YANG Jun
,
WANG Xin-hua
,
JIANG Min
,
WANG Wan-jun
钢铁研究学报(英文版)
The influence of calcium treatment on non-metallic inclusions had been studied when control technology of refining top slag in ladle furnace was used in ultra-low oxygen steelmaking. A sufficient amount aluminium was added to experimental heats for final deoxidizing during BOF tapping, and the refining top slag with strong reducibility, high basicity and high Al2O3 in ladle furnace was used to produce ultra-low oxygen steel and the transformation of non-metallic inclusions in molten steel was compared by calcium treatment and no calcium treatment. The results show that the transformation of Al2O3→MgO·Al2O3 spinel→CaO-MgO-Al2O3 complex inclusions has been completed for aluminum deoxidation products and calcium treatment to molten steel is unnecessary when using the control technology of ladle furnace refining top slag to produce ultra-low oxygen steel, and the complex inclusions are liquid at the temperature of steelmaking and easily removable to obtain very high cleanliness steel by flotation. Furthermore, the problems of nozzle clogging in casting operations do not happen and the remaining oxide inclusions in steel are the relatively lower melting point complex inclusions.
关键词:
ultra-low oxygen
,
top slag
,
deoxidization
,
aluminium
,
oxide inclusion
,
calcium treatment
Q.S. Liu1
,
2
,
3)
,
L.C. Zhao3)
,
G.X. Dong2) and N.J. Gu1) 1) Heibei University of Technology
,
Tianjin 300130
,
China 2) Tianjin Institute of Technology
,
Tianjin 300191
,
China 3) Harbin University of Technology
,
Harbin 150001
,
China
金属学报(英文版)
Theconstruction changinginthereversetransformation ofthestress induced εMin Fe 17 Mn 10 Cr 5 Si 4 Ni alloy is carefully inspected in transmission electron microscope, and then stress induced εM procedure of reverse transformation is analyzed. The behavior of reverse transformationisdissimilar when the organization of εMis different. The reversetransfor mation ofεM withtheshapeofsingle plateandstripisrelativelyeasy,anditsreversibilityincrystallographiciseasilytocarryout,fortheεM with multilayerstructure,thereversetrans formationtakes placein isolatedlayers, fortheεMthat grows well,thereversetransforma tion isrelatively difficult becauseofthe ductile harmonization between itsinternalorganiza tion structures.
关键词:
stress induced εM
,
null
,
null
徐佩
,
卢旭鑫
,
汪传斌
,
杨善中
,
孙晓红
,
丁运生
高分子材料科学与工程
为改善多壁碳纳米管(MWNT)在低密度聚乙烯(LDPE)中的分散性及复合材料的界面特性,采用溴化-1-十六烷基-3-甲基咪唑基离子液体([C16min]Br)对MWNT进行表面改性,并用Raman光谱对改性效果进行了表征.将经过修饰的碳纳米管(MIL)与LDPE熔融共混得到MIL/LDPE复合材料,采用场发射扫描电子显微镜(FESEM)和阻抗分析仪(LCR)对复合材料的结构与介电性能进行了分析.结果表明,相比与MWNT/LDPE(渗流阈值为5.2％,介电常数为82,介电损耗为0.93),MIL/LDPE(渗流阈值为9.1％,介电常数为169,介电损耗为0.51)介电常数增大,介电损耗降低.并且在低温时,MIL/LDPE介电常数随温度的变化甚小,显示出良好的温度-介电常数特性.
关键词:
咪唑基离子液体
,
碳纳米管
,
低密度聚乙烯
,
介电性能
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
倪永中
,
徐鸿
材料科学与工程学报
本文提出了一种基于粒子群算法和有限元方法的弹塑性本构方程参数的确定方法,并在此基础上开发了参数自动优化系统CMPI(Constitutive Material Parameter Identification).通过使最小二乘形式的目标函数达到极小值,实现参数的动态寻优;模型参数作为粒子群优化模块的输入,采用应变(应力)控制方法,调用材料非线性有限元模块计算特定参数时的应力(应变)响应,并计算与实验数据的误差,从而实现优化过程.CMPI目前适用于A-F类模型(Chaboehe、Ohno-Wang、Jiang-Sehitoglu)的参数优化,以此为基础,不难扩展到其他材料模型.
关键词:
粒子群
,
材料非线性
,
有限元
,
Ohno-Wang 模型
张剑
,
周储伟
,
雷笑
,
叶见曙
,
卓家寿
复合材料学报
对于混杂CFRP/GFRP筋高性能混凝土(HPC)梁,研究一种新的三维非线性梁壳组合单元,对HPC梁进行了全过程分析.引入实体退化壳单元理论,利用空间梁单元模拟预应力CFRP筋,并根据CFRP筋单元节点线位移和转角位移的协调性,推导CFRP筋单元对梁壳组合单元刚度矩阵的贡献,同时对GFRP筋和HPC梁采用分层壳单元模拟.并运用Jiang屈服准则、Madrid强化准则等描述混凝土的材料非线性,提出一种新的非线性梁壳组合单元,研制相应的三维非线性计算程序.计算结果与试验数据吻合良好,说明本文构造的非线性梁壳组合单元的正确性和研制程序的可靠性,以及混凝土材料非线性描述的合理性;采用组合单元能准确模拟CFRP筋的几何构形,能综合考虑其拉压弯剪性能,利于全面地反映配筋对结构的增强作用.
关键词:
CFRP筋
,
GFRP筋
,
梁壳组合单元
,
HPC梁
,
材料非线性
王玉东
,
付鹏
,
李晓光
,
刘民英
,
赵清香
高分子材料科学与工程
用差示扫描量热(DSC)研究了尼龙612的等温结晶动力学.实验结果表明,在所研究的等温结晶温度范围内(184℃、186℃、188℃、190℃、192℃),尼龙612达到最大结晶速率时的时间、半结晶期和动力学结晶速率常数分别为:O.12min、0.19 min、0.22 min、0.29 min、0.59 min;0.15 min、0.22 min、0.24 min、0.33 min、0.64 min和22.03 min<'-1>、23.28min<'-1>、8.85 min<'-1>、5.15 min<'-1>、1.93 min<'-1>.等温结晶过程符合Avrmi方程,二次结晶现象不明显.在等温结晶过程中得到的Avrmi指数n在1.81～2.32之间,由理论分析可知,尼龙612等温结晶是一维生长和二维盘状生长.由Arrhenius方程求得尼龙612的等温结晶活化能ΔE=-209.5 kJ/mol.
关键词:
尼龙612
,
等温结晶动力学
,
结晶活化能
靳瑞敏
,
陈兰莉
,
罗鹏辉
,
郭新峰
,
卢景霄
材料导报
用玻璃作衬底在不同温度下用PECVD法直接沉积非晶硅(a-Si∶H)薄膜,在400℃和500℃分别光退火5min、10min、20min、30min、40min、60min、120min,用拉曼光谱分析前后样品,发现随着晶化时间的延长晶化效果越好,500℃退火的薄膜比400℃的晶化效果好.
关键词:
PECVD法
,
非晶硅薄膜
,
光退火晶化
,
拉曼光谱
殷红旗
,
刘永长
,
宁保群
,
徐荣雷
,
张尧卿
,
韩雅静
材料科学与工程学报
doi:10.3969/j.issn.1673-2812.2007.01.030
本文研究了T91钢冷却过程中,不同冷却速度(10 k/min(200 k/min)对相变速度和产物的影响.研究表明不同的冷却速度生成的组织差别较大,在较低速冷却下(10 k/min和30 k/min)的组织为较多的先共析铁素体和板条马氏体,中速冷却(30 k/min和50 k/min)基本都为板条马氏体,在较高速冷却过程中(100 k/min和200 k/min)组织中除了板条马氏体还出现了片状马氏体,另外冷却速度还影响了相变开始点和相变速度.
关键词:
T91
,
冷却速度
,
相变