A much higher elongation of a warm rolled superplastic Al-Li-Cu-Mg-Zr alloy was made under two-stage strain rate tests comparing with the single ones.During initial stage of deformation a deformation-induced continuous recrystallization which converted a subgrain structure into a recrystallized grain structure by a continuous increase in boundary misorientations had occurred.The higher the strain rate,the faster the continuous recrystallization and the finer the recrystallized grains.The fine recrystallized grain structure formed during the first stage deformation is the essential condition for the material to have high strain rate hardening and strain hardening during the low second stage superplastic deformation.The combination of strain rate hardening and strain hardening is the reason why the higher elongation may be obtained during two-stage superplastic deformation of the alloy.
关键词:
Al-Li alloy
,
null
,
null
,
null
LIANG Yong LI Ruiguo Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
ChinaInstitute of Corrosion and Protection of Metals
,
Aademia Sinica
,
Shenyang
,
110015
,
China
材料科学技术（英文）
Recent advances in laser coating technology including laser cladding,laser surface alloying and laser vapour deposition in China are reviewed in this paper.
关键词:
laser
,
null
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null