Thermomechanical Fatigue Behaviour of a Nickel Base Superalloy

LIANG Jin R. M. Pelloux XIE Xishan Univiersity of Science and Technology Beijing , (formely Beijing Univiersity of Iron and Steel Technology) , 100083 , China. MIT , Cambridge MA 02139 USA.

材料科学技术（英文）

The isothermal low cycle fatigue (LCF) and thermomechanical fatigue (TMF) behaviour of a Ni-base superalloy was investigated. The results show that temperature plays an important role in both LCF and TMF. The alloy shows the lowest LCF fatigue resistance in the intermediate temperature range (～760℃). For strain-controlled TMF, in-phase (IP) cycling is more damaging than out-phase (OP) cycling. The high tempera- ture exposure in the TMF cycling influences the deformation behaviour at the low temperature. LCF lives at different temperatures, and IP and OP TMF lives are successfully correlated by using the hysteresis parameter Δσ·Δε_p.

关键词: Ni-base superalloy , null , null

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null

University of Science and Technology Beijing

JIA Shizhen University of Science and Technology Beijing , China.

材料科学技术（英文）

关键词:

R. erythropolis对赤铁矿和石英的吸附?捕收作用

杨慧芬 , 唐琼瑶 , 王传龙 , 张露 , 李甜

中国有色金属学报

为考察红城红球菌(Rhodococcus erythropolis,R. erythropolis)作为赤铁矿捕收剂使用的可能性及效果,对R. erythropolis形貌、细胞壁成分及其吸附前后赤铁矿、石英表面电性、疏水性进行分析,对赤铁矿、石英单矿物以及赤铁矿与石英矿1:1(质量比)混合矿进行浮选实验,对其在赤铁矿表面的吸附状况及吸附机理进行研究.结果表明,杆状R. erythropolis表面既含有非极性基团,又含有极性基团,使得其表面具有较高的负电性和较强的疏水性,因而对赤铁矿的吸附作用明显大于对石英的吸附作用.当以此细菌为捕收剂、在溶液 pH 值为6、R. erythropolis用量为75 mg/L时,赤铁矿的回收率为89.68%,而石英的回收率仅为26.25%.混合矿经过一次浮选,可获得铁品位和回收率分别为50.08%和76.41%的铁精矿.R. erythropolis在赤铁矿表面发生复杂的化学吸附且使赤铁矿颗粒形成疏水絮团,从而证实R. erythropolis可作为赤铁矿的捕收剂使用.

关键词: R. erythropolis , 微生物 , 赤铁矿 , 石英 , 吸附 , 絮团 , 捕收剂

Abstracts of papers from Journal of University of Science and Technology Beijing

稀有金属（英文版）

关键词:

THE EVOLUTION OF TECHNOLOGY DEVELOPMENT AT GE CORPORATE R & D

T.B.Cox(GE Corporate Research & Development , Niskayuna , NY 12309 , USA Manuscript received 26 August 1996)

金属学报(英文版)

A brief review of the nearly 100 year history of Corporate Researeh and Development at GE is presented. Observations on the changing nature and relevance of industrial research are discussed. Examples of current technology projects for aircraft engine materials are reviewed. Emphasis of these projects is placed on high performance,low cost and high quality.

关键词: :spray forming , null , null

Magnetic properties of R2Fe14M3 compounds with M=Ga and Si; R=Y, Nd, Sm, Gd, Tb, Dy, Ho, Er and Tm

Solid State Communications

Samples with composition R2Fe14M3 (M = Ga and Si; R = Y, Nd, Sm, Gd, Tb, Dy, Ho, Er and Tm) have been prepared by are-melting. Crystal-structure studies have shown that the prepared samples are single phase with the rhombohedral Th2Zn17 and/or the hexagonal Th2Ni17 structure. Substitution of Ga for Fe in R2Fe17 leads to an increase of the unit-cell volume, whereas Si substitution reduces the unit-cell volume. The Curie temperatures of the R2Fe14Ga3 and R2Fe14Si3 compounds are much larger than those of the corresponding R2Fe17 compounds. The Fe moment decreases upon Ga or Si substitution. The compounds R2Fe14Ga3 and R2Fe14Si3 With R = Er and Tm exhibit a spin-reorientation transition at low temperature. (C) 1997 Elsevier Science Ltd.

关键词: neutron-diffraction;solid-solutions;substitution;anisotropy;nd2fe17

CHINESE JOURNAL OF METAL SCIENCE & TECHNOLOGY

材料科学技术（英文）

关键词:

Bibliography of Science and Technology of Rare EarthsPublished in China (2001)

稀土学报(英文版)

关键词:

Bibliography of Science and Technology of Rare EarthsPublished in China (2001)

稀土学报(英文版)

关键词: