Hao GUO
,
Guangfu LI
,
Xun CAI
,
Jianjiang ZHOU
,
Wu YANG
材料科学技术（英文）
The stress corrosion cracking (SCC) behaviour of X-70 pipeline steel in near-neutral pH solutions was studied $via$ slow strain rate testing (SSRT). The results showed that the cracking mode of X-70 pipeline steel in near-neutral pH solutions was transgranular at different temperatures and applied potentials with the feature of quasi-cleavage. The pH value of the solution decreased with increasing the addition of CO¬2, which increased the susceptibility to SCC. SCC susceptibility increased as the applied potential moved towards the cathodic direction, suggesting that hydrogen induced cracking (HIC) dominated the cracking process at cathodic potentials. The slight decrease of pH values with decreasing temperature of the solution increased the susceptibility to SCC, which attributed to the change of solubility of CO¬2 in the solution at different temperatures. The propagating directions of SCC cracks were different at different potentials. At rather negative cathodic potentials, the cracks were almost perpendicular to the tensile axis, while at free corrosion potential and near anodic potentials, cracks were nearly at 45 degree, and in the range of moderate cathodic potentials both propagating directions could be observed.
关键词:
Pipeline steel
,
null
,
null
,
null
Hao GUO
,
Guangfu LI
,
Xun CAI
,
Ruipeng YANG
,
Wu YANG
材料科学技术（英文）
The cracking behaviour of X-70 pipeline steel in near-neutral pH solutions was studied under different modes of cyclic loading. The crack propagation process of X-70 pipeline steel under low frequency cyclic loading condition was controlled mainly by stress corrosion cracking (SCC) mechanism. Under mixed-mode cyclic loading, both higher tensile stress and shear stress made cracks easier to propagate. Applied cathodic potentials and high content of carbon dioxide in solutions also promoted the propagation of cracks. The propagation directions of cracks were different under different cyclic loading conditions. Under mode I (pure tensile stress) cyclic loading condition, cracks were straight and perpendicular to the tensile stress axis, while under mixed-mode I/III (tensile/shear stress) cyclic loading, cracks were sinuous and did not propagate in the direction perpendicular to the main tensile stress axis. Under the mixed-mode cyclic loading, cracks were much easier to propagate, suggesting that shear stress intensified the role of tensile stress. In addition, shear stress promoted the interaction between cracks, resulting in easier coalescence of cracks.
关键词:
Pipeline steel
,
null
,
null
,
null
中国腐蚀与防护学报
N。1Atmospheric Corrosivlty for Steels………………………………………………… .LIANG Caideng HO[I i。-tat（6）Caustic Stress Corrosion Cr。king of Alloy 800 Part 2.The Effect of Thiosul执e……………………………………… KONG De-sheng YANG Wu ZHAO Guo-zheng HUANG De.ltL。ZHANG Yu。。he CHEN She。g-bac（13）SERS slid E16CttOCh6iniC81 Stlldy Of Illhibit1Oli M6ch＆tllsth Of ThlollY68 Oil ITOll ID H....
关键词:
李凤娟
,
吕国光
金属世界
doi:10.3969/j.issn.1000-6826.2014.04.14
通过对烧结配料所需原料及对冷烧结矿成品检验采制样方法的分析，找出影响检验结果真实性的因素，采取有效的改进措施，使本钢原料厂一次配料、本钢炼铁厂265 m2烧结二次配料及265 m2烧结系统各项稳定率有了很大的提高，烧结矿实物质量和各项技术质量指标有了很大的进步，保证了高炉的稳定顺行。
提高本钢265 m2冷烧结矿及原料检验代表性的实践
Practice of Improving the 265 m2 Cold Sinter and Raw Material Inspection Representative
供稿|
李凤娟,吕国光/
LI Feng-juan, LV Guo-guang
DOI：10.3969/j.issn.1000-6826.2014.04.14
导读内容
本钢炼铁厂265 m2烧结机生产所需要的含铁原料比较复杂，一次配料料种较多，且烧结含铁原料是由本钢原料厂二车间供料，原料质量的不稳定，会影响烧结矿质量的提高和新一号高炉的强化及高炉技术指标的改善。本钢质量管理中心驻冷烧检查站加强了对烧结配料所需原料及对冷烧结矿成品检验采制样代表性的研究，采取了一些改进措施，达到了良好的效果。含铁料成分稳定率、烧结矿各项质量和技术指标在稳步地提高。下面，对本钢质量管理中心驻冷烧检查站就提高采样及检验过程的准确性所采取的措施和办法进行说明。