材料科学技术（英文）
Various Mo-base alloys with high melting temperature were processed into ribbons and foils by the arc melt-spinning and the arc melt hammer-anvil technique. The preparation of ribbon and foil was introduced. The mechanical proper- ties, the surface topology and the microstructure of rapidly solidified Mo-base alloys containing B were examined. A strong grain refinement and a strong age-hardening response were observed on the as-quenched and the age specimens, the precipitates which cause age hardening were identified to be Mo_2B in Mo-B alloys, Mo_2B and ZrB_2 in Mo-Zr-B alloys, and Mo_2B and ThB_4 in Mo-Th-B alloys. The results indicate that the high strength Mo-base alloys containing boride precipitates can be developed by rapid solidifica- tion technique.
关键词:
Mo-alloys
,
null
,
null
,
null
,
null
Yan NIU
,
Weitao WU and Chaoliu ZENG (State Key Lab. for Corrosion and Protection
,
Institute of Corrosion and Protection of Metals
,
Chinese Academy of Sciences
,
Shenyang 110015
,
China)F. Gesmundo and F. Viani (Instituto di Chimica
,
Facolta di Ingegneria
,
Un
材料科学技术（英文）
The corrosion of an Fe-based alloy containing 15 wt pct Y in H2-H2S mixtures under 10-3 Pa S2 was studied at 600~800℃ in an attempt to find materials with improved sulphidation resistance with respect to pure Fe. The presence of Y has been shown to be beneflcial, but not sufficient to the level expected. In fact, the alloy is able to form at all tested temperatures an external FeS layer, beneath which a zone containing a mixture of the two sulphides is also present. Thus,Fe can still diffuse through this region to form the outer FeS layer with non-negligible rate. The corrosion rate of Fe is considerably reduced by the Y addition. but the alloy corrodes still much more rapidly than Y. The sulphidation kinetics is generally rather irregular for both the pure metals, while the corrosion rate of the alloy decreases with time and tends to become parabolic after an initial period of 12~17 h. The sulphidation behaviour of the alloys is discussed by taking into account the presence of an intermetallic compound Fe17Y2 and the limited solubility of Y in Fe
关键词:
材料科学技术（英文）
The corrosion of an Fe-based alloy containing 15 wt pet Y in H-2-H2S mixtures under 10(-3) Pa S-2 was studied at 600 similar to 800 degrees C in an attempt to find materials with improved sulphidation resistance with respect to pure Fe. The presence of Y has been shown to be beneficial, but not sufficient to the level expected. In fact, the alloy is able to form at all tested temperatures an external FeS layer, beneath which a zone containing a mixture of the two sulphides is also present. Thus, Fe can still diffuse through this region to form the outer FeS layer with non-negligible rate. The corrosion rate of Fe is considerably reduced by the Y addition, but the alloy corrodes still much more rapidly than Y. The sulphidation kinetics is generally rather irregular for both the pure metals, while the corrosion rate of the alloy decreases with time and tends to become parabolic after an initial period of 12 similar to 17 h. The sulphidation behaviour of the alloys is discussed by taking into account the presence of an intermetallic compound Fe17Y2 and the limited solubility of Y in Fe.
关键词:
high-temperature sulfidation;most-reactive component;ni-nb alloys;h2-h2s mixtures;behavior;600-degrees-c-800-degrees-c;oxidation