金属学报(英文版)
The nature of“white layer”found in 55SiMnMo steel subjected to friction test has been stu- died using TEM,SEM,X-ray diffraction and EPMA techniques.It is shown that the struc- ture of the“white laver”on the rubbing surface is duplex,consisting of a special martensite and some austenite.This layer may be 25—50 μm thick.It is ultrafine,with grain diametric approximately 30 nm.Its micro-hardness may be as high as Hm 1500 and is capable of cut- ting glass.It has superb corrosion resistance and resists tempering.Its mierostructure and hardness undergo changes only when the steel is tempered above 500℃.
关键词:
friction
,
null
,
null
LIANG Yong LI Ruiguo Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
ChinaInstitute of Corrosion and Protection of Metals
,
Aademia Sinica
,
Shenyang
,
110015
,
China
材料科学技术（英文）
Recent advances in laser coating technology including laser cladding,laser surface alloying and laser vapour deposition in China are reviewed in this paper.
关键词:
laser
,
null
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null
万小峰
,
张久兴
,
周文元
,
李湘波
,
周美玲
稀有金属材料与工程
研究了FU105大功率广播发射管用碳化镧钼阴极,参照碳化钍钨阴极FU105管的制备工艺,实现了镧钼阴极的碳化以及镧钼阴极FU105管的排气和老炼.通过镧钼阴极FU105管的性能测试,对碳化镧钼阴极的发射能力和稳定性进行了分析.结果认为:FU105管碳化镧钼阴极的发射能力可以达到碳化钍钨阴极的水平,但其稳定性还有待改进.