Wear
The sliding wear behavior of Al2O3/Al composite prepared by the Lanxide process was investigated. Either a carbon steel ring and a Si3N4 pin was selected as the counter face. It is shown that microporosity which is disadvantageous to the mechanical properties of the composite can provide better lubrication due to its oil content and the oil-feeding effect. Scanning electron microscopy observations and energy dispersive X-ray analyses described the influence of metal phases and porosity upon sliding wear of the composite, which leads to an initial discussion of the sliding-wear mechanism of Lanxide Al2O3/Al composite. (C) 1998 Elsevier Science S.A.
关键词:
Lanxide Al2O3/Al composite;wear;lubrication;wear mechanism;directed oxidation;surface dopant;tool steel;alumina;ceramics
窦强
,
王斌
高分子材料科学与工程
研究了β晶型成核剂(酰胺化合物)成核改性纤维级聚丙烯Z30S的力学性能,进行了广角X射线衍射和DSC分析.发现成核改性后生成了β晶型聚丙烯,因而聚丙烯Z30S的冲击性能提高.通过纺丝-拉伸实验和对纤维进行广角X射线衍射分析、SEM观察,发现成核改性纤维在纺丝拉伸过程中发生了晶型转变,产生大量微孔隙.
关键词:
聚丙烯
,
β晶型
,
成核剂
,
纤维
程俊梅
,
张萍
,
于广水
,
赵树高
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2009.06.016
在比表面积相近的情况下,探讨白炭黑(Z125)及碳黑(N234)对天然橡胶(NR)和溶聚丁苯橡胶(S-SBR)硫化胶的抗割口增长能力及动态力学性能的影响.结果表明,Z125和N234对NR和S-SBR两种硫化胶的增强效果相差不大;NR硫化胶的抗割口增长能力明显好于S-SBR硫化胶;NR中填充Z125的抗割口增长能力好于N234且随疲劳次数的增加Z125的优势更加明显,而S-SBR中填充N234的抗割口增长能力好于Z125且两者的抗割口增长速率基本不随疲劳次数的增加而改变;Z125使NR和S-SBR硫化胶在0℃和70℃下的tanδ值分别低于N234增强相应硫化胶.
关键词:
NR
,
S-SBR
,
白炭黑
,
炭黑
,
动态力学性能
,
抗割口增长能力
唐波
,
朱丽慧
机械工程材料
利用RD-2型高温持久试验机、高分辨透射电子显微镜和能谱仪研究了国产S30432耐热钢在供货态及不同温度、应力条件下持久断裂后的第二相,尤其是Z相的析出行为及影响因素.结果表明:供货态S30432钢中只存在MX相;在650℃、170 MPa、10 712 h持久条件下析出了M23 C6碳化物和富铜相;在700℃、150MPa、937 h条件下,不仅析出了M23 C6碳化物和富铜相,还出现了Z相及包含MX相和Z相的颗粒;在700℃、150 MPa、1 944 h条件下Z相粗化缓慢,在700℃、100MPa、11 832 h条件下Z相粗化明显;高温和应力均会加速Z相的析出.
关键词:
耐热钢
,
Z相
,
显微组织
崔宏伟
,
陈建玉
,
丁雨憧
,
狄聚青
,
赛青林
,
赵广军
人工晶体学报
本文通过优化晶体生长工艺,采用提拉法生长了浓度分别为0.5at％、1at％和3at％系列高质量Pr3+掺杂Lu3Al5O12晶体.通过ICP、透射光谱、荧光光谱等系统研究了晶体性能.结果表明:Pr∶ LuAG晶体在紫外光范围内有较强吸收峰；X射线激发荧光峰较光致激发荧光峰发生蓝移；随掺杂浓度的提高,晶体中pr3+的浓度成比例提高,同时晶体的透过率及荧光光谱强度都有相应提高.
关键词:
Pr∶LuAG晶体
,
晶体生长
,
光学性能
王晓丹
,
潘涛
,
臧涛成
,
马春兰
,
徐晓东
,
徐军
,
曾雄辉
人工晶体学报
采用提拉法生长Yb~(3+)掺杂浓度为10 at%的Yb: Lu_3Al_5O_(12)(Yb: LuAG)晶体.对晶体的结晶质量、晶胞参数、分凝系数等进行了表征.采用化学腐蚀的方法,利用光学显微镜和扫描电镜相结合研究了晶体中的缺陷.结果表明晶体具有较好的结晶质量,Yb~(3+)的掺入不会改变LuAG的晶体结构.观察到Yb: LuAG晶体(111)面上呈三角锥形的位错蚀坑和由小面引起的晶体应力双折射现象,并提出了减少缺陷,提高晶体质量的方法.
关键词:
Yb:LuAG晶体
,
晶胞参数
,
位错
,
应力
Corrosion Science
The oxidation process of Ti-45Al-8Nb-0.2W-0.2B-0.02Y (at%) can be divided into three stages during 100 h at 900 degrees C. The change of ion diffusion path leads to the discontinuity of the oxidation curve between the second and third stage. Different stages of oxidation morphology have been investigated combined with TEM and STEM. AlNb2 phase forms at the interface of oxide scale/base alloy. Contrary to a continuous formation of 'x' phase in gamma-TiAl with Nb free at the interface of oxide scale/base alloy. AlNb2 phase hinder continuous 'x' phase formation, which can promote TiAl oxidation protection. (c) 2007 Elsevier Ltd. All rights reserved.
关键词:
alloy;STEM;oxidation;gamma-titanium aluminide;high-temperature air;tial-based alloys;intermetallic alloys;ternary-system;behavior;phase;scales;si
李金凯
,
滕鑫
,
曹丙强
,
刘宗明
无机材料学报
doi:10.15541/jim20150479
以尿素为沉淀剂,通过均匀沉淀技术制备前驱体颗粒,经后续煅烧获得分散性能良好的球形(Lu0.95Eu0.05)3Al5O12((Lu0.95Eu0.05)AG)荧光颗粒.通过调整尿素浓度实现了球形荧光颗粒尺寸的可控合成.在此基础上,采用FT-IR、TG/DTA、XRD、FE-SEM、TEM和PLE/PL对材料的合成、物相形成及荧光性能等进行一系列表征.分析结果表明:前驱体经较低的温度1100℃煅烧即可获得(Lu0.95Eu0.05)AG球形荧光颗粒,且该荧光颗粒具有高的理论密度,适于闪烁体材料的应用.在235 nm电荷迁移带(CTB)的激发下,(Lu0.95Eu0.05)AG石榴石于592 nm(Eu3+的5D0→7F1磁偶极子跃迁)处呈现优异的橙红光发射,其色坐标为(0.63,0.37).该荧光颗粒的发光强度随颗粒尺寸的增大而增强,荧光寿命随颗粒尺寸的增大而缩短.球形(Lu0.95Eu0.05)AG石榴石颗粒有望成为一类新型荧光材料,广泛应用于照明及显示领域.
关键词:
Lu3Al5O12石榴石
,
Eu3+掺杂
,
球形颗粒
,
荧光性能
谢建军
,
施鹰
,
胡耀铭
,
陈启伟
,
施剑林
无机材料学报
doi:10.3724/SP.J.1077.2009.00079
用碳酸氢铵作为沉淀剂，将硝酸镥、硝酸铝和硝酸铈配成混合溶液，采用反滴定共沉淀及低温煅烧前驱体的方法制备 Lu3Al5O12(Ce)纳米发光粉体.采用热分析(TG-DTA)、傅立叶红外光谱(FTIR)、X射线衍射(XRD)、透射电镜(TEM)和光致发光(PL)等分析测试方法对Lu3Al5O12(Ce)粉体制备过程中的物理化学变化及粉体的激发发射发光性能进行了研究.结果表明,采用反滴定共沉淀法制备工艺，经过1000℃煅烧2h,可以得到晶粒尺寸为30nm左右，仅有轻微团聚,单一石榴石相的Lu3Al5O12(Ce)粉体.并且在1000℃处理得到的粉体的光致发光最强.
关键词:
共沉淀
,
Lu3Al5O12(Ce)
,
luminescence
,
nanoscaled powder
谢建军
,
施鹰
,
胡耀铭
,
陈启伟
,
施剑林
无机材料学报
用碳酸氢铵作为沉淀剂,将硝酸镥、硝酸铝和硝酸铈配成混合溶液,采用反滴定共沉淀及低温煅烧前驱体的方法制备 Lu3Al5O12(Ce)纳米发光粉体.采用热分析(TG-DTA)、傅立叶红外光谱(FTIR)、X射线衍射(XRD)、透射电镜(TEM)和光致发光(PL)等分析测试方法对Lu3Al5O12(Ce)粉体制备过程中的物理化学变化及粉体的激发发射发光性能进行了研究.结果表明,采用反滴定共沉淀法制备工艺,经过1000℃煅烧2h,可以得到晶粒尺寸为30nm左右,仅有轻微团聚,单一石榴石相的Lu3Al5O12(Ce)粉体.并且在1000℃处理得到的粉体的光致发光最强.
关键词:
共沉淀
,
铝酸镥石榴石
,
光致发光
,
纳米粉体