MICROSTRUCTURE AND COMPRESSIVE PROPERTIES OF NiAl-TiB_2 PARTICULATE COMPOSITES

XING Zhanping* , GUO Jianting , HU Zhuangqi , AN Geying*Institute of Metal Research , Chinese Academy of Sciences , Shenyang , China * Harbin Institute of Technology , Harbin , China

金属学报(英文版)

Ni-50at.%A1 matrix composites containing 0 to 20v.% TiB2 particles have been successfully fabricated by HPES technique. The results show that the Vickers hardness at room temperature and the compressive yield strength from room temperature to 1000℃ of the composites increase with increasing volume fraction of the strengthening phase. Especially, the yield strength of NiAl-20TiB2 was approximately twice as high as that of unreinforced NiAl. The ductility of the composites at room temperature is also superior to the monolithic NiAl.

关键词: intermetallic matrix composite , null , null , null , null

CHARACTERIZATION OF MECHANICALLY ALLOYED Ni-Al-Ti COMPOUNDS

LIU Zhiguang , GUO Jianting , HU Zhuangqi (National Key Laboratory for RSA and Department of Superalloy and Special Casting , Institute of Metal Research , Chinese Academy of Sciences , Shenyang 110015) , China

金属学报(英文版)

Based on the previous work on the mechanical alloying of Ni-Al-Ti compounds. the mechanically alloyed Ni-Al-Ti compounds was characterized. The results show that with the increase of Ti content. the microhardness of the final products decrease apparently. The thermal behavior of the resultant Ni-Al-Ti compounds shows significant difference, the as-milled powders with different Ti content transform into different products after healing.So the microstructure of the milled alloys could be determined through adequate control of composition and heat treatments.

关键词: : mechanical alloying. Ni-Al-Ti , null

1998 COMPREHENSIVE TABLE OF CONTENTS

中国腐蚀与防护学报

N。1Atmospheric Corrosivlty for Steels………………………………………………… .LIANG Caideng HO[I i。-tat（6）Caustic Stress Corrosion Cr。king of Alloy 800 Part 2.The Effect of Thiosul执e……………………………………… KONG De-sheng YANG Wu ZHAO Guo-zheng HUANG De.ltL。ZHANG Yu。。he CHEN She。g-bac（13）SERS slid E16CttOCh6iniC81 Stlldy Of Illhibit1Oli M6ch＆tllsth Of ThlollY68 Oil ITOll ID H....

关键词:

提高本钢265 m2冷烧结矿及原料检验代表性的实践

李凤娟 , 吕国光

金属世界 doi:10.3969/j.issn.1000-6826.2014.04.14

通过对烧结配料所需原料及对冷烧结矿成品检验采制样方法的分析，找出影响检验结果真实性的因素，采取有效的改进措施，使本钢原料厂一次配料、本钢炼铁厂265 m2烧结二次配料及265 m2烧结系统各项稳定率有了很大的提高，烧结矿实物质量和各项技术质量指标有了很大的进步，保证了高炉的稳定顺行。
　　提高本钢265 m2冷烧结矿及原料检验代表性的实践
　　Practice of Improving the 265 m2 Cold Sinter and Raw Material Inspection Representative
　　供稿|
　　李凤娟,吕国光/
　　LI Feng-juan, LV Guo-guang
　　DOI：10.3969/j.issn.1000-6826.2014.04.14
　　导读内容
　　本钢炼铁厂265 m2烧结机生产所需要的含铁原料比较复杂，一次配料料种较多，且烧结含铁原料是由本钢原料厂二车间供料，原料质量的不稳定，会影响烧结矿质量的提高和新一号高炉的强化及高炉技术指标的改善。本钢质量管理中心驻冷烧检查站加强了对烧结配料所需原料及对冷烧结矿成品检验采制样代表性的研究，采取了一些改进措施，达到了良好的效果。含铁料成分稳定率、烧结矿各项质量和技术指标在稳步地提高。下面，对本钢质量管理中心驻冷烧检查站就提高采样及检验过程的准确性所采取的措施和办法进行说明。
　　烧结矿采样是半自动采样，每两小时采样一次，作为一个批次，来代表整个2h烧结矿的成份。

关键词: