Baode SUN
,
Yaohe ZHOU
材料科学技术（英文）
Cylinder-like in-situ Al/24Si FGMs were produced by using electromagnetic separating process. Si primary phase reinforced layer with volume fraction as high as 16 pct was formed at the outer region of the cylinder-like samples where the local hardness and wear resistance were enhanced remarkably. Moreover, both of strength and ductility in the inner region provided insurance of reliable strength for this as-cast gradient material. It indicated that general mechanical properties such as good wear resistance at the outer region and good ductility in the central part could be obtained with the optimized redistribution of the Si primary particles under the electromagnetic force.
关键词:
FGMs
,
null
,
null
Zhenming XU
,
Tianxiao LI
,
Da SHU
,
Yaohe ZHOU
材料科学技术（英文）
Electromagnetic filtration primary Fe-rich phases (complex compound of AlFeSiMn) from Al-Si alloy melt containing 1.2 wt pet Fe have been studied by theoretical analysis and on a self-designed electromagnetic filtration equipment. The principle of the electromagnetic filtration is that the EMF (electromagnetic force) scarcely acts on the primary Fe-rich phases having low electric conductivity, which are then moved in the direction opposite to that of the EMF. Experimental results show that the primary Fe-rich phases are separated from AI-Si alloy melt and are collected in the filter while the melt is in horizontal flow. The removal efficiency of the primary iron-phases (eta) calculated is less as the greatest flow velocity of the melt (u(M)) and the height of the filter (2h) are larger, while it becomes larger as EMF, operating distance of electromagnetic force (x) and particle size (d(p)) become larger. It has been confirmed that the primary iron-phases larger than 20 mum can be removed efficiently by theoretical analysis and experiments. This new technique is high efficient and available for continuously flowing melts as compared with natural settling and filtration methods, which offer a Possibility for recycling high quality aluminum alloys.
关键词:
Tianxiao LI
,
Zhenming XU
,
Baode SUN
,
Da SHU
,
Yaohe ZHOU
材料科学技术（英文）
Physical simulation is used to study the movement of nonmetallic particles in Al melt in electromagnetic field. It is found that the terminal velocity of particles in different Reynolds number range has different functions. By confirming drag force coefficient of nonmetallic particles with Reynolds number in the range of 0.2 similar to 10 and 10 similar to 25 respectively, two functions of terminal velocity for spherical nonmetallic particles have been got accordingly, which provide a theoretical basis for separating nonmetallic inclusions from Al melt in electromagnetic field.
关键词:
余万华
,
高山
,
刘飞
,
刘力哲
,
孙理
,
刘澄
材料热处理学报
对80级帘线钢C82DA和90级帘线钢C92DA化学成分进行检测,分析化学成分中合金元素差异对其相变的影响.采用光学显微镜、扫描电镜(SEM)、热膨胀仪和显微硬度仪,对比研究C82DA和C92DA的相变规律;相同热处理条件下的相变点、显微组织、珠光体片层间距;以及通过等温转变实验得到的相变动力学方程,并对参数n值和k值关系进行对比.结果表明:C92DA钢中的C、Si、Cr含量要高于C82DA,因此C92DA的片层间距要比C82DA细密,C92DA的n值要比C82DA大.这些结果对制定生产工艺和构建在线质量预报模型提供了基础数据.
关键词:
帘线钢
,
高碳钢
,
冷速
,
显微组织
,
相变模型
Materials Transactions
Effects of phosphorus microalloying on the microstructure and mechanical properties of direct-aging DA761 alloy have been studied. The aim of this work is to find a new way to develop a higher performance of wrought superalloy. The optimum addition of phosphorus in DA761 alloy is determined by investigating effects of phosphorus and boron on the microstructure and properties of DA761 alloy, that are compared to GH761 alloy treated by standard heat treatment. The stability of microstructure and properties of fine-grain DA761 alloy with optimum content of phosphorus is proved by studying the evolution of microstructure and properties of the alloy after long-term high temperature ageing. The practicability of phosphorus microalloying in improving the mechanical properties of DA761 alloy is verified by smelting a 500 kg ingot and detecting the microstructure and properties of billet near the size of engine disk. The results verify the phosphorus microalloying and fine-grain direct aging treatment in improving commercial GH761 alloy. Mechanism of phosphorus microalloying is also discussed. [doi: 10.2320/matertrans.MF200908]
关键词:
phosphorus;GH761 alloy;fine-grain treatment;mechanical property;trace-elements
陈篪
金属学报
本文证明我们所建议的关系: (da/dN)-C[(△K)~2-K_2~2/K_1~2-(△K)~2]~p能够很好地表达R=(K_(min)/K_(max))=常数时(da/dN)随△K的全部变化,其中P值在1左右,C约在3×10~(-3)—10~(-2)毫米/周之间。
关键词:
材料科学技术（英文）
Lower content of carbon can further improve the stress rupture life of p-modified DA 718 alloy up to more than 270%. Meanwhile, the ductility of the alloy decreased a little. More boron atoms dissociate due to decreasing carbon content and interact with phosphorus which brings the longer stress rupture life of the alloy. Less carbon may induce more phosphorus segregating in the grain boundary and result in brittleness.
关键词:
DA 718 alloy;carbon;phosphorus;phosphorus;segregation;superalloy
李淑兰
,
杨玉芬
兵器材料科学与工程
doi:10.3969/j.issn.1004-244X.2008.03.016
在介绍40CrMnSiMoVA钢的力学性能和试验条件基础上,根据金属材料疲劳裂纹扩展的统计分析方法,求出Pa-N和P-da/dN-△k曲线,并对不同应力比条件下的试验数据进行可靠性分析和比较,探讨中值da/dN-△k曲线和99.9%可靠度dddN-△k曲线的变化规律.研究结果表明,P-da/dN-△k曲线与应力比有很强的相关性,随着应力比增强,裂纹扩展速率增加.当可靠度要求增加时,这种趋势更明显.根据研究结果,恰当地考虑40CrMnSiMoVA钢对于不同应力比的影响,便于进行概率断裂力学分析.
关键词:
断裂
,
40CrMnSiMOVA钢
,
P-da/dN-△k曲线
,
应力比
于艳
,
刘鹏涛
,
蹇锡高
,
刘程
,
张元红
,
洪定一
,
李扬
,
吕占霞
高分子材料科学与工程
由自制二胺1,2-二氢-2-(4-氨基苯基)-4-[4-(4-氨基苯氧基)-苯基]-二氮杂萘-1-酮(DHPZ-DA)、4,4'-二氨基二苯醚(DAPE)和对苯二胺(PPD)与2,6-萘二酸(NDA)进行共缩聚反应,改变不同二胺的配比,所得聚芳酰胺树脂特征粘度为0.24 dL/g～2.78 dL/g ;以FT-IR、1H-NMR手段分析了聚合物的结构;用DSC、TGA手段研究了聚合物的耐热性能.结果表明,该类聚合物具有较高的玻璃化转变温度(280 ℃以上);氮气气氛中5%热失重温度在450 ℃以上;当DHPZ-DA+DAPE在二胺中比例达70%时能溶于NMP中,当DHPZ-DA+DAPE含量达80%时能溶于DMAc、DMF等非质子极性溶剂中.
关键词:
聚芳酰胺
,
2,6-萘二酸
,
耐热性
,
可溶性
陈汉存
,
刘正义
,
庄育智
中国腐蚀与防护学报
水介质会延迟疲劳裂纹的扩展,此作用随介质中氧浓度的增加而增强,这是由于裂纹内的腐蚀产物以及粗糙的断口表面促使裂纹提早闭合。文中还用裂纹尖端氧浓度计算公式来解释水介质中da/dN的变化规律。