensite and small amounts of retained austenite,and the teeth mechanical resistance was 9.6 kN and the hardness was increased to 66-75 HRA.

参考文献

[1] 果世驹.粉末冶金温压技术的进展[J].粉末冶金工业,2003(02):3-8.
[2] 张双益,李元元.铁基粉末冶金材料的温压工艺[J].机械工程材料,2000(01):26-28,47.
[3] 沈元勋,肖志瑜,方亮,张文,李元元.部分扩散预合金温压铁-铜-镍-钼-碳材料的组织与性能[J].机械工程材料,2007(09):30-33.
[4] Narasimhan KS. .Sintering of powder mixtures and the growth of ferrous powder metallurgy[J].Materials Chemistry and Physics,2001(1/3):56-65.
[5] 姜峰,李益民,邓忠勇.粉末冶金低合金钢的制备和性能研究进展[J].材料导报,2004(06):39-42,50.
[6] 林文松,李元元,陈维平.镍元素对铁基合金烧结收缩的影响[J].机械工程材料,2003(10):11-13,16.
[7] Wang WF .Effect of alloying elements and processing factors on the microstructure and hardness of sintered and induction-hardened Fe-C-Cu alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):92-97.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%