In order to investigate creep-fatigue life characteristics of Inconel 738LC, fatigue and creep-fatigue tests were carried out at 850℃. Significant life reduction to 30% to 50% of normal fatigue life, occurred when a strain hold period was introduced at the minimum compressive strain. Test results showed that the degree of life reduction did not depend on the length of hold time. To clarify the creep-fatigue damage mechanisms under creep-fatigue loading, in-situ SEM observations were carried out during the tests. In the tensile strain hold test, multi-site grain boundary cracking was observed from the beginning of the test. On the other hand, only a single main crack was observed in the compressive strain hold test. The crack propagated in an intergranular manner and it was different from the features observed under cyclic fatigue conditions. Through detailed observation, it was found that grain boundary sliding damage occured at most surface grain boundaries.

关键词: superalloy , null , null

201不锈钢形变规律研究

汪荣 , 韩斌 , 赵隆崎 , 刘洋 , 汪水泽

钢铁研究

使用Thermecmastor-Z(300 kN)型热加工模拟实验机,研究了201不锈钢在变形温度1 000～1 250℃、变形速率0.1～50 s-1条件下的形变规律,绘制了应力—应变曲线.试验结果表明,该钢的变形抗力随着变形温度的升高而降低,随变形速率的增大而增大.在变形速率为10 s-1、变形温度1 000～1 250℃条件下,变形抗力随应变增加出现明显峰值.通过回归分析建立了变形抗力模型,该模型具有较好的拟合特性,计算值与实测值拟合较好,可为生产工艺参数的制定提供参考.

关键词: 201不锈钢 , 变形抗力 , 热模拟实验 , 变形规律

201、304不锈钢通用化学发黑工艺

胡俊利 , 满瑞林

电镀与涂饰

介绍了一种201、304不锈钢通用发黑工艺.研究了着色液各组分和挂具的材质对黑色膜性能的影响.着色的最佳配方与工艺为:CrO3 165g/L,H2SO4310mL/L,H3PO4 60mL/L,添加剂A(铵盐)60g/L,添加剂B(过渡金属元素的硫酸盐)143g/L,着色温度91～95℃,着色时间20～25 min,以304不锈钢丝作挂具.在最佳配方与工艺条件下,201、304不锈钢黑板的膜层均匀、黑亮,耐蚀性能均优于对应的基体,耐磨擦性能优越.

关键词: 不锈钢 , 化学发黑 , 耐蚀性 , 耐摩擦性

半固态ZL201合金本构关系研究

王姣姣 , 尚淑珍 , 路贵民 , 于建国

材料科学与工艺

采用Gleeble3800热模拟试验机对液相线铸造获得的ZL201合金半固态坯料进行了不同工艺参数下的热模拟试验，并进行了变形抗力本构方程拟合，以此为基础根据Stefan方程确定了幂律模型中的表观粘度等参数，采用商用仿真软件ANYCASTING对汽车发动机支架进行了触变压铸过程数值模拟分析，获得了ZL201合金的半固态充填流动特征响应，结果表明：半固态表观粘度随剪切速率增大而下降，在充型过程中呈现剪切变稀的触变成形特点，半固态浆料将以层流方式充填型腔，可获得充型完好的半固态压铸零件。

关键词: 半固态 , 本构关系 , 幂律模型 , 数值模拟

201不锈钢表面弧光离子镀TiN和CrN薄膜的耐蚀性

马志康 , 高原 , 蔡航伟 , 王成磊 , 袁琳 , 张焱 , 吴炜钦

腐蚀与防护

利用弧光离子镀设备,对201不锈钢表面进行离子沉积TiN薄膜和CrN薄膜.分别在3.5％ NaCl溶液、1 mol·L-1NaOH溶液和1 mol·L-1 H2SO4溶液中进行电化学腐蚀性能测试.结果表明,通过弧光离子镀技术在201不锈钢表面分别形成了厚度为1.2 μm的致密TiN薄膜和3μm的致密CrN薄膜；201不锈钢、TiN薄膜和CrN薄膜在3.5％的NaCl溶液中耐蚀性相当；在1mol·L-1的NaOH溶液中,TiN薄膜的耐蚀性约是201不锈钢的2倍,CrN薄膜的耐蚀性是201不锈钢的24倍,TiN薄膜的12倍；在1mol·L-1的H2SO4溶液中,TiN薄膜和CrN薄膜的耐蚀性相比201不锈钢分别提高20倍和26倍.

关键词: 弧光离子镀 , TiN薄膜 , CrN薄膜 , 耐蚀性

能量输出幅度对电火花沉积Ni201修复层界面行为的影响

赵运才 , 刘宗阳 , 杨雷雷

表面技术 doi:10.16490/j.cnki.issn.1001-3660.2015.12.011

目的获得电火花沉积质量较好的Ni201 修复层. 方法运用电火花沉积技术,采用DHD-6000型电火花沉积设备在Q235 钢表面制备Ni201 修复改性层,利用电子扫描显微镜( SEM )、能谱仪( EDS)、X射线衍射( XRD)等检测方法,研究修复层与基体结合界面的微观结构、元素分布、相组成以及修复层表面残余应力. 结果 Ni201修复层组织均匀致密,基体与修复层之间发生元素扩散;修复层结合界面处主要由Fe10. 8Ni、γ( Fe,Ni)固溶体、CoFe15. 7及Fe相组成;Ni201修复层表面残余应力随能量输出幅度的增加而增大,在40%与45%能量输出条件下,残余应力分别为-38. 1,-81. 6 MPa,残余应力较小. 结论 Q235钢基体与Ni201修复层元素相互扩散,基体与修复层之间形成了冶金结合,Ni201修复层为冶金结合层. 再制造修复设备工艺参数选择是决定修复层质量的关键因素,能量输出幅度为40%的修复层质量优于能量输出幅度为45%.

关键词: 电火花沉积 , 再制造 , Q235钢 , 修复层 , 界面行为 , 残余应力

ZL201合金的半固态成形组织和力学性能

王平 , 尹翔 , 崔建忠 , 路贵民

材料研究学报 doi:10.3321/j.issn:1005-3093.2007.02.008

制备ZL201合金半固态坯料、将其二次加热、触变模锻成形以及成形件热处理,研究了工艺条件对成形件的组织和力学性能的影响.结果表明:采用近液相线半连续铸造技术制备的ZL201合金半固态坯料微观组织为大量细小的等轴晶和少量短程枝晶;在适当的工艺条件(在640℃保温5 min,模具温度250～300℃,留模时间10～15 s)下可触变成形出表面光洁的ZL201合金成形件;经过T5处理后,ZL201合金的抗拉强度达到278 MPa,延伸率达到9%,大大高于压铸成形件的性能,其强化相为CuAl2和TiAl3.由于成形速度高,溶体高速充型,造成成形件气孔率高,使ZL201合金半固态压铸成形的组织致密度不如半固态模锻成形件,这是半固态压铸件强度低、模锻件强度高的主要原因.

关键词: 材料合成与加工工艺 , ZL201合金 , 半固态 , 近液相线铸造 , 性能

ZL201合金液相线铸造与二次加热的合金组织

王平 , 刘静 , 崔建忠

材料科学与工艺

为了研究半固态金属的成型规律,采用电子显微镜及图像分析仪,研究了近液相线半连续铸造ZL201合金的微观组织及其在二次加热过程中的变化.研究表明,在液相线温度下半连续铸造的ZL201合金组织为均匀、细小的蔷薇状组织,晶粒的平均等积圆直径为43.6 μm,晶粒平均圆度为1.88.经二次加热后,铸造组织逐渐转变为等轴晶.在620℃下加热20 min后,晶粒平均等积圆直径为111μm,晶粒平均圆度1.42.在640℃下加热20 min后,晶粒平均等积圆直径为108μm,晶粒平均圆度1.58.研究表明,近液相线半连续铸造可以获得理想的ZL201合金半固态坯料.

关键词: 近液相线铸造 , 半连续铸造 , 半固态 , 非枝晶 , 二次加热

201×7阴离子交换树脂对低浓度铂的吸附性能

赵德鹏 , 杨瑞四 , 邹安琴 , 王世雄 , 郭洪 , 杨项军

贵金属

研究了用201×7强碱性阴离子交换树脂对氯化浸出液中低浓度铂的吸附性能，考察了树脂用量、吸附时间、pH值、反应温度等因素对树脂吸附铂的影响。实验结果表明，pH=1.0时树脂的吸附效果最佳，静态饱和吸附容量可达到190 mg Pt/g干树脂，铂在201×7树脂上的吸附是吸热反应，温度升高有利于铂的吸附，吸附反应热焓变?H=36.72 kJ/mol，熵变为?S=0.190 kJ/(mol·K)。对201×7树脂吸附铂的吸附等温模型及动力学进行了分析，结果表明，吸附平衡过程符合 Langmuir等温式，且为优惠吸附；铂的吸附过程符合准二级动力学方程，准二级常数为 k2=1.58×10-4 g/(mg·min)。用2.4 mol/L的高氯酸可将载铂树脂中的铂洗脱，洗脱率为83%。

关键词: 物理化学 , 阴离子交换树脂 , 铂 , 吸附 , 动力学 , 热力学