LI Chang-sheng
,
YANG Hua
,
WANG Yan-fang
,
YU Yong-mei
钢铁研究学报(英文版)
The hot rolled strip of Fe-3Si steel was experimentally produced by thin slab casting and rolling (TSCR) process in the laboratory. The texture evolution rule was investigated during hot rolling and cold rolling. The texture distribution of cold rolled strips with four kinds of cold rolling reduction schedules was observed through X-ray diffraction method, and the orientation density variation of 1/16 layer, 1/8 layer, 1/4 layer, and 1/2 layer in thickness was analyzed. The cold rolled texture of steel A with four kinds of cold rolling reduction schedules was mainly composed of α and γ fibers. Cold rolling reduction ratio of 70% was more beneficial for obtaining more γ fibers. The γ fiber texture orientation density of {111}<011> and {111}<1 12> was the largest on the 1/8 layer and 1/4 layer and the least on the 1/16 layer and 1/2 layer for steel B. The texture orientation density of {001}-{223}<110> in the α fibers for steel C was increased, but the texture orientation density of {332}-{110}<110> was low.
关键词:
silicon steel
,
texture
,
hot rolling
,
cold rolling
,
thin slab
,
continuous casting
,
direct rolling
MEI Rui-bin
,
LI Chang-sheng
钢铁研究学报(英文版)
The program was developed by finite element method to calculate the temperature distribution in hot strip rolling. The heat transfer coefficient of air cooling, water cooling and thermal resistance between work roll and strip were analyzed. A new heat generate rate model was proposed according to the influence of source current density, work frequency, air gap and distance to edge on induction heating by finite element method (FEM). The heat generate rate was considered into the thermal analysis to predict the temperature distribution in the induction heating. The influence of induction heating on the strip temperature was investigated with different strip thicknesses. The temperature difference became more and more obvious with the increase of thickness. The strip could be heated quickly by the induction heating both in surface and center because of the thermal conductivity and skin effect. The heat loss of radiation has important influence on the surface temperature. The surface temperature could be heated quickly with high frequency when the strip is thicker.
关键词:
Temperature distribution;Finite element method;Induction heating;Skin depth;Hot rolling
李志宏
,
柳卫平
,
白希祥
,
郭冰
,
连钢
,
颜胜权
,
王宝祥
,
陆昀
,
曾晟
,
苏俊
原子核物理评论
doi:10.3969/j.issn.1007-4627.2005.01.006
利用8Li次级束测量了质心系能量7.8 MeV 2H(8Li, 9Li)1H反应的角分布, 导出了8Li(d, p)9Li反应的天体物理S因子及9Li→8Li+n虚衰变的渐近归一化系数.
关键词:
8Li(d,p)9Li反应
,
角分布
,
天体物理S因子
,
渐近归一化系数
HUANG Jianshun CHEN Junming Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai
,
China Research Associate
,
Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai 200050
,
China
金属学报(英文版)
Crystal structure of γ-Li_xFe_2O_3,inserted Li electrochemically,was studied by Moss- bauer spectroscopy together with X-ray diffraction,XPS and electrochemical method,On the insertion of Li at low current density,the crystal structure is keeping original spinel; while at higher current density or by thermal activation,owing to violent movement of Li~+ ions,part of crystal structure transforms into rock type similar to face-centered cubic structure of ferrous oxide.The transition channels during insertion of Li~+ ions and limitation of Li~+ ions inserted were discussed.
关键词:
null
,
null
,
null
Journal of Materials Research
The effect of Li(3)N additive on the Li-Mg-N-H system was examined with respect to the reversible dehydrogenation performance. Screening Study with varying Li(3)N additions (5, 10, 20, and 30 mol%) demonstrates that all are effective for improving the hydrogen desorption capacity. Optimally, incorporation of 10 mol% Li(3)N improves the practical capacity from 3.9 wt% to approximately 4.7 wt% hydrogen at 200 degrees C, which drives the dehydrogenation reaction toward completion. Moreover, the capacity enhancement persists well over 10 de-/rehydrogenation cycles. Systematic x-ray diffraction examinations indicate that Li(3)N additive transforms into LiNH(2) and LiH phases and remains during hydrogen cycling. Combined structure/property investigations suggest that the LiNH(2) "seeding" should be responsible for the capacity enhancement, which reduces the kinetic barrier associated with the nucleation of intermediate LiNH(2). In addition, the concurrent incorporation of LiH is effective for mitigating the ammonia release.
关键词:
complex hydrides;improvement;mixtures;imides;amide;h-2
MANG Weishi WANG Guozhi ZHANG Yongchang HU Zhuangqi SHI Changxu Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China Yongchang Associate Professor
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
A rapidly solidified microcrystalline Al-Li-Cu-Mg-Zr alloy and its superplasicity have been investigated.An optimum tensile elongation of 585% was obtained at 540℃ and strain rate 1.67×10~(-2)s~(-1).The superplastic Al-Li alloy is manufaetured using thermomechanical pro- cessing:solution,overaging,warm rolling and recrystallization.Microstructural changes in thermomechanical processing and cavitation occurred during superplastic deformation have been observed.The superplastic failure of alloy may be caused mainly by nucleation and growth of cavities as well as the linkage around grains.
关键词:
superplasticity
,
null
,
null
,
null
Zhijian LIU
,
Zhiyou LI
,
Wei DUAN
,
Xuanhui QU
,
Baiyun HUANG
,
Siqi ZHANG
材料科学技术（英文）
A LI-B alloy has been prepared using a pretreated amorphous B powder and pure Li ingot as starting materials by continually slow addition of B powder and intensified stirring in the process of melting. The microstructure and the discharge characteristic of the materials have been investigated. Results show that the problem of temperature control in synthesis would be modified by means of continual addition of B powder, the Li7B6 would be more finery distributed in the metal Li by means of intensified stirring. The discharge characteristic of the Li-B alloy using amorphous B as starting materials is almost the same with that of using crystalline B.
关键词: