针对特大截面圆坯连续浇铸的特点,基于依靠浸入式水口自身结构减小钢流冲击深度,同时保证流动与传热沿周向分布均匀的思想,首次提出了新型浸入式伞形水口设计方案,并建立了结晶器内钢水的流-热-固耦合模型,对钢水的流动、传热和凝固行为进行了数值耦合模拟分析,验证了此水口的优越性与合理性:伞形水口的射流在结晶器内形成上下两个回流区,不仅有利于夹杂物、气体等的上浮分离,还能有效降低钢流冲击深度,使过热钢液均匀分布在结晶器上部,可提高弯月面温度和化渣效果;沿周向凝壳生长均匀,减轻了纵裂纹的萌生概率;在0.35 m/min拉速下,出结晶器凝壳厚度达到31.2mm,满足安全生产要求.
参考文献
| [1] | Thomas B G;Mika L J;Najjar F M .Simulation of Fluid Flow Inside a Continuous Slab Casting Machine[J].Metallurgical Transactions B,1990,21(02):387. |
| [2] | Hintikka S;Konttinen J;Leiviska K.Optimization of Molten Steel Flow in Continuous Casting Mold[A].Warrendale:ISS,1992:887. |
| [3] | 吴耀光,陈远清,仇圣桃,赵沛.大圆坯连铸用新型旋流水口的数值模拟[J].钢铁钒钛,2009(04):49-54. |
| [4] | 盛义平,孔祥东,杨永利.连铸结晶器传热边界条件研究[J].中国机械工程,2007(13):1615-1618. |
| [5] | Yin Hebi;Yao Man .Inverse problem-based analysis on non-uniform profiles of thermal resistance between strand and mould for continuous round billets casting[J].Journal of Materials Processing Technology,2007(1):49-56. |
| [6] | Liangliang GUO;Xudong WANG;Huiying ZHAN .Mould Heat Transfer in the Continuous Casting of Round Billet[J].ISIJ International,2007(8):1108-1116. |
| [7] | 姚曼,吴翔宇,尹合壁,王旭东.圆坯连铸结晶器热流研究[J].钢铁研究学报,2006(10):16-19. |
| [8] | 陈家祥.连续铸钢手册[M].北京:冶金工业出版社,1991 |
| [9] | 吴耀光,龚志翔,张建平,范鼎东,刘建坤,吴宗双.圆坯连铸工艺优化试验研究[J].钢铁,2008(08):31-34. |
| [10] | Jong-Kyu YOON .Applications of Numerical Simulation to Continuous Casting Technology[J].ISIJ International,2008(7):879-884. |
| [11] | 冯捷.连续铸钢生产[M].北京:冶金工业出版社,2005 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%