Ming ZENG
,
Xinqiang YUAN
材料科学技术（英文）
Silica sol ceramic mold was made at room temperature with JN-30 silica sol, silica powder and NH4Cl. It is found that the harden time of silica sol ceramic mold is only 0.5 to 1.5 h under the amount of NH4Cl solution of 7% to 8% with 15% concentration, and less surface cracks occur by using vacuum drying. The proper vacuum drying process parameters: vacuum drying temperature is 80 to 100℃, drying time is 5 h and vacuum is 0.06 to 0.07 MPa. The harden mechanics, vacuum drying mechanics and the reason of less surface cracks of silica sol ceramic mold by vacuum drying were also analyzed in this paper.
关键词:
Silica sol
,
null
,
null
,
null
Bin TANG
,
Xinqiang YUAN
,
Tianfeng XUE
,
Jiacheng LI
,
Youyu FAN
材料科学技术（英文）
Crystallization behavior of the glass system AlF3-MgF2-CaF2-SrF2-BaF2-YF3-TeO2 (AMCSBY-TeO2) was studied by the nonisothermal method using differential thermal analysis. The activation energy E and Avrami exponent $n$ were determined by nonisothermal method. It is found that the value of E varies with increasing TeO2 and reaches a minimum at 10~mol~fraction TeO2, while n decreases from 3.65 to 1.78 with the addition of TeO2. X-ray diffraction shows that Ba2Te3O8, MgTe2O5, and SrTeO3 phase formed when the glasses were reheated. The addition of TeO2 changes the crystallization mechanism and improves the stability of the fluoroaluminate glass.
关键词:
Fluoroaluminate glass
,
TeO2
,
析晶
Transactions of Nonferrous Metals Society of China
A new process for the hydrometallurgy of refractory gold concentrates was presented. The process comprises grinding-leaching, intensified alkaline leaching (IAL), cyanidation and adsorption. In a stirring-type pulverizing-leaching tower mill, the concentrate is ground to <35. 6 μm of 95. 5 % while simultaneously leached by NaOH of 12 kg/t, then carried out intensified alkaline leaching for 48 h by NaOH of 108 kg/t in enhanced agitation tanks with the pulp concentration of 40% solids at the environmental temperature of 9. 5 &SIM; 13. 5 &DEG;C and the environmental pressure of 10(5) Pa. The oxidation rate of As is 94. 9%, and 47. 6% for S. The total consumption of NaOH is only 20% of that theoretically calculated under the conditions of full oxidation at the same oxidation rates of arsenic to arsenate and sulfur to sulfate. The gold leaching rate by NaCN in 24 h is increased from 9. 2% before pretreatment to 94. 2%. The consumption of NaCN is 7. 5 kg/t, which is one times less than that before pretreatment. The extraction cost of gold is about 422 Yuan/t.
关键词:
refractory gold concentrates;grinding-leaching;intensified alkaline;leaching (IAL);pretreatment;common temperature and pressure