Time-dependent Fatigue Crack Propagation (FCP) behaviors of five Ni-base superalloys were investigated at various temperatures under fatigue with various holding times and sustained loading conditions. The new concept of damage zone is defined and employed to evaluate the alloys' resistance to hold-time FCP. A special testing procedure is designed to get the maximum damage zone of the alloys. Udimet 720 and Waspaloy show shorter damage zones than alloys 706 and 718. The fractographieal analyses show that the fracture surfaces of the specimens under hold-time fatigue conditions are mixtures with intergranular and transgranular modes. As the extension of holding time per cycle, the portion of intergranular fracture increases, The effects of loading stress intensity, temperature, holding time, alloy chemisty, and alloy microstructure on damage zone and the crack growth behaviors are studied. Hold-time usually increases the alloy's FCP rate, but there are few exemptions. For instance, the steady, state hold-time FCP rate of Waspaloy at 760℃ is lower than that without hold-time. The beneficial effect of hold-time was attributed to the creep caused stress relaxation during the hold-time.
关键词:
Ni-base superalloys
,
null
,
null
刘国栋
,
张利英
,
王艳丽
,
郭丹
,
程翠然
高分子材料科学与工程
采用前期提出的共聚物Tg-组成关系方程研究了MA-EA、MA-n-BA二元共聚物的Tg,新方程中的周期共聚物Tg通过最小二乘法由无规共聚物Tg数据求取,相关周期共聚物的Tg为:Tg[ME]=274.6K、Tg[MB]=246.3K、Tg[MME]=286.3K、Tg[MMB]=262.8K、Tg[EEM]=262.3K、Tg(BBM]=236.7K,由此计算得到的理论值与实验值偏差极小,说明新方程能够更好地解释丙烯酸甲酯二元共聚物Tg与其组成及序列结构之间的关系.进一步预测了不同取代基时有序取代密度对聚丙烯酸甲酯Tg的影响规律,发现与对聚甲基丙烯酸甲酯Tg的影响规律不同,取代基的影响在高取代密度时才能显现.
关键词:
二元共聚物
,
玻璃化温度
,
组成
,
取代基
王晓旭
,
陈利
材料工程
doi:10.3969/j.issn.1001-4381.2011.11.001
通过单根Z-pin从复合材料层合板中拔出的试验方法,测试了Z-pin的拔出强度,计算了Z-pin的临界埋入深度,并引入抗拉强度利用率概念来表征Z-pin的抗拉强度在拔出过程中的利用程度.结果表明,直径0.50mm和0.28mm的Z-pin临界埋入深度分别约为5.1mm和3.1mm.当Z-pin的埋入深度小于临界埋入深度时,Z-pin从层板中拔出；Z-pin拔出强度与埋入深度成正比,与Z-pin的直径成反比；当Z-pin的埋入深度大于临界埋入深度时,Z-pin发生断裂,Z-pin的抗拉强度利用率达到100％.最后提出了提高抗拉强度利用率的建议.
关键词:
Z-pin
,
拔出强度
,
复合材料
,
拔出试验
,
抗拉强度
张强
,
许少普
,
李忠波
,
唐郑磊
,
高照海
,
杨阳
钢铁
doi:10.13228/j.boyuan.issn1001-0963.20150135
采用横截面为350mm×2 320 mm的钢坯轧制横截面为100 mm×2 360 mm的Q345E-Z35.在粗轧阶段以高于动态再结晶临界变形量和形状系数l/h≥0.53的条件下,经过不同的终轧温度和返红温度试验,最终确定精轧阶段终轧温度控制在780℃左右,返红温度控制在610℃左右,生产出的钢板具有优异的力学性能和层状撕裂抗性.
关键词:
Q345E-Z35
,
特厚板
,
控轧控冷
王晓旭
,
陈利
航空材料学报
doi:10.3969/j.issn.1005-5053.2011.4.017
通过三种复合材料Z-pin的轴向压缩试验,观察了各Z-pin的压缩行为,分析了三种复合材料Z-pin在不同长度时的极限应力及其失效形式.结果表明,直径为0.50mm的碳纤维Z-pin的压缩性能最好,其各长度Z-pin所能承担的极限应力都较大.直径0.28mm的碳纤维Z-pin易发生失稳现象,芳纶纤维Z-pin在压缩力的作用下,接触端容易受到破坏.两种碳纤维Z-pin临界应力的理论值与试验值吻合较好,但芳纶纤维Z-pin的临界应力的试验值比理论值偏低.
关键词:
Z-pin
,
复合材料
,
压缩试验
,
临界应力
Li XING
,
Jie ZHAO
,
Fuzhong SHEN
,
Wei FENG
材料科学技术（英文）
A Z-parameter method is used to evaluate the damage process of HK40 austenitic steel. By using Z-parameter based on the Larson-Miller method, the nonlinear master curve of the log stress vs Larson-Miller parameter P can be expressed as: P=27.74-3.4lgσ-0.032σ, and a family of curves parallel to the master curve can be written as: P=(27.74-Z)-3.4lgσ-0.032σ, where Z represents the magnitude of the deviation from the master curve. According to the creep rupture data both from different segments of a serviced tube and from the same segment locations with different service time, the value of parameter Z has close relationship with the deterioration of creep rupture properties. The damage state of the samples is evaluated by monitoring the changes in natural frequency f and Young0s modulus E, and the relationships between Z and the damage parameters are discussed.
关键词:
Damage evaluation
,
蠕变断裂
,
奥氏体钢
,
Z参数