M.F. Geng(Luoyang Ship Material Research Institute
,
Luoyang 471039
,
China)
金属学报(英文版)
The crack growth behavior and fracture feature of superalloy GH2132 (equivalent to A286) under creep-fatigue conditions have been studied in the present paper. The tests were carried out at 550℃ under various cyclic freqencies (hold time) and load levels,and the fracture surfaces were examined by using a scanning electron microscope. It is shown that the fracture mode of creep-fatigue and the effect of cyclic loading on crack growth change with the growth of crack and the increase of net-section stress,and both are reversed when the net-section stress is up to the yield stress of material.When σn <σ0.2, cracking is predominantly cycle-dependent transgranular and cyclic loading accelerates creep crack growth, whereas when σm>σ0.2, the case is reversed.
关键词:
creep-fatigue
,
null
,
null
,
null
,
null
,
null
YANG Ying
,
YAN Qing-zhi
,
GE Chang-chun
钢铁研究学报(英文版)
Modified CNS-Ⅱ F/M steel was designed for in-core components of supercritical water cooled reactor. Study on the hot deformation behavior of modified CNS-Ⅱ F/M steel is of great importance for processing parameter planning and microstructure controlling during hot deformation. The hot deformation behavior of modified CNS-Ⅱ F/M steel was investigated through isothermal hot compression test at temperature ranging from 1223 to 1373 K and strain rate 001 to 10 s-1. The true stress-true strain data gained from compression tests were used to built constitutive equation of modified CNS-Ⅱ F/M steel. The influence of strain on the accuracy of constitutive analysis was incorporated, assuming strain has a influence on material constants. A 5th order polynominal equation with very good accuracy was used to represent the influence of strain on material constant. The flow stresses calculated from the constitutive equation were compared with test values in the whole experiment range and the absolute average error for the constitutive equation in predicting flow stress is 4728%. At last, the recrystallization behavior of modified CNS-Ⅱ F/M steel was investigated. The relationship of critical strain and peak strain with Zener-Hollomon parameter were given by an experimental equation.
关键词:
F/M steel
,
constitutive equation
,
dynamic recrystallization
YANG Ying
,
YAN Qing-zhi
,
MA Rong
,
GE Chang-chun
钢铁研究学报(英文版)
Ferritic/martensitic (F/M) steels have been recommended as one of the candidate materials for supercritical water cooled reactor (SCWR) in-core components use for its high thermal conductivity, low thermal expansion coefficient and inherently good dimensional stability under irradiation condition in comparison to austenitic steel. CNS-Ⅱ F/M steel which has good mechanical properties was one of the 9-12Cr F/M steels designed for SCWR in the previous work. In this study a modified CNS-Ⅱ F/M steel was used and it′s ultimate tensile strength was 925 MPa at room temperature and 483 MPa at 600 ℃ after optimizing heat treatment parameter. The ductile to brittle transition temperature of modified CNS-Ⅱ F/M steel is -55 ℃. Those are at the same level or even higher than that of CNS-Ⅱ and some commercial F/M steels nominated for SCWR in-core component use. The transmission electron microscope (TEM) results showed that the mechanical properties of the tempered martensite was closely related to the decomposition stage of the martensite.
关键词:
supercritical water reactor
,
ferritic/martensitic steel
,
cladding material
沈朝
,
段振刚
,
孙耀
,
张乐福
,
徐雪莲
腐蚀与防护
采用慢应变速率试验(SSRT)研究了12C>F/M钢在25 MPa,550℃和650℃的超临界水(SCW)中的机械性能,以及在550℃的SCW中的应力腐蚀开裂(SCC)倾向.同时通过均匀腐蚀试验研究了12Cr-F/M钢在550℃/25MPa的SCW中的腐蚀性能.SSRT结果表明,12Cr-F/M钢在550℃/25 MPa时具有优良的机械性能,当温度升高到650 ℃时其机械强度下降明显,但延伸率基本不变.由断口SEM形貌可知,12Cr-F/M钢具有沿晶应力腐蚀开裂(IGSCC)倾向.均匀腐蚀结果表明,12CpF/M钢在550℃/25MPa的SCW中的腐蚀性能较差,其腐蚀增重呈现出抛物线生长规律,1 000 h后其腐蚀增重达741mg/dm2.同时发现其在600 h时表面氧化膜出现裂纹,1 000 h时后观察到氧化膜发生剥落,而氧化膜脱落主要是因为在降温过程中基体与氧化物间不一致的热膨胀系数造成的.
关键词:
腐蚀
,
应力腐蚀开裂
,
机械性能
,
超临界水
胡武生
,
沈嘉年
,
李铁藩
,
彭晓
,
马信清
,
李美栓
,
周龙江
腐蚀学报(英文)
静态空气中氧化实验表明,低偏析镍基铸造高温合金M17F比普通镍基铸造高温合金M17F'(M17F的基础上+0.005%P、0.10%S和0.10%Zr)具有更低的恒温氧化增重速率,但氧化膜的粘附性更差。XRD、SEM和EDAX分析实验表明,两合金氧化膜的组成和结构基本相同。分析认为,M17F'合金中相对高含量的S、P和Zr的共同作用加速了该合金氧化膜的生长,另外该合金中0.1%含量的活性元素Zr改善了氧化膜的粘附性。
关键词:
低偏析镍基铸造高温合金
,
null
,
null
Applied Physics Letters
Impedance analysis was employed to study the frequency response characteristics of supercapacitors utilizing single-walled carbon nanotubes (SWNTs) as electrode material. The knee frequency is around 631 Hz for the electrochemically oxidized SWNT supercapacitor, much higher than that of the as-prepared one (around 316 Hz) and the common activated carbon supercapacitor (< 1 Hz). The good frequency response observed in this work is due to the introduction of nanosized mesopores and oxygen-containing groups formed during the electrochemical oxidization of SWNTs. The capacitance of electrochemically oxidized SWNT supercapacitor is 113 F/g, which is much higher than the value of the as-prepared one (20 F/g). (C) 2008 American Institute of Physics.
关键词:
double-layer capacitance;electrochemical capacitors;surface-chemistry;activated carbon;composite;fiber
徐蕾
,
陈彩霞
,
吴申庆
复合材料学报
采用挤压铸造法制备了Al2O3短纤维增强M124F铝合金复合材料,并研究了其拉伸强度、基体凝固组织和界面.结果表明:用挤压铸造法制备的复合材料组织致密,纤维分布均匀,抗拉强度与M124F相比明显提高;基体组织的α-Al枝晶和Si相明显细化.分析表明,纤维的加入具有双重增强作用:高强度陶瓷纤维的介入增强了基体材料的力学性能;在凝固过程中,Al2O3短纤维阻碍了a-Al枝晶的生长,同时可作为Si相非自发形核的衬底,细化了基体组织,提高了复合材料的力学性能.纤维与基体间未发现界面生成物MgAl2O4.
关键词:
挤压铸造
,
氧化铝短纤维
,
M124F铝合金
,
拉伸强度
,
凝固组织
,
界面
Fatih Hayat
,
Hüseyin Uzun
钢铁研究学报(英文版)
Grade A (GA) and high strength steel DH36 ship steels possessing different chemical compositions were used, and strength properties of GA steel and DH36 steel were compared. Additionally, 4 types of dual phase (DP) steels with different martensite volume fractions (MVFs) were produced from GA steel by means of heat treatment and they were compared with other steels through conducting microstructure, microhardness, tensile and impact tests. The fracture surfaces of specimens (DH36, GA and DP steels) exposed to tensile and Charpy impact tests were investigated by scanning electron microscope. Furthermore, it was found that the specimens quenched from 800 and 900 ℃ had better strength than DH36 steel. The tensile test results indicated that the tensile strength of DP steel water quenched from 900 ℃ was 3 times that of GA steel and twice that of DH36 steel.
关键词:
Grade A ship steel
,
DH36 ship steel
,
dual phase steel
,
martensite
,
mechanical property
,
fracture