Low cycle fatigue (LCF)tests under different total strain amplitudes have been conducted in order to ascertain the effect of precipitate sizes on LCF behavior of 8090 Al-Li alloy. A constant strain rate of 3×10-3s-1 and symmetrical triangular waveform were employed for all tests. It is found that the cyclic stress response of the alloy varied with the precipitate sizes and strain amplitudes. The materials in all conditions cyclically handen at first and the higher the strain amplitude, the greater the amount of hardening. The low cyclic flow stress is the highest in the peakaged condition. TEM and SEM observations demonstrated that cyclic stress-strain behavior and fracture mode of Al-Li alloy are closely related to an increase in the dislocation density and interaction between the precipitates and dislocations, sizes of δ particles and pricipitate free zone (PFZ) at grain boundaries.
关键词:
Al-Li alloy
,
null
,
null
李铂
,
周建江
,
夏伟杰
,
吴连慧
液晶与显示
doi:10.3788/YJYXS20142904.0605
直线是机载座舱显示画面中最基本的图元,其显示质量对于整个画面的显示效果影响较大,尤其是小角度下直线显示的“麻花”现象一直是影响显示效果的关键问题之一.为了提高小角度下直线的显示效果,本文提出了一种基于Wu算法的亮度渐变改进算法.该算法通过渐进地展现直线从轴方向上的亮度变化过程,减少亮度畸变,有效地改进了显示效果.通过Matlab仿真和FPGA实现,验证了该算法反走样后的小角度直线显示效果明显优于其他算法,而且结合中点画线法后,绘制时间与Wu算法相当.同时该算法还可改善大角度直线和圆弧的显示效果,消除了大角度直线的边缘锯齿,解决了圆弧在小角度部分的虚化问题.因此本文算法可用于对实时性和显示效果要求高的机载座舱显示系统,以缓解飞行员的视觉疲劳.
关键词:
座舱显示
,
反走样
,
改进Wu算法
,
小角度
,
FPGA实现
吴连慧
,
周建江
,
夏伟杰
,
陈雅雯
液晶与显示
doi:10.3788/YJYXS20153001.0163
对于光栅化的三角形,其边缘存在明显的锯齿现象,因此需要进行反走样处理.基于Wu直线反走样算法的思想,考虑了水平直线外侧直接添加插值点的算法和三角形三边外侧反走样的算法.综合两者的优点,在绘制光栅化的三角形的同时,边缘叠加Wu反走样直线,并考虑背景像素灰度值的作用.结果表明,改进的三角形光栅化的边缘反走样算法有效提高了三角形光栅化后边缘的显示效果,该算法计算量小,便于FPGA实现,可用于对图形显示质量要求很高的机载显示系统.
关键词:
反走样
,
Wu算法
,
光栅化
,
FPGA
胡跃鑫
,
冯玉林
,
姜伟
应用化学
doi:10.3724/SP.J.1095.2011.00521
采用不同尺寸的碳酸钙粒子增韧高密度聚乙烯,研究了不同温度下共混体系的临界粒子间距与碳酸钙粒子尺寸和含量之间的关系,确定了温度是Wu氏增韧理论临界粒子间判据适用性的重要影响因素.结果表明,在17℃下,临界粒子间距与碳酸钙粒子的尺寸和含量无关,该条件下Wu氏增韧理论临界粒子间距判据是适用的;而随着温度的升高,发现临界粒子间距依赖于碳酸钙粒子的尺寸,表明高温条件下,Wu氏增韧理论临界粒子间距判据不再适用.
关键词:
聚合物增韧
,
粒子间距
,
脆韧转变
余宏伟
,
王世森
,
王孝东
,
洪君
物理测试
针对鄂钢轧制的部分宽厚板表面出现结疤现象,应用金相显微镜、扫描电镜和能谱分析仪对Q345q热轧态钢板表面疤状物形态和成分进行观察,对形成原因进行分析并提出改进措施。结果表明：疤状缺陷为块状的非金属夹杂/渣,并在钢板表面形成凹坑,其成分为含有Si、Ti、Al、Ca、Mg的氧化物或硅酸盐、铝酸盐等,其主要为炼钢过程中的脱氧产物和合金的氧化产物。因此在生产过程中,通过去除钢水中夹杂物和清理铸坯等,减少非金属夹杂/渣,以提高钢板表面质量。
关键词:
Q345q
,
疤状缺陷
,
钢板
,
非金属夹杂
,
非金属夹渣
WANG Lei
,
GAO Cai-ru
钢铁研究学报(英文版)
Thermal mechanical control processing (TMCP), the combination of controlled rolling and controlled cooling, provides a powerful means of developing high-strength low alloy (HSLA) steels by intensive microstructural control. In the present investigation, the effects of TMCP parameters, consisting of the finish cooling temperature and the start rolling temperature in non-recrystallization region, on the final microstructure and mechanical properties of Q460q steel have been studied by tensile, Charpy impact tests, optical microscopy. The TMCP parameters for Q460q steel have been optimized by laboratory experiments. And the microstructure and properties of industrial product were coincident with the results of laboratory experiments.
关键词:
;TMCP;mechanical properties;M/A constituent;Q460q steel
王娟
,
李亚江
,
马海军
金属学报
采用扫描电镜(SEM)、能谱分析(EDS)、X射线衍射(XRD)和电子探针(EPMA)对Fe3Al/Q235扩散焊界面的析出相形貌进行观察和成分测定，研究微观析出相的形成以及工艺参数(T, t , p)的影响. 结果表明， Fe3Al/Q235扩散焊界面靠近Fe3Al一侧形成FeAl(Cr)析出相，是引起扩散焊接头脆性断裂的关键. 扩散焊温度T、保温时间t与析出相区宽度y符合抛物线规律: y2=3.5 (t-t0)exp[-5.6×104/(RT)]. 在降低加热温度和保温时间的条件下，增加焊接压力可促进Fe3Al/Q235界面原子的扩散，避免脆性析出相的形成，保证Fe3Al/Q235扩散焊接头的性能.
关键词:
Fe3Al合金
,
steel Q235
,
diffusion bonding