金属学报(英文版)
Starting from cheap inorganic salts , ultrafine P L Z T po w ders were synthesized by a co pre cipitation m ethod . The results show that the precursor precipitate obtained by the co precipita tion method transfor ms co m pletely to P L Z T phase by calcining at 420 ℃ for 4 hours , about300 ℃low er than the nor m al transform ation te m perature of P L Z T obtained by m ixed oxidemethod . The effect of residual N H4 N O3 in the precursor precipitate on transfor m ation te m perature of the P L Z Tpow der w as investigated . The residual N H4 N O3 in the precursor po w der can reduce further the P L Z Ttransfor m ation tem perature to about 300 ℃, but a sm alla mount of Zr O2 and Pb Ti O3 re m ained . By a proper control of the synthesizing route , a P L Z T po w der with a pri m ary particle size of 10 n m and an agglom eration size of 0 3 μm hasbeen produced .
关键词:
P L Z T
,
null
,
null
谭文一
,
胡飞
,
张锋刚
机械工程材料
用光学显微镜、显微硬度计、扫描电镜及三点弯曲疲劳试验机等研究了B级铸钢与Q450NQR1钢焊接接头的组织与性能.结果表明:其焊缝组织为细小树枝状铁素体+珠光体,B级铸钢侧热影响区近焊缝区有马氏体组织;焊缝硬度达240～295 HV,高于两侧母材的;B级铸钢侧热影响区硬度波动最大,硬度也最高,达370 HV;与焊态相比,焊趾处打磨可使接头疲劳强度提高12%,整体喷丸可提高15%;在循环载荷作用下,焊接接头多在焊根处起裂.
关键词:
B级铸钢
,
Q450NQR1钢
,
焊接接头
,
疲劳性能
夏金魁
,
李相付
,
曹龙琼
,
黄道昌
,
陈敏明
连铸
doi:10.13228/j.boyuan.issn1005-4006.20150143
在降本增效的背景下,炼钢厂生产Q235B连铸板坯时,进行了成分优化和工艺流程简化,按照新工艺生产后,Q235B连铸板坯出现较多内部裂纹.经数据统计、低倍检验和扫描电镜分析后表明,Q235B连铸板坯产生内部裂纹主要是由钢水脱氧不良、夹杂物含量高,拉速和二次冷却控制不合理等原因造成,通过深脱氧、延长氩站软吹氩时间及降低浇铸速度等措施,新工艺在w[Mn]/w[S]≤30条件下,Q235B连铸板坯内部裂纹发生率降至原工艺水平.
关键词:
脱氧
,
吹氩
,
拉速
,
二次冷却
卢军辉
,
王晓春
,
刘家琪
,
张成武
,
仇圣桃
,
朴峰云
物理测试
为了考察开发钢Q450NQR1的耐候性,对其分别进行了实验室周期浸润试验和大气暴晒试验,试验结果表明,实验室周期浸润试验中,144h腐蚀率相对Q345B减少了1/3,且Q450NQR1锈层中稳定的α-FeOOH含量较高,而Q345B钢较低;大气暴晒试验中,腐蚀初期Q450NQR1钢试样腐蚀率稍大一些,腐蚀后期,其表面形成稳定的致密锈层后,Q450NQR1钢的耐腐蚀性能开始体现.
关键词:
耐候钢
,
货车车厢
,
X射线衍射
,
大气腐蚀
,
锈层
潘军
,
邓南阳
,
胡惠华
,
赵斌
,
薛顺
,
王义平
钢铁研究
介绍了马钢第三钢轧总厂为降低低合金钢Q345B合金消耗所采取的增C降Mn冶炼工艺.结果表明:在确保钢材力学性能的前提下,采取增C降Mn冶炼工艺,降低低合金钢Q345B合金消耗的方法是可行的,w(C)每提高o.o1％,w(Mn)可降低0.06％.
关键词:
低合金钢
,
力学性能
,
铁合金消耗
Zhaoyang ZENG
,
Lide ZHANG
,
Xiaohong YAN
材料科学技术（英文）
Ballistic transport of Q1D electrons through multiple magnetic barriers is investigated. It is shown that ballistic conductance peaks disappear progressively with the increase of the oscillation frequency of the confining parabolic potential.
关键词:
吴光亮
,
孙彦辉
,
周春泉
,
蔡开科
,
李正邦
钢铁
采用Gleeble1500对CSP连铸坯(Q235B)进行了热模拟研究;分析了试验温度为800、900、1100℃的横、纵向试样的组织和断口形貌及晶界的元素偏析和夹杂物.结果表明:CSP生产的Q235B连铸坯在600～1 320℃间存在2个脆性温度区,即1 320～1 200℃的第Ⅰ脆性温度区域和600～1 000℃的第Ⅲ脆性温度区域;在1 000～1 200℃温度范围内,Q235B钢具有良好的塑性.而在800℃时试样的Z值为8.46%.Q235B钢的第Ⅲ类脆性区的脆化原因:一方面是形变诱导铁素体呈网状析出,产生应力集中;另一方面是奥氏体低温区域发生的氮化物(AlN)析出产生的晶界脆化.AlN在奥氏体晶界的析出,在拉伸力的作用下易形成应力集中源,使空洞形成、长大并聚集,是铸坯裂纹源.
关键词:
CSP板坯
,
Q235B
,
高温力学性能
,
扫描电镜
宿成
,
董方
钢铁
为了研究含V、Ti、Nb微合金Q345B结构钢的高温塑性,利用Gleeble-1500D热模拟试验机对其进行热拉伸试验,分析了在应变速率为1.5×10-3s-1、变形温度700～1 300℃（Δt=100℃）变形条件下的断裂强度和断面收缩率随温度的变化情况。确定Q345B结构钢存在两个脆性区间,即第Ⅰ脆性温度区间为熔点温度1 300℃,第Ⅲ脆性温度区间为850～740℃。通过扫描电镜和光学显微镜对断口形貌及其组织进行了观察,明确了断裂原因,为连铸生产提供一定的理论指导。
关键词:
微合金钢
,
高温塑性
,
断口形貌
艾西
,
孙彦辉
,
曾亚南
,
刘瑞宁
,
刘泳
钢铁
doi:10.7513/j.issn.1004-7638.2014.04.020
采用Gleeble 1500热模拟机对Q345B钢在1×10-4 s-1和1×10-3 s-1应变速率下的热塑性进行了研究.研究表明:在1×10-4 s-1的应变速率下,试样在600 ～TL ℃的温度范围内存在两个脆性区,即高温脆性区,为1 217～TL℃,低温脆性区,为600～930℃;在1×10-3 s-1的应变速率下,试样在600～TL ℃的温度范围内不存在高温脆性区,仅存在低温脆性区,为600～915℃.影响Q345B钢热塑性的主要因素是S偏析、应变速率、铁素体的析出以及细小的AlN粒子的析出.
关键词:
低碳钢
,
热塑性
,
应变速率
,
析出物