FAN Guojiang
,
QUAN Mingxiu
,
HU ZhuangqiInstitute of Metal Research. Chinese Academy of Sciences
,
Shenyang
,
China Manuscript received 6 May
,
1994
金属学报(英文版)
The Al_(100-x)Ti_(x)(x = 5,10,15,35) mixed powders were mechanically alloyed in a planetary bull mill. It was found that the initial composition strongly affects the final productsi a mixture of supersaturated solid solution Al(Ti) and a fee phase for x = 5 and 10; and a single supersaturated solid solution Al(Ti)for x=15 and 35. With inereasing Ti contents from 5at% to 35at%, the grain size of solid solution Al(Ti) decreased from 40nm to 10nm. The results suggest that fast diffusion along nanocrystalline grain boundary is the main alloying process. DSC curves and TEM observation indicate that the solute atom segregation can thermally stabilize the nanocrvstalline solid solutions.
关键词:
mechanical alloy ing. fast diffusion
,
null
B.W. Wang
,
H. Shen
金属学报(英文版)
Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactivesputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as targetmaterial and copper sheets as substrate. Using SEM, Spectrophotometer and Talystepto analyze the relations between the selective characteristic and the structure, theformation and the thickness of the thin films. The aim is to obtain good solar selectivethin films with high absorptance and low emittance, which is applied to flat plate solarheat collectors.
关键词:
solar selective thin film
,
null
,
null
,
null
材料科学技术（英文）
BIOSS4 steel is essentially a nickel-free austenitic stainless steel developed by the Institute of Metal Research, Chinese Academy of Sciences, in response to nickel allergy problems associated with nickel-containing stainless steels that are widely used in medical applications. The high nitrogen content of this steel effectively maintains the austenitic stability and also contributes to the high levels of corrosion resistance and strength. BIOSS4 steel possesses a good combination of high strength and toughness, better corrosion resistance, and better blood compatibility, in comparison with the medical 316L stainless steel. Potential applications of BIOSS4 steel can include medical implantation material and orthodontic or orthopedic devices, as well as jewelries and other decorations.
关键词:
medical stainless steel;nitrogen;nickel-free;nickel-allergy;blood;compatibility;austenitic steels;high-nitrogen;corrosion;cells
Yibin REN
,
Ke YANG
,
Bingchun ZHANG
,
Yaqing WANG
,
Yong LIANG
材料科学技术（英文）
BIOSS4 steel is essentially a nickel-free austenitic stainless steel developed by the Institute of Metal Research, Chinese Academy of Sciences, in response to nickel allergy problems associated with nickel-containing stainless steels that are widely used in medical applications. The high nitrogen content of this steel effectively maintains the austenitic stability and also contributes to the high levels of corrosion resistance and strength. BIOSS4 steel possesses a good combination of high strength and toughness, better corrosion resistance, and better blood compatibility, in comparison with the medical 316L stainless steel. Potential applications of BIOSS4 steel can include medical implantation material and orthodontic or orthopedic devices, as well as jewelries and other decorations.
关键词:
Medical stainless steel
,
null
,
null
,
null
,
null
Corrosion
This paper introduces the design of a localized corrosion rate monitoring instrument that can monitor and evaluate the maximum and stable localized corrosion rate of a nonpassivable metal in a corrosive environment by measuring the current density in a corrosion sensor with an occluded anode.
关键词:
instrument;localized corrosion rate;monitor
WADSWORTH Jeffrey and FLUSS Michael(Chemistry and Materials Science Directorate
,
Lawrence Livermore National Laboratory
,
Livermore
,
CA 94551)
金属学报(英文版)
The role of the National Laboratories is summarized from the era of post World War II to the present time. The U.S. federal government policy for the National Laboratories and its influence on their materials science infrastructure is reviewed with respect to .determining overall research strategies, various initiatives to interact with industry (especially in recent years),building facilities that serve the nation, and developing leading edge research in the materials sciences. Despite reductions in support for research in the U.S. in recent years, and uncertainties regarding the specific policies for Research &Development (R&D) in the U.S., there are strong roles for materials research at the National Laboratories. These roles will be centered on the abilities of the National Laboratories to field multidisciplinary teams, the use of unique cutting edge facilities, a focus on areas of strength within each of the labs,increased teaming and partnerships, and the selection of motivated research areas. It is hoped that such teaming opportunities will include new alliances with China, in a manner similar, perhaps, to those recently achieved between the U.S. and other countries.
关键词:
: U.S. Materials Science. U.S. National Laboratories and Facilities
,
null
Dental Materials
Objectives. To research the crystal structure and surface morphology of anodic films on titanium metal in different electrolytes under various electrochemical conditions and investigate the effect of the crystal structure of the oxide films on apatite-forming ability in simulated body fluid (SBF). Methods. Titanium oxide films were prepared using an anodic oxidation method on the surface of titanium metal in four different electrolytes: sulfuric acid, acetic acid, phosphoric acid and sodium sulfate solutions with different voltages for 1 min at room temperature. Results. Anodic films that consisted of rutile and/or anatase phases with porous structures were formed on titanium metal after anodizing in H(2)SO(4) and Na(2)SO(4) electrolytes, while amorphous titania films were produced after anodizing in CH(3)COOH and H(3)PO(4) electrolytes. Titanium metal with the anatase and/or rutile crystal structure films showed excellent apatite-forming ability and produced a compact apatite layer covering all the surface of titanium after soaking in SBF for 7 d, but titanium metal with amorphous titania layers was not able to induce apatite formation. Significance. The resultant apatite layer formed on titanium metal in SBF could enhance the bonding strength between living tissue and the implant. Anodic oxidation is believed to be an effective method for preparing bioactive titanium metal as an artificial bone substitute even under load-bearing conditions. (C) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
关键词:
Titanium;Anodic oxidation;Rutile;Anatase;Apatite;simulated body-fluid;oxide-films;apatite formation;heat-treatments;surface;anodization;deposition;implants;coatings;ability
S.H.O
材料科学技术（英文）
The magnetic property of soft magnetic metals and alloys depends strongly on the crystallographic orientation. In automated equipment for orientation research. the intensity for drawing up the pole figure is measured in detail. The present research shows that the accurate pole figure can be drawn up without measuring concretely the intensity. For directional Si steel sheet the measuring step may be 4 similar to 5 degrees. In this paper the experimental equation for defocusing correction was derived from the experimental data in different specimens with random orientation.
关键词: