BINDING ENERGY OF SHALLOW DONOR IN In_xGa_(1-x)As/GaAsSTRAINED QUANTUM WELL

J. H. Xing(Department of Physics , Liaoning University , Shenyang 110036 , China)H.L. Huang(Department of Electronic Science and Engineering , Liaoning University , Shenyang 110036 , China)

金属学报(英文版)

The effect of the dielectric mismatch between the well and the barrier materials on the binding energies of shallow donor has been investigated in Inx Ga1-xAs/GaAsstrained quantum well. The binding energies as a function of the well widths and impurity positions in the well and the barriers are obtained by using a variational method. Calculation results show that the effect of the dielectric mismatch is quite sizable and such effect is larger for off-center impurity positions,but the effect of the lattice mismatch is small in general.

关键词: quantum well , null

STATISTICAL EVALUATION OF CRITICAL INCLUSION FACTOR FOR SECONDARY RECRYSTALLIZATON IN 3%Si STEEL Lecturer,Department of Materials Engineering,Southwestern Jiaotong University,Chengdu 610031,China

LI Shuchen Southwestern Jiaotong University , Chengdu , ChinaCHEN Mengzhe KE Jun University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

On the basis of statistical data of MnS in the conventional 3% Si steel sheeets after various annealing processes,the critical inclusion factor has been evaluated to be 20 mm~(-1).The inhi- bition of MnS to grain growth has been exactly described.

关键词: 3%Si steel , null , null

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null