Microbridge testing is used to measure the Young's modulus and residual stresses of
metallic films. Nickel film microbridges with widths of several hundred microns are
fabricated by Microelectromechanical Systems. In order to measure the mechanical
properties of nickel film microbridges, special shaft structure is designed to solve the
problem of getting the load-deflection curves of metal film microbridge by Nanoindenter XP system with normal Berkovich probe. Theoretical analysis of the microbridge load-deflection curve is proposed to evaluate the Young's modulus and residual
stress of the films simultaneously. The calculated results based on the experimental
measurements show that the average Young's modulus and residual stress are around
190GPa and 175MPa respectively, while the Young's modulus measured by Nano-
hardness method on nickel film with silicon substrate is 186.8±7.34GPa.
关键词:
nickel film microbridge
,
null
,
null
,
null
李开明
,
李亚洲
,
冯维贵
,
林长
量子电子学报
doi:10.3969/j.issn.1007-5461.2007.05.014
采用非线性反馈控制,用附加了带参数的正弦项对Chen系统进行了有效的控制.随着参数k的逐渐增大,系统的动力学行为呈现出一系列的变化.数值研究结果表明:随控制参数的增大,驱动信号的强度渐大,混沌系统由混沌运动到周期轨道,最终到一相点.
关键词:
混沌
,
Chen系统
,
不动点
,
Lyapunov指数
,
反馈控制
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
Physical Review B
The Hamiltonian for a four-sublattice Heisenberg ferrimagnet or ferromagnet with different exchange constants (J(ab) = J(cd) not equal J(bc) = J(da)) was established. An extended Bogoliubov transformation was developed by solving an equation group, consisting of 20 equations and 20 unknowns. The procedure for solving the equation group was carried out by introducing a simple way of reducing the numbers of the equations and the unknowns. The spin-wave spectra in the present system have been determined by performing the standard Holstein-Primakoff transformation and the Bogoliubov one. It has been found that the spin-wave spectra of the present system depend on the exchange constants and that the degeneracy of the spin-wave spectra remains. The results for a special case (J(ab) = J(bc)) i.e., an antiferromagnet are discussed briefly. The spin-wave spectra of the four-sublattice Heisenberg antiferromagnet are found to be degenerative also and they are linear in k for small k.
关键词:
model
Y.G. Cao
,
X.Y. Sun
金属学报(英文版)
J-integral and crack opening displacement δ(COD) were important parameters for characterization of fractures in engineering materials. The relationship between J-integral and COD has been investigated for a long time and was enerally represented as J = m σyδ, where σy is the yield strength and m is a function of specimen geometry and material properties. To determine the value of m, extensive studies and experiments have been performed. The method that used the fracture-surface topography analysis (FRASTA) for determining J-integral from fracture surfaces of materials was introduced. On the basis of the relationship between COD and fracture surface average profile, the relationship between J-integral and COD was deduced and compared with the generally used equation. The method was experimentally confirmed to be able to provide a new way to determine the relationship between J-integral and COD.
关键词:
FRASTA
,
null
,
null
null
,
null
金属学报
在工程上,经常由于应力腐蚀开裂和氢脆引起中强度钢结构件发生滞后破坏。这类脆断往往从结构件中预先存在的疲劳或焊接裂纹处开始,因此,运用传统的光滑试样的检验方法不能反映这类破坏的特点。 本文将弹塑性断裂力学中的J积分概念用于滞后破坏的研究,提出用带预制疲劳裂纹的悬臂弯曲试样测定J积分的临界值J_(Ic)和应力腐蚀开裂阈值J_(Iscc)的方法。测定了40CrNiMo钢的J_(Ic)值及其在硫化氢水溶液中的J_(Iscc)值。通过和三点弯曲方法测定的J_(Ic)值的对比,以及和满足线弹性条件时直接测定的应力强度因子K_I值的对比,说明这种方法的可靠性。最后,对悬臂弯曲方法的特点进行了讨论。
关键词:
平荣刚
原子核物理评论
doi:10.3969/j.issn.1007-4627.2004.02.026
通过J/Ψ→pp-,pN-*,N*N-*衰变,研究了Roper共振态的混杂态结构对衰变角分布和分支比的影响.计算结果表明,如果Roper共振态为纯混杂态,那么J/Ψ→pN-*,N*N-*的角分布几乎相等,而J/Ψ衰变到混杂态的衰变宽度还不到J/Ψ→pp-的1%,给出了Γ(J/Ψ→ N*p-)/Γ(J/Ψ→pp-)和Γ(J/Ψ→ N*N-*)/Γ(J/Ψ→pp-)随混合参数的变化关系,并讨论了在J/Ψ衰变中研究Roper混杂态结构的可能性.
关键词:
Roper共振态结构
,
混杂态
,
J/Ψ
Journal of Physics-Condensed Matter
The temperature dependences of the magnetization, internal energy and specific heat in a three-sublattice ferrimagnet or ferromagnet with /J(ab)/ = /J(bc)/ not equal /J(ca)/ are calculated within the framework of the linear spin-wave approximation, by employing retarded Green's functions. For both the ferromagnet and the ferrimagnet, the internal energy and the specific heat decrease with increasing J ' /J and/or the value of the spins. For fixed values of S,, Sb, S, and J ' /J, the internal energy and the specific heat increase, whereas the sublattice magnetization decreases with increasing temperature theta. The three-sublattice ferrimagnet has some particular characteristics which are not shown by the systems with two sublattices. For ferrimagnets, the antiferromagnetism of the system becomes weaker with increasing J ' /J. The sublattice magnetization at low temperatures (also the magnetization M(0) at 0 K) of a ferrimagnet increases with increasing J ' /J for fixed values of S(a), S(b) and S(c). The effects of the spins S(a) (S,) and Sb On the magnetizations of other sublattices differ. The characteristics of the a-sublattice are the same as those of the c-sublattice, due to their similarity as well as the symmetry of the system. The behaviours of the b-sublattice are different from those of the a- and c-sublattices, due to the asymmetry of the three-sublattice system. The spin-value dependences of the spin deviation Deltam per spin land also the energy for the zero-point quantum fluctuation) of the system are different for different sublattices. These differences are ascribed to the asymmetry of the three-sublattice systems, which leads to the new intrinsic properties of the systems.
关键词:
layered heisenberg ferrimagnets;spin-wave theory;elementary;excitations;superlattices;systems;magnetoresistance;antiferromagnet;interfaces