INTERACTIONS BETWEEN La2O3 PARTICLES AND DISLOCATIONS IN Mo-La2O3 ALLOYS

J.X. Zhang , D.M. Liu , Y.Q. Liu , M.L. Zhou , T.Y. Zuo

金属学报(英文版)

The mechanical properties of molybdenum wires doped with different contents of La2O3 were investigated systematically and the interaction between La2O3 particles with dislocations in Mo- La2O3 wires were observed by SEM and TEM. It is shown that Mo-La2O3 wires possess much higher tensile strength than the pure Mo. In wires the dislocation motion is strongly hindered by La2O3 particles, which remains up to much higher temperature. Moreover, a number of prismatic dislocation loops and hexagonal dislocation network have been formed in annealed Mo-La2O3 wires. The higher strength of Mo-La2O3 than the pure Mo is attributed to the La2O3 particles dispersion strengthening and dislocation strengthening.

关键词: molybdenum , null , null

FeMoB Enhanced Sintering of P/M 316L Stainless Steel

YANG Xia , GUO Shiju

钢铁研究学报(英文版)

Liquidphase enhanced sintering of powder metallurgy (P/M) 316L stainless steel by addition of sintering aids was studied. 2%-8% of prealloyed FeMoB powder with two different particle sizes was added as sintering aids, and the specimens were sintered in vacuum at 1 200-1 350 ℃. The results show that the fine FeMoB powder (5-10 μm) has stronger activated effect. The sintered density increases with the increase in sintering aid content or sintering temperature. Warm compaction has a better effect on the control of dimensional precision of compacts. The prealloyed FeMoB powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.

关键词: P/M 316L stainless steel;liquidphase sintering;activated sintering;FeMoB;sintering aid

试棒的w_0/l_0值对Zn-5%Al合金超塑性m-δ关系的影响

刘勤 , 裔式珙

材料研究学报

在250℃以■=0.025min~(-1)测到的Zn-5%Al 合金的超塑性m-δ曲线均属式。w_0/l_0值加大使m_0,m_L 和δ_F 值增大,但对δ_L 和m_F 值无大影响。试样厚度的加大(由1增大到2mm)仅使δ_L 和δ_F 值增大,考虑w_0/l_0比值的影响,C_3~((m_0-m_L))-(m_L=m_(mas))型C.L.m-δ方程式规划为:或其中,m′_0(W_0/l_0)=m_0,m′_0>m_0;m′_L(w_0/l_0)=m_L,m′_L>m。w_0/l_0=0.15—0.39。当w_O/l_0=1时,缺口效应消失,δ(或δ_F)值为最大。

关键词: Zn-5%Al合金 , mechanics of superplasticity , C.L.m-δequation

Ni64Al21V15沉淀过程DO22向L10(M=1)结构转变的微观相场模拟

常秀丽 , 王永欣 , 陈铮 , 张静 , 程立维

稀有金属材料与工程

基于微观相场模型,研究了Ni64Al21V15合金在1150 K时效过程中相结构演化.结合微观组织演化图像和各个格点上原子占位几率的演化,分析了DO22结构向L10 (M=1)结构转变机制.合金沉淀中期,在相界处析出L10(M=1)结构.研究发现,L10 (M=1)结构形成可分为3类:在DO22与L12相界处形核,沿[001]方向排列,向DO22相扩张;在DO22结构90°有序畴界处形核,沿[001]方向排列,向DO22扩张;在2个[100]向排列的DO22结构交界处形核,沿[100]方向排列,向DO22结构扩张.DO22相中,V主要占据β位,Ni主要占据α2和α3位,Al主要占据α1位;随后,V向α2位跃迁,在(002)面富聚且发生有序化,逐渐占据β和α2位,Ni原子发生面间跃迁,由α2位跃迁至α1位,逐渐占据α1和α3位,Al原子向相外扩散.DO22结构最终转变为高度有序的L10(M=1)结构.

关键词: 结构转变 , L10(M=1)结构 , 序参数 , Ni-Al-V合金 , 微观相场

异材焊接件A508/52M/316L在高温水环境中的应力腐蚀破裂

李光福李冠军方可伟彭君杨武张茂龙孙志远

金属学报 doi:10.3724/SP.J.1037.2011.00316

采用慢应变速率实验(SSRT)方法, 研究了先进的异材焊接件A508/52M/316L在模拟压水堆一回路290 ℃高温水环境中的应力腐蚀破裂(SCC)特性. 实验在-780 mV至+200 mV范围的电位下进行, 模拟一回路水化学从低O含H的理想低电位状态到溶解O$_{2}$明显超标的高电位状态的服役环境. 该焊接件显微组织和化学成分分布较复杂, 显著的变化发生在A508/52M和52M/316L 2个界面附近. 在SSRT拉伸试样的典型位置处加工了同样尺寸的尖锐缺口, 以模拟应力集中和加速实验, 并比较这些典型位置的SCC 敏感性. 结果表明, 当电位位于-780 mV至-300 mV范围时, SSRT试样总是以韧性断裂形式在镍基合金焊缝中部发生断裂. 当电位升到-200 mV至+200 mV范围时, 试样发生显著的SCC脆断, A508/52M界面区周围是该焊接件最脆弱的部位, 在该界面和附近的A508热影响区发生穿晶应力腐蚀破裂(TGSCC), 在紧邻界面的镍基合金焊缝薄层发生沿晶应力腐蚀破裂(IGSCC). 讨论了破裂机理和实验结果的工程意义.

关键词: 压水堆核电站 , primary water , dissimilar metal weld , stress corrosion cracking , electrode potential , water chemistry

异材焊接件A508/52M/316L在高温水环境中的应力腐蚀破裂

李光福 , 李冠军 , 方可伟 , 彭君 , 杨武 , 张茂龙 , 孙志远

金属学报 doi:10.3724/SP.J.1037.2011.00316

采用慢应变速率实验(SSRT)方法,研究了先进的异材焊接件A508/52M/316L在模拟H压水堆一回路290℃高温水环境中的应力腐蚀破裂(SCC)特性.实验在-780 mV至+200 mV范围的电位下进行,模拟一回路水化学从低O含H的理想低电位状态到溶解O2明显超标的高电位状态的服役环境.该焊接件显微组织和化学成分分布较复杂,显著的变化发生在A508/52M和52M/316L 2个界面附近.在SSRT拉伸试样的典型位置处加工了同样尺寸的尖锐缺口,以模拟应力集中和加速实验,并比较这些典型位置的SCC敏感性.结果表明,当电位位于-780mV至-300mV范围时,SSRT试样总是以韧性断裂形式在镍基合金焊缝中部发生断裂.当电位升到-200mV至+200 mV范围时,试样发生显著的SCC脆断,A508/52M界面区周围是该焊接件最脆弱的部位,在该界面和附近的A508热影响区发生穿晶应力腐蚀破裂(TGSCC),在紧邻界面的镍基合金焊缝薄层发生沿晶应力腐蚀破裂(IGSCC).讨论了破裂机理和实验结果的工程意义.

关键词: 压水堆核电站 , 一回路水环境 , 异材焊接件 , 应力腐蚀破裂 , 电位 , 水化学

超塑性 m-δ关系

刘勤 , 周善佑

材料研究学报

超塑性m-δ关系曲线可以分为m_L=m_(max)和m_L=m_(min)两大类型。均可由下面的C.L.(刘勤)m-σ方程表示:σ(%)=〔cε~(m-m_0)-1〕×100当σ=σ_0=0时,m=m_0≠0,C=C_0=κ_0/κ_0=1。当σ=σ_1(σ_(11),σ_(12),σ_(13),…,)时,m=m_1(m_(11),m_(12),m_(13),…),C=C_1(C_(11),C_(12),C_(13),…)=κ_1(κ_(11),κ_(12),κ_(13),…)/κ_0,当σ=σ_F时,m=m_F,C=C_F=κ_F/κ_0。对C 值进行“规划”,得到的C_1~(σ_O-σ_L)-(m_L=m_(max)),C_2~(σ_F-σ_L)-(m_L=m_(min)),C_3~(m_0-m_L)-(m_L=m_(max)和C_4~(m_F-m_L)-(m_L=m_(min))四种类型的“规划”方程分别对m_L=m_(max)和m_L=m_(min)型m-σ曲线适用。若m-σ曲线属简单的下降式,C 及其“规划”值均可近似地取1。否则,C-σ关系是应加以研究的问题。m 和k 值对σ值的效应可以分为动态(直接)和静态(间接)两种。最后的σ值是两种效应的综合结果。(注:m 和κ值见基本方程σ=κε~m)

关键词:

基于L-M算法BP神经网络的转炉炼钢终点磷含量预报

李长荣 , 赵浩文 , 谢祥 , 尹青

钢铁

转炉炼钢过程是一个非常复杂的物理化学变化过程,人工控制很难一次达到终点目标值,通常需要经过多次补吹才能出钢.通过研究影响转炉冶炼终点磷含量的主要因素,确定了影响转炉终点磷含量的参数,建立了基于Levenberg-Marquardt(LM)算法BP神经网络转炉终点磷含量的预报模型.结果表明:在预报误差目标精度为土0.002%内,命中率达到了90%.

关键词: BP神经网络 , 终点磷含量 , Levenberg-Marquardt算法 , 预报模型

基于L-M算法BP神经网络的转炉炼钢终点磷含量预报

李长荣赵浩文谢祥尹青

钢铁

摘 要：转炉炼钢过程是一个非常复杂的物理化学变化过程，人工控制很难一次达到终点目标值，通常需要经过多次补吹才能出钢。本文通过研究影响转炉冶炼终点磷含量的主要因素，确定了影响转炉终点磷含量的参数，建立了基于Levenberg-Marquardt(LM)算法BP神经网络转炉终点磷含量的预报模型。结果表明：在预报误差目标精度为±0.002%内,命中率达到了90%。

关键词: 预报模型

Fe-Mo-B Enhanced Sintering of P/M 316L Stainless Steel

钢铁研究学报(英文版)

关键词: