金属学报(英文版)
On the basis of analysis of low carbon steel fracture macro-features and micro-processes at low temperature,the definition was given of the characteristic transition temperature of brittleness,T_(pm),and its physical meaning was expounded.Discussion was carried out of phys- ical characteristic of variation at T_(pm) in respect of the fracture toughness and property of crack arrest.In addition,research was made on the application of T_(pm),which can give infor- mation about the transition of the fracture toughness,the property of crack arrest and critical crack size,to estimation the brittleness of low carbon steel at low temperatures.
关键词:
low carbon steel
,
null
,
null
,
null
,
null
B.W. Wang
,
H. Shen
金属学报(英文版)
Ni-Cr System solar selective thin solid films were prepared by d.c. magnetron reactivesputtering under the atmosphere of O2 and N2. Ni-Cr alloy was chosen as targetmaterial and copper sheets as substrate. Using SEM, Spectrophotometer and Talystepto analyze the relations between the selective characteristic and the structure, theformation and the thickness of the thin films. The aim is to obtain good solar selectivethin films with high absorptance and low emittance, which is applied to flat plate solarheat collectors.
关键词:
solar selective thin film
,
null
,
null
,
null
MA Zongyi YAO Zhongkai Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
The SiC_w/Al composite prepared by squeeze casting has a combination of superior room temperature specific strength and modulus together with excellent thermal properties.The extrusion can make an improvement on the strength and ductility of the composite from 582 MPa as squeeze casted up to 639 MPa,and on the transformation from isotropic to the anisotropic structure.This seems to be explained by the orientation of whiskers and the densification of dislocations in matrix.TEM observation indicates that the stacking fault is the usual planar defect on the SiC_w surface. composite;;SiC whisker;;Al alloy;;microstructure
关键词:
composite
,
null
,
null
,
null
LIANG Yong LI Ruiguo Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
ChinaInstitute of Corrosion and Protection of Metals
,
Aademia Sinica
,
Shenyang
,
110015
,
China
材料科学技术（英文）
Recent advances in laser coating technology including laser cladding,laser surface alloying and laser vapour deposition in China are reviewed in this paper.
关键词:
laser
,
null
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null
Yang LUO
材料科学技术（英文）
Due to continued growth in key markets, a broadening of application base and performance improvements, the market demands of NdFeB magnet increased steadily in 1998, and the global output of sintered NdFeB magnet exceeded 10,000 t, in spite of the economic recession in Asia. In 1998 China produced 3,850 t sintered NdFeB block magnet, with an annual growth rate of +22% over the output in 1997.
关键词: