The solidification microstructure and phase composition of Ni-base superalloy FGH95 pow- der with different mesh size have been investigated.The structure transition was found from dendrite in major into cellular structure as the powder size reduces and the cooling rate in- creases.The predominant phase was identified as MC-type carbide,with different morphologies,which may be related to their composition and the condition of solidification.Minor phases,such as boride,Laves and primary γ' are also present as ac- companiments of the carbide.
关键词:
powder metallurgy
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,