Chao YUAN
,
Jianting GUO and Shuhe WANG(Institute of Metal Research
,
Chinese Academy of Sciences
,
Shenyang 110015
,
China)Hongcai YANG(Dept. of Materials Science and Engineering
,
Northeastern University
,
Shenyang 110006
,
China)
材料科学技术（英文）
The tensile creep-fracture properties of DZ17G. a directionally solidified superalloy, were inves-tigated at 830~ 900℃. The results show that all of the creep curves exhibit negligible primary creep, relatively little steady-state creep and dominant tertiary creep stage. The higher apparent activation energy for creep (540 kJ/mol ) suggests that the creep is controlled by Orowan bowing process. A large ratio of the fracture time to the onset time of tertiary creep is the consequence of microstructure change, i.e., γ particles oriented coarsening parallel to the applied stress axis.The creep fracture data follow the Monkman-Grant relationship. The transgranuIar fracture mechanism proposed on the basis of the metallographic examinations is the linkage of the creep cracks which initiate at the discontinuities with the microstructure (such as the cast porosity,and the carbide/matrix intedece) and also at the specimen surface, that propagate along the γ/γ intedece with perpendicular to the applied stress axis, and the process of crack propagation can be described by the Tien model.
关键词:
MA Zongyi YAO Zhongkai Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
The SiC_w/Al composite prepared by squeeze casting has a combination of superior room temperature specific strength and modulus together with excellent thermal properties.The extrusion can make an improvement on the strength and ductility of the composite from 582 MPa as squeeze casted up to 639 MPa,and on the transformation from isotropic to the anisotropic structure.This seems to be explained by the orientation of whiskers and the densification of dislocations in matrix.TEM observation indicates that the stacking fault is the usual planar defect on the SiC_w surface. composite;;SiC whisker;;Al alloy;;microstructure
关键词:
composite
,
null
,
null
,
null
Corrosion
This paper introduces the design of a localized corrosion rate monitoring instrument that can monitor and evaluate the maximum and stable localized corrosion rate of a nonpassivable metal in a corrosive environment by measuring the current density in a corrosion sensor with an occluded anode.
关键词:
instrument;localized corrosion rate;monitor
Juhua HUANG
,
Jinjun RAO
,
Xuefeng LI
材料科学技术（英文）
Sheet metal forming is widely applied to automobile, aviation, space flight, ship, instrument, and appliance industries. In this paper, based on analyzing the shortcoming of general finite element analysis (FEA), the conception of parametric finite element analysis (PFEA) is presented. The parametric finite element analysis, artificial neural networks (ANN) and genetic algorithm (GA) are combined to research thoroughly on the problems of process parameters optimization of sheet metal forming. The author programs the optimization scheme and applies it in a research of optimization problem of inside square hole flanging technological parameters. The optimization result coincides well with the result of experiment. The research shows that the optimization scheme offers a good new way in die design and sheet metal forming field.
关键词:
Sheet metal forming
,
null
,
null
,
null
J.Q.ZHANGD.J.YOUNG
中国腐蚀与防护学报
Metaldusting attacks iron, low and high alloy steels and nickel-or cobalt-base alloys by disintegrating bulk metals and alloys into metal particles in a coke deposit. It occurs in strongly carburising gas atmospheres (carbon activity aC>1) at elevated temperatures (400 ℃~1000 ℃). This phenomenon has been studied for decades, but the detailed mechanism is still not well understood. Current methods of protection against metal dusting are either directed to the process conditions-temperature and gas composition-or to the development of a dense adherent oxide layer on the surface of the alloy by selective oxidation. However, metal dusting still occurs by carbon dissolving in the base metal via defects in the oxide scale. The research work at UNSW is aimed at determining the detailed mechanism of metal dusting of both ferritic and austenitic alloys, in particular the microprocesses of graphite deposition, nanoparticle formation and underlying metal destruction. This work was carried out using surface observation, cross-section analysis by focused ion beam and electron microscopic examination of coke deposits at different stages of the reaction. It was found that surface orientation affected carbon deposition and metal dusting at the initial stage of the reaction. Metal dusting occurred only when graphite grew into the metal interior where the volume expansion is responsible for metal disintegration and dusting. It was also found that the metal dusting process could be significantly changed by alterations in alloy chemistry. Germanium was found to affect the iron dusting process by destabilising Fe3C but increasing the rate of carbon deposition and dusting, which questions the role of cementite in ferritic alloy dusting. Whilst adding copper to iron did not change the carburisation kinetics, cementite formation and coke morphology, copper alloying reduced nickel and nickel-base alloy dusting rates significantly. Application of these fundamental results to the dusting behaviour of engineering alloys is discussed.
关键词:
metal dusting
,
null
,
null
,
null
,
null
,
null
Z. Yang
,
J.P. Li
,
J.X. Zhang
,
G.W.Lorimer
,
J. Robson
,
null
,
null
,
null
,
null
金属学报(英文版)
The current research and development of magnesium alloys is summarized. Several aspects of magnesium alloys are described: cast Mg alloy, wrought Mg alloy, and novel processing. The subjects are discussed individually and recommendations for further study are listed in the final section.
关键词:
Magnesium alloys
,
null
,
null