钢铁研究学报(英文版)
The recrystallization behavior of a low carbon high Nb microalloyed steel was investigated using Continuous and interrupted hot compression tests. The results showed that the onset of dynamic recrystallization (DRX) could be detected from inflection in the plot of the strain hardening rate θ against stress σ regardless of whether the stress peak appears or not. According to Zener-Hollomon parameter the activity energy of DRX (Qdef) was obtained, and a new modified expression calculating Qdef was proposed in consideration of the chemical composition of experimental steel. Applying the 2% offset method the static softening fraction was determined. The graphic representation of the softening fraction vs. interrupt time gave the information of the non-static recrystallization temperature (about 1000℃)and the relationship of precipitation-time-temperature. Static recrystallization kinetics follow Avrami’s law in high deformation temperature, and different values of the exponent n were given to illustrate the different effects of Nb element on static recrystallization at different deformation temperature.
关键词:
dynamic recrystallization;static recrystallization;high Nb microalloyed steel;activity energy.
章莎
,
周益春
材料导报
应用纳米压痕法测量残余应力的2种理论模型对5种电沉积镍镀层中的残余应力在不同压痕深度处进行了测量,并与X射线衍射法的测量结果进行了比较.结果表明,压深位于薄膜/基底界面处的2种压痕法测量结果与X射线衍射法的测量结果相近,且Yun-Hee模型与其符合得更好.
关键词:
纳米压痕法
,
电沉积镍镀层
,
残余应力
,
X射线衍射法