针对2种碳纤维织物/环氧预浸料,采用热压罐工艺在不同条件下制备了变厚度层板,并通过层板内部形貌、层板厚度、纤维含量、吸胶量、织物渗透率的测试分析,研究了变厚度层板的密实过程和纤维分布的影响因素.结果表明:密实过程中树脂的二维流动导致2种织物变厚度层板厚板区的纤维含量高于薄板区;G0827单向织物的面内渗透率与厚度方向渗透率比值大于G0803缎纹织物,造成G0827织物变厚度层板的纤维分布不均匀性更大;无吸胶材料的条件下层板内纤维分布均匀,说明吸胶材料内树脂的面内流动对层板的纤维分布有很大影响.
参考文献
| [1] | 孙秦,席德科,侯成义.变厚度多层介质结构的一种三维数值半解析方法[J].应用力学学报,1999,16(3):71-76.Sun Qin,Xi Deke,Hou Chengyi.A new 3-D numerical semianalytical algorithm for multiply composite structures with varied thickness[J].Chinese Journal of Applied Mechanics,1999,16(3):71-76. |
| [2] | Poon C Y,Ruiz C.Finite element analysis of a tapered composite[J].Composites Science and Technology,1994,51(3):429-440. |
| [3] | 顾轶卓,张佐光,李敏,等.复合材料变厚层板热压成型缺陷类型与成因实验研究[J].复合材料学报,2008,25(2):41-46.Gu Yizhuo,Zhang Zuoguang,Li Min,et al.Experimental study on type and cause of defects in variable thickness composite laminates during hot pressing proces[J].Acta Materiae Compositae Sinica,2008,25(2):41-46. |
| [4] | Loos A C,Springer G S.Curing of epoxy matrix composites[J].Journal of Composite Materials,1983,17(2):135-169. |
| [5] | Gutowski T G,Morigaki T,Cai Z.The consolidation of laminate composites[J].Journal of Composite Materials,1987,21(2):173-188. |
| [6] | Dave R,Kardos J L,Dudukovic M P.A model for resin flow during composite processing Ⅰ:General mathematical development[J].Polymer Composites,1987,8(1):29-38. |
| [7] | Dave R.A unified approach to modeling resin flow during composite processing[J].Journal of Composite Materials,1990,24(1):22-41. |
| [8] | Saunders R A,Lekakou C,Bader M G.Compression and microstrueture of fiber plain woven cloths in the processing of polymer composites[J].Composites Part A:Applied Science and Manufacturing,1998,29(4):443-454. |
| [9] | 简抗抗,张佐光,顾轶卓,等.不同纤维堆积状态下饱和渗透率实验研究[J].复合材料学报,2006,23(1):31-36.Jian Kangkang,Zhang Zuoguang,Gu Yizhuo,et al.Experimental research of saturated permeability with different fiber stacking states[J].Acta Materiae Compositae Sinica,2006,23(1):31-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%