Y.N. Sun
,
K.X. Zhang
,
X. Gao
金属学报(英文版)
Nanostructured C-Cu thin films were deposited by reactive sputtering method and co-sputtering method. The relationships between microstructures, properties, and depo-sition parameters were studied and the results obtained from TEM, AFM, and XPS.indicate that the thin films are nanostructural, and have good in-depth uniformity. Theselected area electron diffraction (SAED) found that the nanosize Cu particles havethe fcc structure and the others are amorphous carbon or nanocrystallized graphiticcarbon. The peak positions of the Cu and C in XPS indicate them to be at the ele-mental state. In the IR transmission spectrum, diamond two-phonon absorption andgraphite Raman peaks were observed, which suggests microcrystal diamond particlesand graphite components exist in the C-Cu film. The higher electrical resistivity wasobtained.
关键词:
C-Cu film
,
null
,
null
Journal of Alloys and Compounds
A solid solution with formula (Y1-xTbx)(3)GaO6 (x = 0-0.5) was prepared by solid-state reaction method. Powder X-ray diffraction (XRD) shows that Y3GaO6 is isostructural to Gd3GaO6 (Cmc2(1)), and the lattice parameters are a = 8.8364(1) angstrom, b = 11.0899(1) angstrom and c = 5.3937(1) angstrom. Atomic parameters were derived by Rietveld refinement of the XRD pattern. Photoluminescence (PL) spectra show a strong green emission of 543 nm from the D-5(4) -> F-7(5) transition of Th3+ at room and liquid nitrogen temperature. There is a wide saturation range of the PL intensity for the Th3+ content from x = 0.04-0.20, and a long life time about 1200 mu s for the green 543 nm emission at room temperature. (c) 2006 Elsevier B.V. All rights reserved.
关键词:
Y3GaO6;crystal structure;Tb3+ doped;photoluminescence;luminescence properties;dependence;y3al5o12;phosphor;ions;ce3+;tb-3;uv
Journal of Solid State Chemistry
The crystal structures of a series of compounds with the composition Ln(3)GaO(6)(Ln = Nd, Sm, Eu, Gd, Tb, Dy, Ho and Er) synthesized by solid-state reaction at 1400degreesC are investigated. X-ray diffraction shows that Ln3GaO6 has a non-centro symmetric orthorhombic structure (space group Cmc2(1)). Lattice parameters a, b, c and cell volume and the average distances between Ln(l)-O, Ln(2)-O of these compounds decrease with the decreasing of the radii of trivalent Ln ions, which accord with the expected lanthanide contraction behavior. There are two sites of seven-fold coordination for Ln atoms with oxygens, and Ga atoms are in oxygen tetrahedra which are distorted and elongated along the a-axis. Magnetization measurements indicate that the susceptibility X changes with temperature in Curie-type manner. (C) 2004 Elsevier Inc. All rights reserved.
关键词:
Ln(3)GaO(6);crystal structure;Rietveld refinement;X-ray diffraction;garnets
Journal of Luminescence
Ln(3+) (Ln = Nd, Sm, Eu, Gd, Dy, Ho, Er)-doped Y3GaO6 compounds were prepared by solid-state reaction, and their optical spectra such as absorption, photoluminescence, excitation and time-resolved spectra have been measured for Ln Nd, Sm, Dy, Ho, Er. X-ray powder diffraction shows that the lattice parameters of the compounds (Y(0.96)Ln(0.04))(3)GaO6 decrease with the decrease of the radii of trivalent Ln(3+) ions, indicating that Ln(3+) ions have substituted for y(3+) ions in the lattice. Optical spectra show that there are obvious absorptions at ultraviolet to visible region. The strong emissions in visible and infra-red region show that Y3GaO6 is a suitable host for rare-earth-doped laser crystal and phosphor materials. (C) 2004 Elsevier B.V. All rights reserved.
关键词:
crystal-field;absorption-spectra;luminescence;y3ga5o12;glasses;garnet;y2o3;ions;laf3;tb3
Journal of Solid State Chemistry
A serial of samples in Y2O3-Ga2O3-Tm2O3 pseudo-ternary system are prepared by solid-state chemical reaction method. The range of solid solution in (Y1-xTmx)(3)GaO6 is 0 < x < 0.384. Powder X-ray diffraction shows that the compounds crystallize in Gd3GaO6 (Cmc2(1))-type structure. The solid solubilities of Y3+xGa5-xO12 (x = 0-0.77) and Tm3+xGa5-xO12 (x = 0-0.62) are 37.5-47.11 at% Y2O3, and 37.5-45.26 at% Tm2O3, respectively. PL spectra of Tm-doped Y3GaO6 show that there is a sharp blue emission at similar to 456 nm from the D-1(2) -> F-3(4) transition at room temperatures with two lifetimes (similar to 5 and similar to 15 mu s) and a narrow saturation range of PL intensity for the Tm3+ content from x = 0.005 to 0.03. The sharp emission and long lifetime of (Y1-xTmx)(3)GaO6 indicate that Y3GaO6 is a potential phosphor and laser crystal host material. (c) 2005 Elsevier Inc. All rights reserved.
关键词:
Tm3+ -doped Y3GaO6;Y2O3-Ga2O3-Tm2O3 system;(Y1-xTmx)(3)Ga5O12 solid;solution;luminescence;crystal-structure;luminescence;phosphor;cations;ions;tb3
张兰河
,
李德生
,
王旭明
,
张海丰
硅酸盐通报
为了提高生物除磷效率,研究采用AOA-SBR工艺进行了长期连续除磷实验,考察不同温度下碳源(乙酸钠、丙酸钠、葡萄糖)对PAO与GAO竞争的影响.结果表明:当温度由10℃升高至25℃时,利用丙酸钠作为碳源时,污泥含磷量与含糖量分别从7.2％和5.1％升高至7.9％和6.3％,PHA转化量升高了23.1 mg/L,厌氧释磷量从105.9 mg/L升高至149.9 mg/L,VSS/MLSS由71％降低至65％;利用乙酸钠作为碳源时,污泥含磷量与含糖量分别从6.9％和5.3％升高至7.6％和6.7％,PHA转化量升高了23.9 mg/L,厌氧释磷量从73.8 mg/L升高至108.8 mg/L,VSS/MLSS由73％降低至71％;利用葡萄糖作为碳源时,污泥含磷量与含糖量分别从5.8％和6.3％升高至6.6％和8.8％,PHA转化量升高了33.2 mg/L,厌氧释磷量从37.4 mg/L升高至43.2 mg/L,VSS/MLSS由80％升高至88％.当温度升高至30℃时,3个反应器均出现厌氧末期PHA浓度下降和糖原浓度升高,厌氧释磷量减少,污泥含磷量均下降,污泥含糖量上升,VSS/MLSS均很高.与葡萄糖相比,采用乙酸钠和丙酸钠作为碳源,有利于PAO生长繁殖,PAO为优势菌种,抑制GAO增殖.同时,低温更有利于PAO的生长繁殖.
关键词:
温度
,
碳源
,
SBR
,
PAO与GAO
Ieee Transactions on Magnetics
The microstructure, magnetic properties and magnetostriction of Tb0.2Pr0.8(Fe0.4Co0.6)(infinity) (1.65 less than or equal to x less than or equal to 1.90) alloys has been studied. The Curie temperatures for the 1:2 and 1:3 phases decrease with increasing x, whereas the saturation magnetization increases with increasing cc. The remanent magnetization remains almost constant for all the samples and the coercivity decreases with increasing x. The spontaneous magnetostriction (lambda (111)) estimated from the splitting of the (440) lines is found to decrease with increasing x. The largest lambda (111) recorded for Tb0.2Pr0.8(Fe0.4Co0.6)(1.65) is 2900 ppm at room temperature.
关键词:
Laves phase;microstructure;spontaneous magnetostriction;alloys
Y.M.Hao1) and Y.Gao2) 1)Department of Physics
,
Tianjin Normal University
,
Tianjin 300074
,
China 2)Library
,
Tianjin Normal University
,
Tianjin 300074
,
China
金属学报(英文版)
tructuraland magnetic propertiesof Ho2 AlFe16 x Mnx( x= 0 8) compoundshave been in vestigated by means of x ray diffraction and magnetization measurements. Thecompoundshave a hexagonal Th2 Ni17 typestructure. With increasing x,the unit cell volumes have a smallincreaseinitially,followed by a greaterlinearincrease. The Curietemperatureandthe saturation magnetization of these compounds show marvelous drop with increasing x. The valuesofJRTofthecompoundsfor x =2 ,3 , and 4 are given.
关键词:
unit cellvolume
,
null
,
null
,
null
Journal of Alloys and Compounds
Pseudo-1-3 magnetostrictive particulate composites consisting of light rare earth (Sm and Nd)-based magnetostrictive Sm(1-x)Nd(x)Fe(1.55) particles with the Nd content x of 0-0.56 and randomly distributed sizes of 10-180 mu m membedded and aligned in a passive epoxy matrix are fabricated using the particulate volume fraction of 0.5. The quasistatic magnetomechanical properties of the composites are investigated and the results are compared with their monolithic alloys for various x. The composites exhibit similar qualitative trends in properties with the alloys for all x. The Sm(0.92)Nd(0.08)Fe(1.55) composite shows a large unsaturated magnetostriction lambda of -530ppm at 500 kA/m and a high piezomagnetic coefficient d(33) of -2.0 nm/A at 100 kA/m as a result of the magnetocrystalline anisotropy compensation between Sm(3+) and Nd(3+) ions in the Sm(0.92)Nd(0.08)Fe(1.55) alloy. (C) 2011 Elsevier B.V. All rights reserved.
关键词:
Light rare earths;Magnetocrystalline anisotropy;Magnetomechanical;properties;Negative magnetostriction;Magnetostrictive composites;Sm(1-x)NdxFe(1.55) alloys;terfenol-d
Journal of Alloys and Compounds
Stabilizer (B, Co)-free, light rare earth (Pr)-substituted Laves alloys (Tb(0.3)Dy(0.7))(1-x)Pr(x)Fe(1.55) (0 <= x <= 0.4) are synthesized, and their structural, magnetic, and magnetostrictive properties are investigated. X-ray diffraction analysis confirms the presence of single cubic Laves phase with an MgCu(2)-type structure in the (Tb(0.3)Dy(0.7))(1-x)Pr(x)Fe(1.55) alloys with 0 <= x <= 0.35. The lattice parameter a of the Laves phase increases, while the Curie temperature decreases, with increasing x from 0 to 0.35. The saturation magnetization of the alloys decreases with increasing x. The linear anisotropic magnetostriction lambda(a) (=lambda(parallel to) - lambda(perpendicular to)) shows a maximum of 1502 ppm at x = 0.25 as a result of the magnetocrystalline anisotropy compensation. (C) 2008 Elsevier B.V. All rights reserved.
关键词:
Alloys and compounds;Laves phase;Light rare earths;Magnetocrystalline;anisotropy;Magnetostriction;Terfenol-D;anisotropy compensation;boron