TIME-DEPENDENT FATIGUE AND ITS MICROMECHANISM OF SUPERALLOY GH169 UNDER OXIDATION

HE Jinrui LU Younian WANG Qingsui SU Hansheng ZHANG Xueduo WU Mingchang ZHU Qiao Beijing Institute of Aeronautical Materials , Beijing , China P.O.No.81—23 , Beijing 100095 , China

金属学报(英文版)

The time-dependent fatigue and its micromechanism of superalloy GH169 at 650℃ have been studied.Under the same stress and duration,its cyclic life in Ar is shorter than that in air.The damage mechanism is mainly of the interaction between high temperature oxidation and fa- tigue.The fracture surface of GH169 specimen oxidized at 650℃ in air is revealed to be cov- ered with a dense and even oxide film,but in Ar,with uncontinuous oxide particles.As the time prolonged,the Cr_2O_3 content in the surface oxides increases in air and decreases in Ar.

关键词: superalloy GH169 , null , null , null

Institute of Materials Science at Jilin University——A Brief Overview

WANG Yuming Institute of Materials Science , Jilin University , Changchun , 130023 , China

材料科学技术（英文）

关键词:

Image analysis of periodic rain accelerated corrosion of aeronautical aluminium alloys

Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing

Periodic rain tests have been carried out for simulating atmospheric corrosion of aeronautical aluminium alloys. A digital image preprocessing and analysis method based on wavelet transformation was used to study the corrosion morphology of aluminium alloys samples, through which an image feature parameter 8 was extracted and discussed. The influences of orthogonal experiment parameters on acceleration were analyzed according to image feature parameter 6 with analysis of variance (ANOVA) method, and the optimal parameters for accelerated corrosion test were also obtained. The result was shown to be consistent with that from weight loss method. (c) 2007 Elsevier B.V. All rights reserved.

关键词: aeronautical aluminium alloys;accelerated corrosion;linage analysis;simulated environment;atmospheric corrosion;electrochemical impedance;pitting corrosion;exposure;steel;zinc

小角度直线反走样的改进Wu算法

李铂 , 周建江 , 夏伟杰 , 吴连慧

液晶与显示 doi:10.3788/YJYXS20142904.0605

直线是机载座舱显示画面中最基本的图元,其显示质量对于整个画面的显示效果影响较大,尤其是小角度下直线显示的“麻花”现象一直是影响显示效果的关键问题之一.为了提高小角度下直线的显示效果,本文提出了一种基于Wu算法的亮度渐变改进算法.该算法通过渐进地展现直线从轴方向上的亮度变化过程,减少亮度畸变,有效地改进了显示效果.通过Matlab仿真和FPGA实现,验证了该算法反走样后的小角度直线显示效果明显优于其他算法,而且结合中点画线法后,绘制时间与Wu算法相当.同时该算法还可改善大角度直线和圆弧的显示效果,消除了大角度直线的边缘锯齿,解决了圆弧在小角度部分的虚化问题.因此本文算法可用于对实时性和显示效果要求高的机载座舱显示系统,以缓解飞行员的视觉疲劳.

关键词: 座舱显示 , 反走样 , 改进Wu算法 , 小角度 , FPGA实现

∑-N相互作用的研究及4∑He结合能的计算

曹会英 , 刘广东 , 刘家荣

原子核物理评论 doi:10.3969/j.issn.1007-4627.2007.04.004

基于SU(3)夸克模型,用共振群方法研究了两种理论下的∑-N相互作用,得到了它们的相互作用非定域位以及∑超子与3He壳心核的相互作用势,并在此基础上计算了4∑He基态结合能.计算结果表明,SU(3)夸克模型能较好地描述两种理论下的∑-N相互作用及∑超子与3He壳心核的相互作用势,同时由其得到的4∑He基态结合能也与实验值基本相吻合.

关键词: SU(3)手征夸克模型 , 共振群 , 非定域位 , 结合能

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null

SU-8光刻胶与Ni基底结合性的分子模拟

杜立群 , 郭照沛 , 张晓蕾

高分子材料科学与工程

运用分子动力学模拟软件Materials Studio针对SU-8胶与Ni基底的结合性进行模拟分析,计算了不同前烘温度下SU-8胶与Ni(100)面的结合能,发现在343K的前烘温度下,光刻胶与基底的界面结合能达到最大,说明此时界面结合最好.通过对SU-8胶与Ni基底的相互作用能分析,发现影响结合能的主要因素是两种分子之间的范德华力,其中色散力起主要作用,其值是排斥力的近两倍.

关键词: SU-8光刻胶 , Ni基底 , 结合能 , 分子动力学模拟

THERMAL NUCLEATION AND GROWTH OF He BUBBLES IN He IMPLANTED STAINLESS STEELS

ZHANG Lei WANG Peixuan TAO Rong MA Ruzhang ZHANG Guoguang University of Science and Technology Beijing , Beijing , China professor , Department of Materials Physics.University of Science and Technology Beijing.Beijing 100083 , China

金属学报(英文版)

Nucleation and growth of He bubbles at different annealing temperatures T≤1023 K in stain- less steels HR-2 and SS321,implanted with He~+(40-70 keV.1×10~(16)-6× 10~(17) He~+/cm~2),were ohserved under TEM.T=0.45T_m seems to be a transition temperature.The He bubbles continue mainly their nucleation at 0.3T_m< T<0.45T_m,and grow predominantly at T≥0.45T_m,due probably to migration and coalescence by surface diffusion of metal atoms around the bubbles.The apparent activation energies for the growth are found to he 0.41 and 0.31 eV for HR-2 and SS321 respectively.The bubble density in HR-2 is greater than that in SS321 within whole measuring temperature range,and the onset temperature of rapid swelling is also higher.It is believed that the resistance of HR-2 to He is superior to that fo SS321.

关键词: stainless steel , null , null , null , null

Two-step magnetization in a spin-chain system on the triangular lattice: Wang-Landau simulation

Physical Review B

The Wang-Landau algorithm is used to study the thermodynamic and magnetic properties of triangular spin-chain system based on two-dimensional Ising model in order to understand the magnetic-order dynamics in Ca(3)Co(2)O(6) compound. The calculated results demonstrate that the equilibrium state of the rigid spins produces the two-step magnetization curve at low temperature even when the random-exchange term is considered. This work indicates that the four-step magnetization behavior observed experimentally must be due to the nonequilibrium magnetization.

关键词: calcium compounds;exchange interactions (electron);Ising model;magnetisation;thermodynamics;one-dimensional ca3co2o6;density-of-states;compound ca3co2o6;phase-diagram;proteins;crystal

高温退火后含He纳米晶钛膜中He相关缺陷的演化

李悦 , 邓爱红 , 刘莉 , 王康 , 谢莎

材料研究学报

利用x射线衍射(xRD)和慢正电子束分析(SPBA)技术研究高温退火后含He钛膜的微观结构和钛膜内He相关缺陷的演化.XRD分析表明,高温退火后Ti和Si在高温下发生反应形成稳定的多晶TiSi2化合物,He原子的掺入会影响TiSi2晶体的择优取向,而对TiSi2晶粒尺寸的影响较小.SPBA结果表明,室温下,钛膜内的缺陷浓度或尺寸会随着掺He浓度的增加而增大;高温退火后,当He浓度小于5％(原子分数,下同)时(除2％外),钛膜内的He相关缺陷浓度随着He浓度增加相应地增加.当He浓度增加到14％时,高温会使较高浓度的He原子、He-空位复合体以及小He泡迁移聚集形成一些尺寸较大He泡,而较大He泡周围与He相关的小尺寸缺陷的浓度则会发生相应地减少.

关键词: 金属材料 , 含He钛膜 , 直流磁控溅射 , He相关缺陷 , XRD , SPBA