Nanocrystalline powders in the Ni-Ti and Ni-Cr systems were prepared by mechanical alloying (MA) of elemental crystalline powders in an inert atmosphere. The microstructure of the mechanically alloyed powders were characterized by XRD and TEM. The ball-milling process results in a drastic decrease of the crystallite size to the nanometer scale. X-ray diffraction analysis reveals that in the Ni-Cr system, no diffraction peaks from NiCr compound were observed even after 20 h of ball milling; while the lattice parameter of Ni increased with the milling time. In the Ni-Ti system, amorphous alloy was formed. Crystalline intermetallic compounds were obtained by post heat treatment of the amorphous alloy.The crystallization temperature of the amorphous NiTi alloy was obtained be DSC measurement.
关键词:
B.W. Wang
,
H. Shen
金属学报(英文版)
Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactivesputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as targetmaterial and copper sheets as substrate. Using SEM, Spectrophotometer and Talystepto analyze the relations between the selective characteristic and the structure, theformation and the thickness of the thin films. The aim is to obtain good solar selectivethin films with high absorptance and low emittance, which is applied to flat plate solarheat collectors.
关键词:
solar selective thin film
,
null
,
null
,
null