研究Na_2SiO_3 -NaOH体系电解液中Ce(NO_3)_3含量在0～0.20 g/L范围内变化时对ZAlSi12合金表面微弧氧化陶瓷层组织和厚度的影响.采用SEM、XRD分析微弧氧化处理后陶瓷层的表面形貌和相组成.结果表明:随着Ce(NO_3)_3含量增加,陶瓷氧化层厚度逐渐增大,电解液中Ce(NO_3)_3加入量0.15 g/L时可获得最大厚度为170 μm的陶瓷层;电解液中加入Ce(NO_3)_3后,膜层仍主要由α-Al_2O_3和γ-Al_2O_3相组成,但α-Al_2O_3相的相对含量增加.
Ceramic coatings were obtained by micro-arc oxidation (MAO) on surface of ZAlSi12 alloy in sodium silicate and sodium hydroxide electrolyte with addition of Ce(NO_3)_3.The effects of contents of Ce(No_3)_3 in the range of 0 ～ 0.20 g/L in the electrolyte on microstructure and thickness of the ceramic coatings were investigated.The surface morphology of the coatings was observed by SEM and phases of the coatings were analyzed by XRD.The results reveal that thickness of the coatings increases with the increase of the content of Ce (NO_3)_3 in the electrolyte to the maximum value of 170 μm when the content of Ce(NO_3)_3 is 0.15 g/L.The coatings formed in the electrolyte containing Ce(NO_3)_3 are still composed of α-Al_2O_3 and γ-Al_2O_3 phases, however, the amount of α-Al_2O_3 phase increases with the addition of Ce (NO_3)_3 in electrolyte.
参考文献
| [1] | Shi Zhiming.Preparation of Cordierite Ceramic Using Mixtures of Ce4+-Modified Amorphous Powder and Oxide Powders[J].稀土学报（英文版）,2006(z2):263-265. |
| [2] | B. Rajasekaran;S. Ganesh Sundara Raman;S. V. Joshi;G. Sundararajan .Effect of microarc oxidised layer thickness on plain fatigue and fretting fatigue behaviour of Al-Mg-Si alloy[J].International Journal of Fatigue,2008(7):1259-1266. |
| [3] | Voevodin A A;Yerokhin A L;Lyubimov V V et al.Characterization of wear protective Al-Si-O coatings formed on Al-based alloys by microare discharge treatment[J].Surface and Coatings Technology,1996,86 -87:516-5521. |
| [4] | 薛文斌,华铭,施修龄,田华.铸造铝合金微弧氧化膜的生长动力学及耐蚀性能[J].硅酸盐学报,2007(06):731-735. |
| [5] | 段关文,李金富,王拥军,徐志雄.铝合金的微弧氧化研究[J].表面技术,2007(03):30-33. |
| [6] | 李凌杰,李荻,张胜涛,雷惊雷.稀土盐对铝合金阳极化过程的影响[J].中国稀土学报,2001(04):350-353. |
| [7] | 徐俊,胡正前,马晋,杜广建.电解液参数对铝合金微弧氧化膜层质量的影响[J].电镀与涂饰,2006(10):43-45,49. |
| [8] | 梁戈,赵仁兵,蒋百灵.电解液参数对铝合金微弧氧化黑色陶瓷膜性能的影响[J].材料热处理学报,2006(05):91-94. |
| [9] | Xue WB .Features of film growth during plasma anodizing of Al 2024/SiC metal matrix composite[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(18):6195-6200. |
| [10] | V.B. Santos;J.-C. M'Peko;M. Mir .Microstructural, structural and electrical properties of La~(3+)-modified ferroelectric ceramics[J].Journal of the European Ceramic Society,2009(4):751-756. |
| [11] | LI Jianzhong,TIAN Yanwen,CUI Zuoxing,HUANG Zhenqi.Effects of rare earths on the microarc oxidation of a magnesium alloy[J].稀有金属(英文版),2008(01):50-54. |
| [12] | 颜建辉,刘锦平.稀土元素在铝合金阳极氧化后处理中的应用[J].电镀与涂饰,2002(01):19-22. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%