在500MPa、900℃和300MPa、1000℃两种环境条件下,通过实验研究了[001]、[011]、[111]三种取向的镍基单晶合金DD6的蠕变特性及断裂机理。结果表明：DD6单晶高温合金蠕变性能具有明显的晶体取向相关性,在相同的温度和应力条件下,三种取向的单晶合金寿命差别很大,温度是影响[001]取向单晶合金蠕变寿命的主要因素,而应力则是影响[011]和[111]取向单晶合金蠕变寿命的主要原因。同时,晶体取向和实验条件的不同,都会使最小蠕变率发生变化,随着温度的升高,不同取向晶体的各向异性减弱,相同条件下,[111]取向最大蠕变量最大,[001]取向次之,[011]取向最小。而晶体取向对断裂机理有直接的影响,[001]、[111]取向DD6单晶合金的断裂是由微孔引起的断裂,[011]取向的DD6单晶合金在900℃、500MPa条件下的蠕变断裂为滑移断裂,1000℃、300MPa条件下的断裂为滑移面断裂和韧窝断裂二者兼有的混合型断裂。
Creep properties of Ni-base single crystals with , and orientations were studied under two loading conditions 500MPa,900℃ and 300MPa,1000℃.The results show that the creep properties of DD6 single crystals are strongly orientation dependent.Under the same temperature and stress conditions,fracture life is obviously different among the three orientations.Temperature is the major influence factor for the creep life of the crystals with orientation,while stress is the main reason for the creep life of the crystals with and orientations.The minimum creep rate is related with both of the loading condition and the crystal orientation.Anisotropy will reduce in all the crystals at higher temperature.Creep deformation decreases in the order of , and orientation.The rupture mode of the specimens with and orientations is microporous.For the orientational specimen,at 500MPa and 900℃,the fracture is induced by the slipping.At 300MPa and 1000℃,the fracture mode is the combination of slipping and dimples.
参考文献
| [1] | J.L. Liu;T. Jin;X.F. Sun;J.H. Zhang;H.R. Guan;Z.Q. Hu .Anisotropy of stress rupture properties of a Ni base single crystal superalloy at two temperatures[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):277-284. |
| [2] | 王开国,李嘉荣,刘世忠,曹春晓.DD6单晶高温合金980℃蠕变性能研究[J].材料工程,2004(08):7-11. |
| [3] | 王开国,李嘉荣,刘世忠,曹春晓.DD6单晶高温合金980℃蠕变性能研究[J].材料工程,2004(08):7-11. |
| [4] | Kassner ME;Hayes TA .Creep cavitation in metals[J].International Journal of Plasticity,2003(10):1715-1748. |
| [5] | Mackay.R.A;Maier.R.D .The influence of orientation on the stress rupture properties of nickel-based superalloy single crystals[J].Metallurgical and Materials Transactions,1982,13A:1747-17551. |
| [6] | Sass.V;Glatzel.U et al.Anisotropic creep properties of the nickel-base superalloy CMSX-4[J].Acta Materialia,1996,44:1967-19771. |
| [7] | 王自强;祝平.塑性细观力学[M].北京:科学出版社,1995 |
| [8] | S. S. K. Gunturi;D. W. MacLachlan;D. M. Knowles .Anisotropic creep in CMSX-4 in orientations distant from <001>[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):289-298. |
| [9] | 赵明汉;张继;冯滁.高温合金断口分析图谱[M].北京:冶金工业出版社,2006 |
| [10] | 韩梅,骆宇时.DD3单晶高温合金的高温蠕变断裂行为[J].失效分析与预防,2008(03):28-31. |
| [11] | Kassner ME;Hayes TA .Creep cavitation in metals[J].International Journal of Plasticity,2003(10):1715-1748. |
| [12] | T.Schacht;N.Untermann .crystallographic orientation on E.Steck.The influence of the deformation behaviour of single crystals containing microvoid[J].International Journal of Plasticity,2003,19:1605-1626. |
| [13] | Derek Hull.断口形貌学[M].北京:科学出版社,2009 |
| [14] | 李嘉荣,史振学,袁海龙,刘世忠,赵金乾,韩梅,刘维维.单晶高温合金DD6拉伸性能各向异性[J].材料工程,2008(12):6-10. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%