The deformation behavior of AZ61 Mg alloy during hot deformation has been investigated in wide temperature and strain rate range by a Gleeble simulator. Specimens are deformed in compression in the temperature range of 523~673 K and at strain rates of 0.001~1 s¬¬¬-1. It is found that the flow curves exhibit a peak and then decrease towards steady-state of classical DRX, which decrease with rising temperature and decreasing strain rate. The deformation behavior of the specimens can be attributed to the occurrence of strain hardening and softening. As stress decreases, the strain hardening rate declines at a fast rate when temperature rises or strain rate decreases. The shapes of θ-σ curves indicate some important features such as subgrain formation, the critical stress, the peak stress and steady stress. The onset of DRX can be determined by the point of inflection on θ-σ or lnθ-σ curves.
关键词:
AZ61 Mg alloy
,
null
,
null
Liufa LIU
,
Chen LU
,
Wenjiang DING
,
Akio Hirose
,
Kojiro F.Kobayashi
材料科学技术（英文）
The effect of δ phase on the hydrogen embrittlement (HE) sensitivity of Inconel 718 was investigated by conducting notch tensile tests. Notch tensile specimens with various precipitation morphologies of δ phase were prepared with different heat treatments, and hydrogen was charged into the tensile specimens before tensile tests via a cathodic charging process. The loss of notch tensile strength (NTS) due to the charged hydrogen was used to evaluate the hydrogen embrittlement sensitivity. The results show that δ phase has deleterious effect on NTSs, and the fracture of hydrogen-charged specimens initiated near the notch surfaces. The loss of NTS caused by precharged hydrogen can be greatly decreased by dissolving δ phase. δ-free Inconel 718 alloy is proposed for the applications in hydrogen environments.
关键词:
Superalloy
,
null
,
null
,
null
杨文虎
,
易冉
,
徐阳
,
惠思思
,
曹晓珑
绝缘材料
doi:10.3969/j.issn.1009-9239.2012.01.014
研究了不同外施工频电压下环氧树脂绝缘中的电树枝结构、生长的特性,并用Ding等提出的模型解释了电树枝的发展过程,模拟了其生长曲线.结果表明:在同一电压下,环氧树脂中电树枝的生长速度基本为恒定值,随外施电压的升高,电树枝分枝变少,生长速度基本呈指数增加,且利用模型模拟的生长曲线与实验测试的结果吻合,最后讨论了模型的物理基础.
关键词:
电树枝
,
环氧树脂
,
劣化
,
动力学
,
模型
,
模拟
陈伟亮
,
张宁
,
唐昭辉
,
丁学勇
材料研究学报
将Miedema模型与实验数据相结合得到适于Miedema模型的O和S的参数(O:电负性7.04、电子密度6.03、摩尔体积4.59;S:电负性5.8、电子密度3.24、摩尔体积6.97),计算了141种O的二元化合物和145种S的二元化合物生成焓其平均绝对误差(MAPE)分别为36.8％、32.4％.结合Ding导出的三元系相互作用系数计算模型,计算了1873 K时Fe基熔体中O和S与其它元素之间的相互作用系数.与实验数据的比较表明,除个别元素外,计算值与实验值之间误差不大且变化趋势比较一致.将误差较大的Nb、Ag、Pt的电负性参数由原来的4.05、4.35、5.65修正为4.31、4.17、5.57,使用Miedema模型的计算精度有很大的提高.
关键词:
材料科学基础学科
,
Miedema模型
,
含O和S熔体与合金
,
相互作用系数
,
参数的修正