G.G.Cheng
,
M.L.Wang
,
X.E.Yang
,
Y.L.Li
,
Y.G.Wang
,
L.Y.Wang
,
P.Zhao
金属学报(英文版)
Precipitation condition and nucleation of Ti2 03 during solidification of clean steel have been studied. The behavior of Ti2 03 during solidification as well as possibility of using Ti203 to refine as-cast grains as heterogeneous nucleation sites is discussed. It is shown that Ti2 03 can be formed provided that the steelmaking and solidification process is controlled strictly. And inoculating clean steel with Ti203 is an effective way to refine as-cast grains.
关键词:
clean steel
,
null
,
null
YANG Xia
,
GUO Shiju
钢铁研究学报(英文版)
Liquidphase enhanced sintering of powder metallurgy (P/M) 316L stainless steel by addition of sintering aids was studied. 2%-8% of prealloyed FeMoB powder with two different particle sizes was added as sintering aids, and the specimens were sintered in vacuum at 1 200-1 350 ℃. The results show that the fine FeMoB powder (5-10 μm) has stronger activated effect. The sintered density increases with the increase in sintering aid content or sintering temperature. Warm compaction has a better effect on the control of dimensional precision of compacts. The prealloyed FeMoB powder deviated from Mo2FeB2 component can also be sintering aid of P/M 316L stainless steel.
关键词:
P/M 316L stainless steel;liquidphase sintering;activated sintering;FeMoB;sintering aid
刘勤
,
裔式珙
材料研究学报
在250℃以■=0.025min~(-1)测到的Zn-5%Al 合金的超塑性m-δ曲线均属式。w_0/l_0值加大使m_0,m_L 和δ_F 值增大,但对δ_L 和m_F 值无大影响。试样厚度的加大(由1增大到2mm)仅使δ_L 和δ_F 值增大,考虑w_0/l_0比值的影响,C_3~((m_0-m_L))-(m_L=m_(mas))型C.L.m-δ方程式规划为:或其中,m′_0(W_0/l_0)=m_0,m′_0>m_0;m′_L(w_0/l_0)=m_L,m′_L>m。w_0/l_0=0.15—0.39。当w_O/l_0=1时,缺口效应消失,δ(或δ_F)值为最大。
关键词:
Zn-5%Al合金
,
mechanics of superplasticity
,
C.L.m-δequation
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
常秀丽
,
王永欣
,
陈铮
,
张静
,
程立维
稀有金属材料与工程
基于微观相场模型,研究了Ni64Al21V15合金在1150 K时效过程中相结构演化.结合微观组织演化图像和各个格点上原子占位几率的演化,分析了DO22结构向L10 (M=1)结构转变机制.合金沉淀中期,在相界处析出L10(M=1)结构.研究发现,L10 (M=1)结构形成可分为3类:在DO22与L12相界处形核,沿[001]方向排列,向DO22相扩张;在DO22结构90°有序畴界处形核,沿[001]方向排列,向DO22扩张;在2个[100]向排列的DO22结构交界处形核,沿[100]方向排列,向DO22结构扩张.DO22相中,V主要占据β位,Ni主要占据α2和α3位,Al主要占据α1位;随后,V向α2位跃迁,在(002)面富聚且发生有序化,逐渐占据β和α2位,Ni原子发生面间跃迁,由α2位跃迁至α1位,逐渐占据α1和α3位,Al原子向相外扩散.DO22结构最终转变为高度有序的L10(M=1)结构.
关键词:
结构转变
,
L10(M=1)结构
,
序参数
,
Ni-Al-V合金
,
微观相场
李光福李冠军方可伟彭君杨武张茂龙孙志远
金属学报
doi:10.3724/SP.J.1037.2011.00316
采用慢应变速率实验(SSRT)方法, 研究了先进的异材焊接件A508/52M/316L在模拟压水堆一回路290 ℃高温水环境中的应力腐蚀破裂(SCC)特性. 实验在-780 mV至+200 mV范围的电位下进行, 模拟一回路水化学从低O含H的理想低电位状态到溶解O$_{2}$明显超标的高电位状态的服役环境. 该焊接件显微组织和化学成分分布较复杂, 显著的变化发生在A508/52M和52M/316L 2个界面附近. 在SSRT拉伸试样的典型位置处加工了同样尺寸的尖锐缺口, 以模拟应力集中和加速实验, 并比较这些典型位置的SCC 敏感性. 结果表明, 当电位位于-780 mV至-300 mV范围时, SSRT试样总是以韧性断裂形式在镍基合金焊缝中部发生断裂. 当电位升到-200 mV至+200 mV范围时, 试样发生显著的SCC脆断, A508/52M界面区周围是该焊接件最脆弱的部位, 在该界面和附近的A508热影响区发生穿晶应力腐蚀破裂(TGSCC), 在紧邻界面的镍基合金焊缝薄层发生沿晶应力腐蚀破裂(IGSCC). 讨论了破裂机理和实验结果的工程意义.
关键词:
压水堆核电站
,
primary water
,
dissimilar metal weld
,
stress corrosion cracking
,
electrode potential
,
water chemistry
李光福
,
李冠军
,
方可伟
,
彭君
,
杨武
,
张茂龙
,
孙志远
金属学报
doi:10.3724/SP.J.1037.2011.00316
采用慢应变速率实验(SSRT)方法,研究了先进的异材焊接件A508/52M/316L在模拟H压水堆一回路290℃高温水环境中的应力腐蚀破裂(SCC)特性.实验在-780 mV至+200 mV范围的电位下进行,模拟一回路水化学从低O含H的理想低电位状态到溶解O2明显超标的高电位状态的服役环境.该焊接件显微组织和化学成分分布较复杂,显著的变化发生在A508/52M和52M/316L 2个界面附近.在SSRT拉伸试样的典型位置处加工了同样尺寸的尖锐缺口,以模拟应力集中和加速实验,并比较这些典型位置的SCC敏感性.结果表明,当电位位于-780mV至-300mV范围时,SSRT试样总是以韧性断裂形式在镍基合金焊缝中部发生断裂.当电位升到-200mV至+200 mV范围时,试样发生显著的SCC脆断,A508/52M界面区周围是该焊接件最脆弱的部位,在该界面和附近的A508热影响区发生穿晶应力腐蚀破裂(TGSCC),在紧邻界面的镍基合金焊缝薄层发生沿晶应力腐蚀破裂(IGSCC).讨论了破裂机理和实验结果的工程意义.
关键词:
压水堆核电站
,
一回路水环境
,
异材焊接件
,
应力腐蚀破裂
,
电位
,
水化学
刘勤
,
周善佑
材料研究学报
超塑性m-δ关系曲线可以分为m_L=m_(max)和m_L=m_(min)两大类型。均可由下面的C.L.(刘勤)m-σ方程表示:σ(%)=〔cε~(m-m_0)-1〕×100当σ=σ_0=0时,m=m_0≠0,C=C_0=κ_0/κ_0=1。当σ=σ_1(σ_(11),σ_(12),σ_(13),…,)时,m=m_1(m_(11),m_(12),m_(13),…),C=C_1(C_(11),C_(12),C_(13),…)=κ_1(κ_(11),κ_(12),κ_(13),…)/κ_0,当σ=σ_F时,m=m_F,C=C_F=κ_F/κ_0。对C 值进行“规划”,得到的C_1~(σ_O-σ_L)-(m_L=m_(max)),C_2~(σ_F-σ_L)-(m_L=m_(min)),C_3~(m_0-m_L)-(m_L=m_(max)和C_4~(m_F-m_L)-(m_L=m_(min))四种类型的“规划”方程分别对m_L=m_(max)和m_L=m_(min)型m-σ曲线适用。若m-σ曲线属简单的下降式,C 及其“规划”值均可近似地取1。否则,C-σ关系是应加以研究的问题。m 和k 值对σ值的效应可以分为动态(直接)和静态(间接)两种。最后的σ值是两种效应的综合结果。(注:m 和κ值见基本方程σ=κε~m)
关键词:
李长荣
,
赵浩文
,
谢祥
,
尹青
钢铁
转炉炼钢过程是一个非常复杂的物理化学变化过程,人工控制很难一次达到终点目标值,通常需要经过多次补吹才能出钢.通过研究影响转炉冶炼终点磷含量的主要因素,确定了影响转炉终点磷含量的参数,建立了基于Levenberg-Marquardt(LM)算法BP神经网络转炉终点磷含量的预报模型.结果表明:在预报误差目标精度为土0.002%内,命中率达到了90%.
关键词:
BP神经网络
,
终点磷含量
,
Levenberg-Marquardt算法
,
预报模型