B.X. Gu
,
J.R. Zhang
,
B.G. Shen and H Wang (Department of Physics
,
Nanjing University
,
Nanjing 210093
,
China)(State Key Lab. of Magnetism
,
Institute of Physics
,
Chinese Academy of Sciences
,
Beijing 100080
,
China)(Department of Physics
,
Southeastern University
,
Nanjing 210008
,
China)
金属学报(英文版)
The phase component and Curie tempemture of Nd4(Fe1-xCrx)77.5B18.5 (0 0.1. The magnetic measurement shows that Curie temperutures of Fe3B and Nd2Fe14B phases decrease with increasing Cr content. The influence of the substitution of Cr for Fe was discussed.
关键词:
Nd_4(Fe_(1-x)Cr_x)_(77.5)B_(18.5)alloy
,
null
,
null
H.P. Chen and Z.J. Deng (State Key Lab. for Mechanical Behavior of Materials
,
Xi'an Jiaotong University
,
Xi'an 710049
,
China)
金属学报(英文版)
The effect of specimen thinkness on JR resistance curve has been investigated using low and middle strength steels. As the J dominance regime is reached, the initial J-integral values, J(i), are definite even if the elastic component Ji(e) and plastic component Ji(p)vary with the thinkness of specimen. The wider the specimen width, the larger the Ji(e)/Ji and the smaller the Ji(p)/Ji. The crack propagation resistance, dJR/da and dJp/da, decreases, while dJe/da increases linearly with increasing specimen thinness.Based on the above experimental results, an empirical formula dJ/da = α+β. B is given, which can be used to evaluate the safety of practical structural components.A modified J-integral is presented, upon which a new view is Put forward that the increase in crack growth resistance is induced mainly by the increase in the plastic J-integral component with the crack propagation,
关键词:
: fracture mechanics
,
null
,
null
,
null
Physical Review B
The Hamiltonian for a four-sublattice Heisenberg ferrimagnet or ferromagnet with different exchange constants (J(ab) = J(cd) not equal J(bc) = J(da)) was established. An extended Bogoliubov transformation was developed by solving an equation group, consisting of 20 equations and 20 unknowns. The procedure for solving the equation group was carried out by introducing a simple way of reducing the numbers of the equations and the unknowns. The spin-wave spectra in the present system have been determined by performing the standard Holstein-Primakoff transformation and the Bogoliubov one. It has been found that the spin-wave spectra of the present system depend on the exchange constants and that the degeneracy of the spin-wave spectra remains. The results for a special case (J(ab) = J(bc)) i.e., an antiferromagnet are discussed briefly. The spin-wave spectra of the four-sublattice Heisenberg antiferromagnet are found to be degenerative also and they are linear in k for small k.
关键词:
model
Y.G. Cao
,
X.Y. Sun
金属学报(英文版)
J-integral and crack opening displacement δ(COD) were important parameters for characterization of fractures in engineering materials. The relationship between J-integral and COD has been investigated for a long time and was enerally represented as J = m σyδ, where σy is the yield strength and m is a function of specimen geometry and material properties. To determine the value of m, extensive studies and experiments have been performed. The method that used the fracture-surface topography analysis (FRASTA) for determining J-integral from fracture surfaces of materials was introduced. On the basis of the relationship between COD and fracture surface average profile, the relationship between J-integral and COD was deduced and compared with the generally used equation. The method was experimentally confirmed to be able to provide a new way to determine the relationship between J-integral and COD.
关键词:
FRASTA
,
null
,
null
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
null
,
null
金属学报
在工程上,经常由于应力腐蚀开裂和氢脆引起中强度钢结构件发生滞后破坏。这类脆断往往从结构件中预先存在的疲劳或焊接裂纹处开始,因此,运用传统的光滑试样的检验方法不能反映这类破坏的特点。 本文将弹塑性断裂力学中的J积分概念用于滞后破坏的研究,提出用带预制疲劳裂纹的悬臂弯曲试样测定J积分的临界值J_(Ic)和应力腐蚀开裂阈值J_(Iscc)的方法。测定了40CrNiMo钢的J_(Ic)值及其在硫化氢水溶液中的J_(Iscc)值。通过和三点弯曲方法测定的J_(Ic)值的对比,以及和满足线弹性条件时直接测定的应力强度因子K_I值的对比,说明这种方法的可靠性。最后,对悬臂弯曲方法的特点进行了讨论。