X L Tian1)
,
Y M Sun1)
,
S X Zhao1)and X C Chen2) 1) College of Materials Science and Engineering
,
Shandong University of Technology
,
Jinan 250061
,
China2) Institute of Physics
,
The Chinese Academy of Sciences
,
Beijing 100081
,
China
金属学报(英文版)
Thethermal parameterofthe bulk amorphous Zr41 Ti14 Ni10 Cu12 5 Be22 5 alloy thermal dif fusivity,thermalcapacity andcoefficientofthermalconductivityatthestateofsolid andsu percooled liquid hasbeen measuredinthisstudy.It wasfoundthatthecoefficientofthermalconductivity and thethermalcapacity vary significantly with temperature. An error occursinthe measurementofthecoefficientofthethermalconductivity andthethermalcapacity us ing the method adoptedin this paper bothintheglasstransition processand when crystalliza tion processappears.
关键词:
Zr41Ti14Ni10Cu12 5Be22 5
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null