本文借助光学显微镜,透射电镜和扫描电镜,分析了HT20-40灰铸铁于激光熔化处理后表面显微组织特征,并探讨其形成原因。
The microstructures of the laser hardened layer on the gray cast iron HT20--40 af-ter laser melting processing were examined by optical microscopy, transmission electron microscopy(TEM) and scanning electron microscopy (SEM). Experimental results showed that a structurewith dendritic (M+A') and interdendriticly iaminal transformed ledeburite (M+A'+Fe_3C) wasproduced after laser melting processing. The martensite was a mixture of dislocation martensite andtwin martensite. Dislocation pile-ups and twins were found to exist in the residual austenite.Microsegregation of composition and heterogeneity of microstructure were also apparent after lasermelting processing.