金属学报(英文版)
When Sn segregated at grain boundaries of high induction oriented silicon steel,no remarka- ble interaction between Sn and other elements was observed.At the starting temperature of secondary recrystallization,950℃,a certain Sn still segregates at grain boundaries.Sn seems to act as a supplemental inhibitor through grain boundary segregation.According to theoreti- cal analysis,an addition of Sn may decrease the secondary recrystallization temperature of high induction oriented silicon steel,and it is in agreement with the experimental result.
关键词:
silicon steel
,
null
,
null
,
null
,
null
白璇
,
赵昆渝
,
姜雯
,
李俊
,
李绍宏
,
李智东
材料热处理学报
研究了淬火+回火(No.1钢)及淬火+冷处理+回火(No.2钢)两种处理工艺下,超级马氏体不锈钢组织和性能的差异.结果表明:两钢中基体组织均为回火马氏体,但经过冷处理的No.2钢马氏体板条更平直,尺寸更小.在No.1、No.2钢中,随回火温度的升高,逆变奥氏体含量的变化趋势都为先增高后降低.在No.1、No.2钢中逆变奥氏体达到最大值的回火温度分别为650℃,700℃.No.2钢中Ni元素富集点含量比No.1钢低,但Ni富集点数比No.1钢多.No.1、No.2钢的硬度变化趋势都为先快速降低后缓慢回升,但在相同回火温度下,No.2钢的硬度值更低.
关键词:
超级马氏体钢
,
冷处理
,
组织
,
硬度
,
逆变奥氏体
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null
陈继平
,
康永林
材料热处理学报
对工业生产的No.1微碳BH钢和No.2微碳BH钢热轧板、冷轧板和退火板的工艺和组织性能进行研究.结果表明,No.1和No.2微碳BH钢的γ织构组分在{111} <110>附近分别达到了最大值12 046和10.549.No.2微碳BH钢退火板平均晶粒尺寸均小于No.1微碳BH钢,细晶强化效果使得其强度略高.No.2微碳BH钢退火板铁素体晶界处和晶粒内均存在游离渗碳体,晶界处珠光体片层较少,No.1微碳BH钢退火板铁素体晶界处存在片层状珠光体和块状渗碳体,更多珠光体片层结构也使其强度较低.No.2微碳BH钢中较高含量P、Cr、Cu元素固溶在基体中引起固溶强化,碳氮化物析出的弥散强化作用,均弥补了C含量较低引起的强度下降.
关键词:
微碳
,
烘烤硬化钢
,
γ纤维织构
,
组织和性能
DING Hua
,
TANG ZhengYou
,
LI Wei
,
WANG Mei
,
SONG Dan
钢铁研究学报(英文版)
The mechanical properties and microstructure of two low carbon high manganese steels with 238% (No1) and 33% (No2) (mass percent) of manganese were investigated. The results showed that No1 steel possesses high strength and high plasticity, and No2 steel has a relatively high strength and extraordinary plasticity. The No1 steel exhibits both TRIP (transformation induced plasticity) and TWIP (twin induced plasticity) effects during the deformation; while only TWIP effect appeared under the same deformation condition for No.2 steel. The comparison between the microstructures and mechanical properties of two steels was made, and the strengthening mechanisms were also analyzed.
关键词:
manganese;TRIP;TWIP;microstructure;mechanical property