Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
Nuclear Engineering and Design
Liquid droplet erosion (LDE), which often occurs in bellows made of nickel-based alloys, threatens the security operation of the nuclear power plant. As the candidate materials of the bellows, Inconel 600 and Inconel 625 were both tested for resistance to cavitation erosion (CE) and jet impingement erosion (JIE) through vibratory cavitation equipment and a jet apparatus for erosion-corrosion. Cumulative mass loss vs. exposure time was used to evaluate the erosion rate of the two alloys. The surface and cross-sectional morphologies before and after the erosion tests were observed by scanning electron microscopy (SEM), the inclusions were analyzed by an energy dispersive spectroscopy (EDS), and the surface roughness was also measured by surface roughness tester to illustrate the evolution of erosion process. The results show that the cumulative mass loss of CE of Inconel 625 is about 1/6 that of Inconel 600 and the CE incubation period of the Inconel 625 is 4 times as long as that of the Inconel 600. The micro-morphology evolution of CE process illustrates that the twinning and hardness of the Inconel 625 plays a significant role in CE. In addition, the cumulative mass loss of JIE of Inconel 625 is about 2/3 that of Inconel 600 at impacting angle of 90 degrees, and almost equal to that of the Inconel 600 at impacting angle of 30 degrees. Overall, the resistance to CE and JIE of Inconel 625 is much superior to that of Inconel 600. (C) 2010 Elsevier By. All rights reserved.
关键词:
stress-corrosion cracking;aluminide intermetallic alloys;high-purity;water;mechanical-properties;crevice corrosion;solid particles;wear;behavior;microstructure;deformation;steam
方磊
,
刘宏亮
,
刘承军
,
姜茂发
稀土
doi:10.3969/j.issn.1004-0277.2008.01.022
以重轨钢为研究对象,建立可以定量描述稀土在重轨钢中行为特性的热力学模型,并通过实验验证了模型的精确度.利用该热力学模型,研究分析了在不同氧、硫的质量分数条件下,铈加入量对重轨钢液及其凝固过程中铈的赋存状态以及夹杂物组成的影响作用规律,得到以下结论:当钢中氧、硫的质量分数较低时,随着铈加入量的增加,Ce2O2S的析出量略有减少;当钢中氧、硫的质量分数较高时,随着铈加入量的增加,Ce2O2S的析出量有所增加;铈加入量的增加以及温度的下降均有利于Ces的析出;当钢中氧、硫的质量分数较低时,在凝固过程中钢中析出CeN和固溶铈;随着铈加入量的增加,CeN的析出温度和析出量均有所增加,当CeN的析出达到平衡时,固溶铈大量析出.
关键词:
铈
,
重轨钢
,
夹杂物
,
固溶铈
,
热力学模型
Nuclear Engineering and Design
A composite coating was deposited on Inconel 600 substrate by cold spray method using pure Ni powder (60 wt.%) blended with alpha-Al(2)O(3) (40 wt.%) as feedstock. It is expected to be applied to repair the bellows eroded by the liquid droplet erosion (LDE). Microstructure of the coating was observed using optical microscope (OM) and scanning electron microscopy (SEM). Microhardness of the coating was determined by Vickers hardness tester. Cavitation erosion (CE) experiments were carried out in the distilled water. Jet impingement erosion (JIE) experiments were performed in slurry containing 1 wt.% quartz particle with the flow velocity of 15 m/s at impingement angles of 30 degrees, 60 degrees and 90 degrees, respectively. Cumulative mass loss vs. testing time was used to evaluate the erosion rate of the coating. The erosion mechanism was analyzed by OM, SEM, X-ray diffraction (XRD) and the microhardness measurement. The results show that the composite coating has compact microstructure and relatively high hardness. The resistance to CE of the coating is not as good as that of Inconel 600 substrate due to the weak bonds of the Al(2)O(3) particles. However, the results of the JIE test indicate that the slurry erosion resistance of the coating is better than that of Inconel 600 at the impact angles of 30 degrees and 60 degrees, but not at the normal impact angle. (C) 2011 Elsevier B.V. All rights reserved.
关键词:
large powder particles;composite coatings;slurry erosion;kinetic;spray;liquid impact;alloy;microstructure;steels;deposition;resistance
Philosophical Magazine
The error of Equation (15b) in my article [Z.D. Zhang, Phil. Mag. 87 (2007) p.5309] in the application of the Jordan-Wigner transformation does not affect the validity of the putative exact solution, since the solution is not derived directly from that equation. Other objections of Perk's comment [J.H.H. Perk, Phil. Mag. 89 (2009) p.761] are the same as those in Wu et al.'s comments [F.Y. Wu et al., Phil. Mag. 88 (2008) p.3093; p.3103], which do not stand on solid ground and which I have sought to refute in my previous response [Z.D. Zhang, Phil. Mag. 88 (2008) p.3097]. The conjectured solution can be utilized to understand critical phenomena in various systems, whereas the conjectures are open to rigorous proof.
关键词:
3D Ising model;exact solution;conjecture;critical phenomena;ferromagnetism;magnetic phase transition;model;analyticity