X.B. Tian
,
X.F. Wang
,
A.G. Liu
,
L.P. Wang
,
S. Y. Wang
,
B. Y. Tang and P. K. Chu 1)Advanced Welding Production & Technology National Key Laboratory
,
Harbin Institute of Technology
,
Harbin 150001
,
China 2)Department of Physics & Materials Science
,
City University of Hong Kong
,
China
金属学报(英文版)
The research on plasma immersion ion implantation has been conducted for a little over ten years. Much is needed to investigate including processing technlogy, plasma sheath dynamics, interaction of plasma and surface, etc. Of the processing methods elavated temperature technique is usually used in PIII to produce a thick modified layer by means of the thermal diffusion. Meanwhile plasma ion heating is more recently developed by Ronghua Wei et al[1]. Therefore the temeperature is a critical parameter in plasma ion processing. In this paper we present the theoretical model and analysize the effect of imlantation voltage, plasma density, ion mass,etc on the temperature rise.
关键词:
plasma immersion ion implantation
,
null
,
null
B.L. Li
,
H.M. Du
,
X.F. Wang
,
E.Y. Jiang
金属学报(英文版)
Fe-N thin films were fabricated on both 100Si and NaCl substrates by RF magnetron sputtering under low nitrogen partial pressure. The microstructure and magnetic properties of Fe-N thin films were investigated with the increase of the substrate temperature (Ts) and the annealing temperature (Ta). It is more difficult for nitrogen atoms to enter the Fe lattice under higher Ts above 150℃. The phase evolution is visible at higher Ta above 200℃. The phase transformation of α''-Fe16N2 occurred at 400℃. The change of crystal size with Ta was clearly visible from bright and dark field images. The clear high-resolution electron microscope (HREM) images of 110α, 111γ', 112α'', and 200α'' phases were observed. The interplanar distances from TEM and HREM match the calculated values very well. From the results of the vibrating sample magnetometer (VSM), the good magnetic properties of Fe-N films were obtained at 150℃ of Ts and 200℃ of Ta, respectively.
关键词:
Fe-N thin film
,
null
,
null
,
null
Superconductor Science & Technology
It is shown that the superconductivity in Ce(1-x)Gd(x)FeAsO(0.84)F(0.16) compounds can be modulated by internal (chemical) pressure. The internal pressure is induced by Gd substitution for Ce in CeFeAsO(0.84)F(0.16), which compresses the crystal lattice. The temperature dependences of resistivity and magnetization show that the superconducting-transition temperature T(c) is enhanced from 40 K for CeFeAsO(0.84)F(0.16) to 47.5 K for Ce(0.6)Gd(0.4)FeAsO(0.84)F(0.16). The increase and subsequent decrease of Tc upon application of external pressure, as observed previously in LaFeAsO(0.89)F(0.11), is entirely confirmed by the modulation of Tc of the Ce(1-x)Gd(x)FeAsO(0.84)F(0.16) superconductors by internal pressure.
关键词:
layered quaternary compound;43 k;iron
Journal of Applied Physics
Structural parameters have a critical impact on superconductivity in iron-based oxypnictide superconductors. Structural evolution study was performed on Ce(1-x)Gd(x)FeAsO(0.84)F(0.16) superconductors by the analysis of the x-ray diffraction patterns with Rietveld refinement. Substitution of Gd for Ce generates internal pressure that compresses the crystal lattice. The contraction of the c axis is also indicated by the reduction of Ce/Gd-As and Ce/Gd-O/F distances, while there is a slight increase in the As-Fe-As block size, which is compensated by a large reduction in the Ce/Gd-O/F-Ce/Gd block with Gd substitution. The diagonal Fe-As-Fe angle for Ce(0.6)Gd(0.4)FeAsO(0.84)F(0.16), with the highest T(c) among Ce(1-x)Gd(x)FeAsO(0.84)F(0.16) compounds, is 111.13 degrees. It is close to the ideal value of 109.47 degrees for the perfect FeAs tetrahedron, which is situated in the region of Fe-As-Fe bond angles where RFeAsO compounds tend to have the highest T(c). (C) 2011 American Institute of Physics. [doi:10.1063/1.3565408]
关键词:
layered quaternary compound;high-temperature superconductivity
崔雅静
,
陈永亮
,
杨烨
,
王雅真
,
张勇
,
赵勇
低温物理学报
通过先制备一种纳米尺寸的GdF_3作为GdFeAsO_(1-x)F_x样品中F的反应原料,在相对较低的温度(1120℃)下成功制备出一系列GdFeAsO_(1-x)F_x(x=0,0.05,0.1,0.15,0.2,0.25)多晶样品.X射线衍射结果表明,超导样品属四方ZrCuSiAs-type结构,晶格参数随着掺F量的增加而减小.扫描电子显微镜测试结果表明,样品具有片层状晶体形貌特征.当掺F量x=0.1时,样品表现出超导电性,超导转变温度为22K,随着掺F量的增多,超导转变温度升高.和其他制备方法相比,这种制备方法更有利于F的掺入,而且可有效减少样品中杂质相的含量.
关键词:
铁基超导体
,
ZrCuSiAs结构
魏惠元
稀有金属材料与工程
介绍了可适用钛金属0.4 m～1.2 m不同焦距、微粒胶片X射线照相用的KUPTF新型曝光曲线的制作原理及方法.试验结果表明,新型曝光曲线具有制作简便、经济实用、可兼顾底片象质和拍片效率的优点,是钛制压力容器现场变焦距透照选取准确管电压值的理想工具.
关键词:
钛
,
X射线照相
,
KUPTF
,
曝光曲线
梁庆华
,
史瑶
,
马望京
,
杨新民
,
李智
影像科学与光化学
doi:10.7517/j.issn.1674-0475.2014.02.150
X射线成像板的成像性能很大程度上取决于存储荧光粉材料的物理化学性能.本文采用水热制备方法,以BaCl2、EuBr2、NaBF4为反应原料,以乙二胺四乙酸(EDTA)为辅助剂制备了Ba7 F12 Cl2:Eu2+荧光粉.利用X射线粉末衍射(XRD)、场发射扫描电镜(SEM)、X射线能量损失谱(EDS)、拉曼光谱(Raman)、荧光光谱(PL)等对制备的Ba7 F12 Cl2:Eu2+进行了表征.根据反应条件对产物的影响,初步提出了产物的形成过程.结果表明:反应温度及EDTA用量对产物物相和形貌有显著影响;制备的Ba7 F12 C12:Eu2+荧光粉有较好的发光性能.
关键词:
荧光粉
,
水热合成
,
Ba7F12Cl2
,
成像板