同步采用无皂乳液聚合法和溶胶-凝胶法制备了聚丙烯酸酯/纳米SiO2复合材料,通过TEM、力学性能、DSC、TG和XRD等检测手段研究了不同有机硅烷偶联剂对聚丙烯酸酯/纳米SiO2复合材料性能的影响.结果表明,分别采用3-甲基丙烯酸氧丙基三甲氧基硅烷(MEMO)和乙烯基三甲氧基硅烷(VTMO)制备的纳米复合材料,力学性能随其用量的增加而同步增强增韧;TEM结果表明,采用MEMO和VTMO制备的聚丙烯酸酯/纳米SiO2复合材料中的纳米SiO2的粒径约20nm,且分布均匀;热性能结果表明,采用乙烯基三乙氧基硅烷(VTEO)制备的纳米复合材料的玻璃化温度(-8.1℃)和热裂解温度(350℃)最高;XRD结果表明,有机硅烷偶联剂的加入降低了纳米复合材料的结晶度.
参考文献
| [1] | Bauer F.;Glasel HJ.;Decker U.;Ernst H.;Freyer A.;Hartmann E. Sauerland V.;Mehnert R. .Trialkoxysilane grafting onto nanoparticles for the preparation of clear coat polyacrylate systems with excellent scratch performance [Review][J].Progress in Organic Coatings: An International Review Journal,2003(2):147-153. |
| [2] | 欧宝立,李笃信.SiO2大分子单体与苯乙烯共聚制备PS/SiO2纳米复合材料[J].中国科学B辑,2007(01):25-30. |
| [3] | 欧宝立,李笃信.表面修饰纳米SiO2与聚丙烯共混制备聚丙烯/SiO2纳米复合材料[J].材料导报,2006(z2):229-231. |
| [4] | Ma J Z;Hu J;Yang Z S .[J].Material and Manufure Process,2007,22(06):782-786. |
| [5] | 郑秋红,刘丰,李小红,丁涛,吴志申.可分散性纳米二氧化硅补强硅橡胶的性能[J].高分子材料科学与工程,2007(03):139-142. |
| [6] | 庞久寅,王春鹏,林明涛,储富祥.细乳液聚合制备纳米二氧化硅-丙烯酸酯复合乳液的研究[J].高分子材料科学与工程,2007(03):63-65. |
| [7] | Ma J Z;Hu J;Yang Z S .[J].Jnl Sol-Gel Sci Tech,2007,41(03):209-216. |
| [8] | 张卫国,王小燕,姚素薇,王宏智.纳米二氧化硅复合涂料的制备及其性能[J].化工学报,2006(11):2745-2749. |
| [9] | Qi D M;Bao Y Z;Weng Z X et al.[J].Polymer,2006,47:4622-4629. |
| [10] | Zeng Z;Yu J;Guo ZX .Preparation of polymer/silica composite nanoparticles bearing carboxyl groups on the surface via emulsifier-free emulsion copolymerization[J].Journal of Polymer Science, Part A. Polymer Chemistry,2005(13):2826-2835. |
| [11] | Ma J Z;Hu J;Zhang Z J .[J].European Polymer Journal,2007,43:4619-4177. |
| [12] | Qiao XG;Chen M;Zhou J;Wu LM .Synthesis of raspberry-like silica/polystyrene/silica multilayer hybrid particles via miniemulsion polymerization[J].Journal of Polymer Science, Part A. Polymer Chemistry,2007(6):1028-1037. |
| [13] | 姜立忠,战佳宇,武德珍,金日光.甲基丙烯酰氧基三甲氧基硅烷改性SiO2的制备[J].北京化工大学学报（自然科学版）,2007(03):287-289. |
| [14] | Zou W J;Peng J;Yang Y et al.[J].Materials Letters,2007,61:725-729. |
| [15] | Wang ZY;Han EH;Ke W .Effect of acrylic polymer and nanocomposite with nano-SiO2 on thermal degradation and fire resistance of APP-DPER-MEL coating[J].Polymer Degradation and Stability,2006(9):1937-1947. |
| [16] | Lee M S;Jo N M .[J].Journal of Sol-Gel Science and Technology,2002,24:175-180. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%