GUO Shouren LU Dezhong Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China
金属学报(英文版)
The precipitation and dissolution together with their control of the primary η-phase in a high-Ti Ni-Fe-Cr base superalloy have been investigated.The precipitation of primary η-phase was found to be closely related to Ti or Al content and solidification rate of the alloy. The aggregation of blocky η-phase may remarkably reduce the tensile strength,ductility and rupture life of the alloy.The temperature-time relation of dissolution of the primary η-phase obeys T=1370-86.1 lgt for as-cast superalloy.The formation of primary η-phase may be prevented by the reasonable control of Ti or Al content and smelting process.The adoption of treatment under large hot deformation and homogenization may be the remedy for unfavorable influence of η-phase.
关键词:
superalloy
,
null
,
null
,
null
MA Zongyi YAO Zhongkai Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
The SiC_w/Al composite prepared by squeeze casting has a combination of superior room temperature specific strength and modulus together with excellent thermal properties.The extrusion can make an improvement on the strength and ductility of the composite from 582 MPa as squeeze casted up to 639 MPa,and on the transformation from isotropic to the anisotropic structure.This seems to be explained by the orientation of whiskers and the densification of dislocations in matrix.TEM observation indicates that the stacking fault is the usual planar defect on the SiC_w surface. composite;;SiC whisker;;Al alloy;;microstructure
关键词:
composite
,
null
,
null
,
null
Journal of Magnetism and Magnetic Materials
Magnetization curves of the ternary tetragonal compound Lu2Fe14C were measured in an extracting-sample magnetometer in the temperature range from 1.5 to 300 K. The temperature dependence of the magnetic properties of Lu2Fe14C is discussed.
关键词:
anisotropy
Corrosion
This paper introduces the design of a localized corrosion rate monitoring instrument that can monitor and evaluate the maximum and stable localized corrosion rate of a nonpassivable metal in a corrosive environment by measuring the current density in a corrosion sensor with an occluded anode.
关键词:
instrument;localized corrosion rate;monitor
Solid State Communications
Magnetic anisotropy fields at room temperature of ternary tetragonal compounds of R2Fe14C(R = Lu, Gd, Nd) and R2Fe14B(R = Gd, Nd) were determined by Singular-Point-Detection (SPD) technique. The magnetocrystalline anisotropies of the carbides were found to be larger than those of their corresponding borides, indicating that the outstanding permanent-magnetic properties may be obtained in the R2Fe14C-based alloys.
关键词:
Juhua HUANG
,
Jinjun RAO
,
Xuefeng LI
材料科学技术（英文）
Sheet metal forming is widely applied to automobile, aviation, space flight, ship, instrument, and appliance industries. In this paper, based on analyzing the shortcoming of general finite element analysis (FEA), the conception of parametric finite element analysis (PFEA) is presented. The parametric finite element analysis, artificial neural networks (ANN) and genetic algorithm (GA) are combined to research thoroughly on the problems of process parameters optimization of sheet metal forming. The author programs the optimization scheme and applies it in a research of optimization problem of inside square hole flanging technological parameters. The optimization result coincides well with the result of experiment. The research shows that the optimization scheme offers a good new way in die design and sheet metal forming field.
关键词:
Sheet metal forming
,
null
,
null
,
null
J.Q.ZHANGD.J.YOUNG
中国腐蚀与防护学报
Metaldusting attacks iron, low and high alloy steels and nickel-or cobalt-base alloys by disintegrating bulk metals and alloys into metal particles in a coke deposit. It occurs in strongly carburising gas atmospheres (carbon activity aC>1) at elevated temperatures (400 ℃~1000 ℃). This phenomenon has been studied for decades, but the detailed mechanism is still not well understood. Current methods of protection against metal dusting are either directed to the process conditions-temperature and gas composition-or to the development of a dense adherent oxide layer on the surface of the alloy by selective oxidation. However, metal dusting still occurs by carbon dissolving in the base metal via defects in the oxide scale. The research work at UNSW is aimed at determining the detailed mechanism of metal dusting of both ferritic and austenitic alloys, in particular the microprocesses of graphite deposition, nanoparticle formation and underlying metal destruction. This work was carried out using surface observation, cross-section analysis by focused ion beam and electron microscopic examination of coke deposits at different stages of the reaction. It was found that surface orientation affected carbon deposition and metal dusting at the initial stage of the reaction. Metal dusting occurred only when graphite grew into the metal interior where the volume expansion is responsible for metal disintegration and dusting. It was also found that the metal dusting process could be significantly changed by alterations in alloy chemistry. Germanium was found to affect the iron dusting process by destabilising Fe3C but increasing the rate of carbon deposition and dusting, which questions the role of cementite in ferritic alloy dusting. Whilst adding copper to iron did not change the carburisation kinetics, cementite formation and coke morphology, copper alloying reduced nickel and nickel-base alloy dusting rates significantly. Application of these fundamental results to the dusting behaviour of engineering alloys is discussed.
关键词: