The corrosion resistance of 2024 Al and SiC particle reinforced 2024 Al metal matrix composite (SiCp/2024Al MMC) in 3.5% NaCl solution was investigated with electrochemical method and immersion test, and the corrosion protection of sulfuric acid anodized coatings on both materials was evaluated by electrochemical impedance spectroscopy. The results showed that the SiCp/2024Al MMC is more susceptible to corrosion than its matrix alloy in 3.5% NaCl. For 2024Al, the anodized coating provides excellent corrosion resistance to 3.5% NaCl.The anodized coating on the SiCp/2024Al provides satisfactory corrosion protection, but it is not as effective as that for 2024Al because the structure of the anodized layer is affected by the SiC particulates.
关键词:
2024 Al
,
null
,
null
,
null
Chunlin HE
,
Changsheng LIU
,
Fengqin LI
,
Qingkui CAI Zhiming SHI
,
Liqing CHEN
,
Jing BI
材料科学技术（英文）
The influences of volume fraction and particle size of SiC particulate reinforcements on the corrosion characteristics of SiCp/2024 Al metal matrix composites in aerated 3.5 wt pct NaCl aqueous solution were investigated. The electrochemical behavior was investigated by potentiodynamic polarization and electrochemical impedance spectroscopy, the general corrosion behavior of the composites was studied further by immersion tests. The results showed that pitting susceptibility was about the same for the composites and the alloy. The corrosion potentials were also independent of SiC phase. The corrosion resistance for the composites decreased as the volume fraction increased or particle size decreased.
关键词:
SiCp/2024Al matrix composites
,
null
,
null
李志宏
,
柳卫平
,
白希祥
,
郭冰
,
连钢
,
颜胜权
,
王宝祥
,
陆昀
,
曾晟
,
苏俊
原子核物理评论
doi:10.3969/j.issn.1007-4627.2005.01.006
利用8Li次级束测量了质心系能量7.8 MeV 2H(8Li, 9Li)1H反应的角分布, 导出了8Li(d, p)9Li反应的天体物理S因子及9Li→8Li+n虚衰变的渐近归一化系数.
关键词:
8Li(d,p)9Li反应
,
角分布
,
天体物理S因子
,
渐近归一化系数
HUANG Jianshun CHEN Junming Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai
,
China Research Associate
,
Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai 200050
,
China
金属学报(英文版)
Crystal structure of γ-Li_xFe_2O_3,inserted Li electrochemically,was studied by Moss- bauer spectroscopy together with X-ray diffraction,XPS and electrochemical method,On the insertion of Li at low current density,the crystal structure is keeping original spinel; while at higher current density or by thermal activation,owing to violent movement of Li~+ ions,part of crystal structure transforms into rock type similar to face-centered cubic structure of ferrous oxide.The transition channels during insertion of Li~+ ions and limitation of Li~+ ions inserted were discussed.
关键词:
null
,
null
,
null
Journal of Materials Research
The effect of Li(3)N additive on the Li-Mg-N-H system was examined with respect to the reversible dehydrogenation performance. Screening Study with varying Li(3)N additions (5, 10, 20, and 30 mol%) demonstrates that all are effective for improving the hydrogen desorption capacity. Optimally, incorporation of 10 mol% Li(3)N improves the practical capacity from 3.9 wt% to approximately 4.7 wt% hydrogen at 200 degrees C, which drives the dehydrogenation reaction toward completion. Moreover, the capacity enhancement persists well over 10 de-/rehydrogenation cycles. Systematic x-ray diffraction examinations indicate that Li(3)N additive transforms into LiNH(2) and LiH phases and remains during hydrogen cycling. Combined structure/property investigations suggest that the LiNH(2) "seeding" should be responsible for the capacity enhancement, which reduces the kinetic barrier associated with the nucleation of intermediate LiNH(2). In addition, the concurrent incorporation of LiH is effective for mitigating the ammonia release.
关键词:
complex hydrides;improvement;mixtures;imides;amide;h-2
MANG Weishi WANG Guozhi ZHANG Yongchang HU Zhuangqi SHI Changxu Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China Yongchang Associate Professor
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
A rapidly solidified microcrystalline Al-Li-Cu-Mg-Zr alloy and its superplasicity have been investigated.An optimum tensile elongation of 585% was obtained at 540℃ and strain rate 1.67×10~(-2)s~(-1).The superplastic Al-Li alloy is manufaetured using thermomechanical pro- cessing:solution,overaging,warm rolling and recrystallization.Microstructural changes in thermomechanical processing and cavitation occurred during superplastic deformation have been observed.The superplastic failure of alloy may be caused mainly by nucleation and growth of cavities as well as the linkage around grains.
关键词:
superplasticity
,
null
,
null
,
null
Zhijian LIU
,
Zhiyou LI
,
Wei DUAN
,
Xuanhui QU
,
Baiyun HUANG
,
Siqi ZHANG
材料科学技术（英文）
A LI-B alloy has been prepared using a pretreated amorphous B powder and pure Li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstructure and the discharge characteristic of the materials have been investigated. Results show that the problem of temperature control in synthesis would be modified by means of continual addition of B powder, the Li7B6 would be more finery distributed in the metal Li by means of intensified stirring. The discharge characteristic of the Li-B alloy using amorphous B as starting materials is almost the same with that of using crystalline B.
关键词: