T4003 and Q450NQR1, as well as Nirosta 4003 and Q450NQR1 dissimilar metal joints were welded by ER-309 welding wire. The microstructure oftheir base metal and joint were analyzed by metallographic approach. The corrosion resistance of base metal and joints was evaluated by salt fog and electrochemical corrosion tests. The results demonstrated that as far as the similar metal joints of Nirosta 4003 and T4003 was concerned, the corrosion resistance of welding line was much better than that of base metal. However, the corrosion resistance of heat affected zone (HAZ) became worse. In the case of dissimilar metal joints of Nirosta 4003 and Q450NQR1, as well as T4003 and Q450NQR1, the corrosion resistance of welding line was reduced. Under salt spray condition, the corrosion resistance of welding line and base metal of similar metal joints was comparative. However, the dissimilar metal joints of Nirosta 4003 and Q450NQR1, as well as T4003 and Q450NQR1 exhibited obvious corrosion. Especially, abundant corrosion pits were found near the side of Q450NQR1. Due to the different corrosion voltages of stainless steel, weathering steel, HAZ, and welding line, a series of micro-batteries were formed in the dissimilar metal joints, which worsened the corrosion of weathering steel.

关键词: 铁素体不锈钢 , weathering steel , dissimilar metal joint , corrosion resistance

6082铝合金FSW焊接接头的组织与力学性能研究

许鸿吉 , 唐海鹰 , 解鹏 , 谢明 , 焦建强

材料导报

通过拉伸、弯曲、硬度试验以及金相分析等对6082铝合金FSW焊接接头的力学性能与显微组织进行了研究.结果表明,以转速1500r/min、焊速600mm/min的参数焊接6082铝合金时,其接头具有较好的抗拉性能,板厚6mm和3mm焊接接头的抗拉强度分别为母材的77.23%和78.86%;正弯断裂位置集中在HAZ处,角度约90°,背弯断裂位置集中在焊缝中心,角度较小;硬度试验显示两侧热影响区处均软化;6082铝合金FSW焊接接头焊核区和轴肩影响区发生了动态再结晶,形成了细小的等轴晶组织,热机影响区组织发生了较大程度的变形;热影响区仅受热循环的作用,组织略有粗化.

关键词: 6082铝合金 , 焊接接头 , 组织 , 力学性能

14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能

蒋立明 , 郑华勇 , 许鸿吉 , 谢明

机械工程材料

采用E551T1-Ni2药芯焊丝对Q345E钢与14NiCrMo10 6V钢进行焊接,并通过室温拉伸、弯曲、冲击、硬度试验以及金相分析等对焊接接头的力学性能与显微组织进行了研究。结果表明：采用此焊丝可以获得拉伸、弯曲和冲击性能均良好的焊接接头,焊缝硬度在200～250HV之间;焊缝处晶界组织为先共析铁素体、少量无碳贝氏体（从晶界伸向晶内）,晶内为针状铁素体与珠光体,个别部位有粒状贝氏体;Q345E钢侧热影响区与焊缝过渡区的组织为沿晶界析出的块状先共析铁素体和向晶内生长的条状铁素体以及少量的珠光体和贝氏体;14NiCrMo10 6V钢侧热影响区与焊缝过渡区的组织为板条状马氏体。

关键词: Q345E钢 , 14NiCrMo10 , 6V钢 , 焊接接头 , 力学性能

S355J2W耐候钢的耐腐蚀性能

鲁二敬 , 卢峰华 , 许鸿吉 , 谢明 , 钮旭晶

机械工程材料

通过周期浸润腐蚀试验，对比研究了S355．12W耐候钢和Q345R低合金钢在NariSOs溶液中的耐腐蚀性能，并用扫描电镜对腐蚀产物进行了观察和分析。结果表明：在相同试验条件下，S355J2W耐候钢的腐蚀速率低于Q345R钢的；S355J2W耐候钢会在表面形成黑褐色锈层，而Q345R钢表面形成橘红色易剥落的疏松锈层；S355J2W耐候钢腐蚀产物微观形貌为沿放射性方向生长的针状晶体，Q345R钢为颗粒状聚合物堆积而成，形状无规则，颗粒之间有较大的空隙。

关键词: S355J2W耐候钢 , 周期浸润腐蚀试验 , 耐腐蚀性能

05CuPCrNi钢等离子弧焊焊接接头的组织与力学性能

李晨 , 许鸿吉 , 谢明 , 董强

钢铁 doi:10.13228/j.boyuan.issn0449-749x.20160016

为了研究等离子弧焊在焊接薄板耐候钢时的优越性，对2 mm厚05CuPCrNi耐大气腐蚀钢分别进行等离子弧焊与MAG焊(熔化极活性气体保护电弧焊)对接焊接，然后对焊接接头分别进行拉伸、弯曲、金相、硬度等试验，通过与MAG焊焊接接头的组织与力学性能对比，结果表明，与MAG焊相比，等离子弧焊时05CuPCrNi耐大气腐蚀钢焊接接头强度相对提高约6%，焊接接头组织为更均匀且细小的铁素体＋珠光体，并无MAG焊中出现的粗大块状铁素体及贝氏体，焊接热影响区较小，焊接接头弯曲性能良好，硬度值及硬度分布情况与MAG相近且无软化现象。

关键词: 05CuPCrNi耐大气腐蚀钢 , 等离子弧焊 , MAG焊 , 金相组织 , 力学性能

焊接工艺参数对A-TIG焊的焊缝成形影响

武丹 , 裘荣鹏 , 许鸿吉

兵器材料科学与工程 doi:10.3969/j.issn.1004-244X.2004.04.007

研究了奥氏体不锈钢 A- TIG焊和普通 TIG焊在焊接工艺参数不同时对其焊缝成形的影响.试验结果表明:在相同的焊接工艺参数下,与普通 TIG焊相比,涂活性化焊剂的 A- TIG焊的焊缝熔深有显著增加,而熔宽明显减少;在涂敷的活性化焊剂成分和涂层厚度相同时,与普通 TIG焊一样, A- TIG焊的焊缝熔深也是随焊接电流的增加或焊接速度的减少而增大的.

关键词: A- TIG焊 , 熔深 , 活性化焊剂 , 焊接工艺参数

06Cr19Ni10不锈钢CMT焊接接头组织与性能的研究

董强 , 许鸿吉 , 谢明

兵器材料科学与工程

通过拉伸试验、弯曲试验、脉动拉伸疲劳试验、硬度试验以及金相显微组织分析,对1.5 mm厚06Cr19Ni10不锈钢的冷金属过渡焊焊接接头的组织与性能进行研究.结果表明:06Cr 19Ni 10不锈钢冷金属过渡焊焊缝的δ铁素体含量约为8.0％;焊缝组织为网状、骨架状δ铁索体均匀分布在奥氏体基体上;冷金属过渡焊焊接接头具有良好的弯曲性能、拉伸性能,平均抗拉强度为684 MPa;焊缝中心硬度值为230HV,硬度值由熔合线向焊缝中心逐渐提高;焊接接头(保留余高)的疲劳强度为251 MPa.

关键词: 06Cr19Ni10不锈钢 , CMT , 焊接接头 , 组织与性能

确定雷达罩设计许用值的方法研究

周春苹 , 李兴德 , 朱杉

玻璃钢/复合材料

按照CCAR25.613条款“材料与结构许用值”的要求,民用飞机雷达罩需进行许用值设计.本文通过研究确定了进行雷达罩玻璃纤维复合材料设计许用值试验的试验项目、试验采用的标准、试验环境、试验件数量以及试验数据的处理方法等,并将采用ASTM标准测试得到的许用值试验数据与用GB标准得到的测试数据进行了比较.结果表明,按照ASTM标准进行玻璃纤维复合材料结构设计许用值试验得到的数据分散性小,许用值的测试数据高,避免了采用国内标准导致的性能数据低的情况.该设计许用值已成功应用于新型涡扇支线飞机雷达罩的设计和静力试验.

关键词: 雷达罩 , 玻璃纤维复合材料 , 结构许用值