GAO Hua CAO Weijie ZHOU Deqi WANG Ruizhen Shanghai University of Engineering Science
,
Shanghai
,
China
金属学报(英文版)
A series of mixed mode tests were carried out on 18-8 stainless steel in boiling 42% MgCl_2 solution.The results show that for any K_Ⅱ/K_Ⅰ ratio,the SCC direction coin- cides well with the crack tip maximum normal stress plane,while the SCC resistance of the material reduces as the ratio of K_Ⅱ/K_Ⅰ increases.The experimental results were discussed in the light of anode dissolving mechanism and the effect of mixed mode loading on crack tip stress and strain.It is concluded that for fracture analysis if mixed mode cracks were simply taken into account as mode Ⅰ cracks,and only mode Ⅰ testing results as mode Ⅰ fracture criter- ion were employed,it may not be safe.
关键词:
18-8 stainless steel
,
null
,
null
Andrej Atrens
材料科学技术（英文）
Corrosion research by Atrens and co-workers has made significant contributions to the understanding of the service performance of engineering materials. This includes: (1) elucidated corrosion mechanisms of Mg alloys, stainless steels and Cu alloys, (2) developed an improved understanding of passivity in stainless steels and binary alloys such as Fe-Cr, Ni-Cr, Co-Cr, Fe-Ti, and Fe-Si, (3) developed an improved understanding of the melt spinning of Cu alloys, and (4) elucidated mechanisms of environment assisted fracture (EAF) of steels and Zr alloys. This paper summarises contributions in the following: (1) intergranular stress corrosion cracking of pipeline steels, (2) atmospheric corrosion and patination of Cu, (3) corrosion of Mg alloys, and (4) transgranular stress corrosion cracking of rock bolts.
关键词:
Stress corrosion cracking
,
null
,
null